A pore-free ceramic is provided that has a high modulus of elasticity and a low coefficient of thermal expansion. A process for producing a corresponding ceramic is also provided. The pore free ceramic is a dimensionally stable substrate material in applications subjected to temperature gradients including semiconductor manufacture.

Disclosed is a joined ceramic body comprising a first ceramic portion comprising a first ceramic, a second ceramic portion comprising a second ceramic, and a joining layer formed between the first ceramic portion and the second ceramic portion. The joining layer has a bond thickness of from 0.5 to 20 um and comprises silicon dioxide having a total impurity content of 20 ppm and less. A method of making the joined ceramic body and a joining material are also disclosed.

Disclosed is a joined ceramic body comprising a first ceramic portion comprising a first ceramic, a second ceramic portion comprising a second ceramic, and a joining layer formed between the first ceramic portion and the second ceramic portion. The joining layer has a bond thickness of from 0.5 to 20 um and comprises silicon dioxide having a total impurity content of 20 ppm and less. A method of making the joined ceramic body and a joining material are also disclosed.

A method of manufacturing a lithium aluminosilicate glass product suitable for making a glass-ceramic product, includes melting a vitrifiable mixture of raw materials, which are free from arsenic oxides and antimony oxides, apart from unavoidable traces, refining the molten material, cooling the molten material so as to form a glass, forming of the glass, wherein the vitrifiable mixture of raw materials includes petalite having a fraction by weight of total iron, expressed as Fe.sub.2O.sub.3, less than or equal to 200 ppm.

The present invention relates to a crystallized glass including: at least one crystal of indialite and cordierite, in which the crystallized glass has a total amount of the crystal is 40 mass % or more of the crystallized glass, and the crystal comprises at least one of a vacancy and a different element at an Al site.

The present invention relates to a glass ceramic for veneering a dental frame structure, wherein said glass ceramic is characterized by a high content of B.sub.2O.sub.3, to a process for the preparation thereof, and to the use thereof in the production of dental restorations.

A process for preparing roofing granules includes forming kaolin clay into green granules and sintering the green granules at a temperature of at least 900 degrees Celsius to cure the green granules until the crystalline content of the sintered granules is at least ten percent as determined by x-ray diffraction.

A process for preparing roofing granules includes forming kaolin clay into green granules and sintering the green granules at a temperature of at least 900 degrees Celsius to cure the green granules until the crystalline content of the sintered granules is at least ten percent as determined by x-ray diffraction.

Embodiments of a glass-based article including a first surface and a second surface opposing the first surface defining a thickness (t) of about 3 millimeters or less (e.g., about 1 millimeter or less), and a stress profile, wherein all points of the stress profile between a thickness range from about 0.Math.t up to 0.3.Math.t and from greater than about 0.7.Math.t up to t, comprise a tangent with a slope having an absolute value greater than about 0.1 MPa/micrometer, are disclosed. In some embodiments, the glass-based article includes a non-zero metal oxide concentration that varies along at least a portion of the thickness (e.g., 0.Math.t to about 0.3.Math.t) and a maximum central tension in the range from about 80 MPa to about 100 MPa. In some embodiments, the concentration of metal oxide or alkali metal oxide decreases from the first surface to a value at a point between the first surface and the second surface and increases from the value to the second surface. The concentration of the metal oxide may be about 0.05 mol % or greater or about 0.5 mol % or greater throughout the thickness. Methods for forming such glass-based articles are also disclosed.

A glass-ceramic that includes a first crystal phase including (Mg.sub.xZn.sub.1-x)Al.sub.2O.sub.4, where x is ≤1, and a second crystal phase including tetragonal ZrO.sub.2. The glass-ceramic may be substantially free of arsenic, tin, antimony, and cesium, each of the arsenic, tin, antimony, and cesium present at less than 0.01% (by mole of oxide). Further, the glass-ceramic may include a transmittance of at least about 80% to light having a wavelength of 380 nm to 760 nm.