A shock absorbing member 50 having a ceramic bonded body 15 having: a plurality of first sheet-like members 5 each having a ceramic containing 60 mass % or more of boron carbide and each having a thickness of 0.1 to 50 mm; and a bonding layer arranged between the first sheet-like members 5 adjacent to each other, the bonding layer bonding surfaces to be bonded facing each other of the first sheet-like members adjacent to each other, wherein the bonding layer has a bonding material containing at least one metal selected from the group consisting of aluminum, copper, silver, and gold.

A method for forming an ultra-high temperature (UHT) composite structure includes dispensing a polymeric precursor with a spinneret biased at a first DC voltage; forming a plurality of nanofibers from the polymeric precursor; receiving the plurality of nanofibers with a collector biased at a second DC voltage different than the first DC voltage; and changing a direction of movement of the plurality of nanofibers between the spinneret and the collector with a plurality of magnets having a magnetic field by adjusting the magnetic field.

Provided is a ceramic member in which the difference in thermal expansion coefficient between an insulating ceramic material and an electrically conductive ceramic material is extremely small and therefore any mismatch caused in association with this difference in thermal expansion coefficient does not occur, and which does not undergo any failure such as breakage, cracking, detachment or destruction. The ceramic member (1) includes an electrically conductive ceramic material (2) which contains yttrium oxide as the main component and additionally contains a fibrous electrically conductive substance such as carbon nanotubes in an amount of 0.1 to 3 vol % inclusive and an insulation ceramic material (3) which contains yttrium oxide as the main component, wherein the electrically conductive ceramic material (2) and the insulation ceramic material (3) are adhered to each other in an integrated manner through an adhesive layer (4) which includes an inorganic adhesive material.

A method is described for assembling at least two parts made of silicon carbide based materials by non-reactive brazing in an oxidizing atmosphere, each of the parts comprising a surface to be assembled, wherein the parts are placed in contact with a non-reactive brazing composition, the assembly formed by the parts and the brazing composition is heated to a brazing temperature sufficient for completely or at least partially melting the brazing composition, or rendering the brazing composition viscous, and the parts and the brazing composition are cooled so as to form, after cooling the latter to ambient temperature, a moderately refractory joint. The non-reactive brazing composition is a composition A consisting of silica (SiO.sub.2), alumina (Al.sub.2O.sub.3), and calcium oxide (CaO), or a composition B consisting of alumina (Al.sub.2O.sub.3), calcium oxide (CaO), and magnesium oxide (MgO), and, before heating the assembly formed by the parts and the brazing composition to the brazing temperature, a supply of silicon in a non-oxidized form is carried out on the surfaces to be assembled of the parts to be assembled, and/or on the surface layers comprising the surfaces to be assembled of the parts to be assembled, and/or in the brazing composition.

A method is described for assembling at least two parts made of silicon carbide based materials by non-reactive brazing in an oxidizing atmosphere, each of the parts comprising a surface to be assembled, wherein the parts are placed in contact with a non-reactive brazing composition, the assembly formed by the parts and the brazing composition is heated to a brazing temperature sufficient for completely or at least partially melting the brazing composition, or rendering the brazing composition viscous, and the parts and the brazing composition are cooled so as to form, after cooling the latter to ambient temperature, a moderately refractory joint. The non-reactive brazing composition is a composition A consisting of silica (SiO.sub.2), alumina (Al.sub.2O.sub.3), and calcium oxide (CaO), or a composition B consisting of alumina (Al.sub.2O.sub.3), calcium oxide (CaO), and magnesium oxide (MgO), and, before heating the assembly formed by the parts and the brazing composition to the brazing temperature, a supply of silicon in a non-oxidized form is carried out on the surfaces to be assembled of the parts to be assembled, and/or on the surface layers comprising the surfaces to be assembled of the parts to be assembled, and/or in the brazing composition.

The present invention relates to inorganic fibres having a composition comprising: 65.7 to 70.8 wt % SiO.sub.2; 27.0 to 34.2 wt % CaO; 0.10 to 2.0 wt % MgO; and optional other components providing the balance up to 100 wt %,
wherein the sum of SiO.sub.2 and CaO is greater than or equal to 97.8 wt %; and the other components, when present, comprise no more than 0.80 wt % Al.sub.2O.sub.3; and wherein the amount of MgO and other components are configured to inhibit the formation of surface crystallite grains upon heat treatment at 1100° C. for 24 hours, wherein said surface crystallite grains comprise an average crystallite size in a range of from 0.0 to 0.90 μm.

A vibrating plate-bonded body includes a supporting substrate composed of silicon, a vibrating plate composed of a highly rigid ceramics and having a thickness of 100 μm or smaller, and a bonding layer between the supporting substrate and vibrating plate, contacting a bonding surface of the vibrating plate and composed of α-Si. The arithmetic average roughness Ra of the bonding surface of the vibrating plate is 0.01 nm or more and 10.0 nm or less, and the pit density of the bonding surface of the vibrating plate is 10 counts or more per 100 μm.sup.2.

A mullite sintered body according to the present invention has an impurity element content of 1% by mass or less and contains sintered mullite grains having an average grain size of 8 μm or less. When a surface of the mullite sintered body is finished by polishing, pores in the surface have an average largest pore length of 0.4 μm or less. The surface preferably has a center line average surface roughness (Ra) of 3 nm or less. The surface preferably has a maximum peak height (Rp) of 30 nm or less. The number of pores in the surface is preferably 10 or less per unit area of 4 μm×4 μm.

Provided is a hearth roll for supporting and conveying a steel sheet in a continuous annealing furnace, wherein all of a shaft portion and a roil main body are made from one or more ceramic materials, preferably constituted with concentric ceramic layers of different ceramic materials centering on the rotation shaft of the roll. The hearth roll has not only an excellent pickup resistance but also a long roll life free from maintenance for long periods. Also provided is a continuous annealing facility using the hearth roll in at least one of a heating zone, a soaking zone and a cooling zone.

A cordierite-based sintered body according to the present invention contains cordierite as a main component and silicon nitride or silicon carbide. The cordierite-based sintered body preferably has a thermal expansion coefficient less than 2.4 ppm; ° C. at 40° C. to 400° C., an open porosity of 0.5% or less, and an average grain size of 1 μm or less.