Disclosed is an adhesive film. The adhesive film has a silicone adhesive layer on one surface or both surfaces of a substrate film. A silicone adhesive material is used to form the silicone adhesive layer. The silicone adhesive material has 120 to 380% of an elongation at break (tensile speed of 300 mm/min, temperature of 25° C.) specified in JIS K 6251, and 1.8×10.sup.5 to 4.5×10.sup.5 Pa of a shear storage modulus (frequency of 10 Hz, temperature of 25° C.). The adhesive film generally has good wettability to the surface of an adherend and in general can be easily attached without creating air bubbles, to the extent that, even if air bubbles are created, the air bubbles can be easily dissipated. Further, even though the adhesive film is generally not easily peeled, peeling is generally possible with a small adhesive force during high speed peeling.

Disclosed is an adhesive film. The adhesive film has a silicone adhesive layer on one surface or both surfaces of a substrate film. A silicone adhesive material is used to form the silicone adhesive layer. The silicone adhesive material has 120 to 380% of an elongation at break (tensile speed of 300 mm/min, temperature of 25° C.) specified in JIS K 6251, and 1.8×10.sup.5 to 4.5×10.sup.5 Pa of a shear storage modulus (frequency of 10 Hz, temperature of 25° C.). The adhesive film generally has good wettability to the surface of an adherend and in general can be easily attached without creating air bubbles, to the extent that, even if air bubbles are created, the air bubbles can be easily dissipated. Further, even though the adhesive film is generally not easily peeled, peeling is generally possible with a small adhesive force during high speed peeling.

Powderous formulations are disclosed containing vitamin E which can be produced easily and which can be used in many fields of application, but mainly in beverages.

Powderous formulations are disclosed containing vitamin E which can be produced easily and which can be used in many fields of application, but mainly in beverages.

Powderous formulations are disclosed containing vitamin E which can be produced easily and which can be used in many fields of application, but mainly in beverages.

An earth plant-based compostable biodegradable composition for the formation of a bioplastic and method of producing said resin, the composition comprising: about 17.5 to 45% ethanol-based green polyethylene by weight, about 20 to 25% calcium carbonate by weight, about 2 to 12% hemp hurd or soy protein by weight, about 32 to 45% starch by weight, and about 0.5 to 1% biodegradation additive by weight to enable biodegradation and composting of the bioplastic; wherein the composition is produced by first mill grinding the ethanol-based green polyethylene, calcium carbonate, hemp hurd or soy protein, starch and the biodegradation additive into fine powders, then mechanically mixing the fine powders one by one into a final mixture for about 5-25 minutes at a time, dry and without heat, and then heating the final mixture to about 220 to 430 degrees Fahrenheit.

An earth plant-based compostable biodegradable composition for the formation of a bioplastic and method of producing said resin, the composition comprising: about 17.5 to 45% ethanol-based green polyethylene by weight, about 20 to 25% calcium carbonate by weight, about 2 to 12% hemp hurd or soy protein by weight, about 32 to 45% starch by weight, and about 0.5 to 1% biodegradation additive by weight to enable biodegradation and composting of the bioplastic; wherein the composition is produced by first mill grinding the ethanol-based green polyethylene, calcium carbonate, hemp hurd or soy protein, starch and the biodegradation additive into fine powders, then mechanically mixing the fine powders one by one into a final mixture for about 5-25 minutes at a time, dry and without heat, and then heating the final mixture to about 220 to 430 degrees Fahrenheit.

A method for producing starch soft capsules comprises the following steps: preparing a mixture comprising starch, plasticizer and water, wherein more than 50 weight percent of the starch is present in the form of particles of granular starch; shaping the mixture to form a film in a shaping process; solidifying the mixture by increasing the temperature of the mixture during and/or after the shaping process by more than 5° C.; and shaping the film to form a soft capsule. Soft capsules produced by this method have starch particles bonded to one another. A device for performing this method comprises a shaping device to enable shaping of the starch material to form a film, and a heating device to perform a heat treatment to destructure the starch during and/or after the shaping. It comprises a rotary die device.

A method for producing starch soft capsules comprises the following steps: preparing a mixture comprising starch, plasticizer and water, wherein more than 50 weight percent of the starch is present in the form of particles of granular starch; shaping the mixture to form a film in a shaping process; solidifying the mixture by increasing the temperature of the mixture during and/or after the shaping process by more than 5° C.; and shaping the film to form a soft capsule. Soft capsules produced by this method have starch particles bonded to one another. A device for performing this method comprises a shaping device to enable shaping of the starch material to form a film, and a heating device to perform a heat treatment to destructure the starch during and/or after the shaping. It comprises a rotary die device.

A method for producing starch soft capsules comprises the following steps: preparing a mixture comprising starch, plasticizer and water, wherein more than 50 weight percent of the starch is present in the form of particles of granular starch; shaping the mixture to form a film in a shaping process; solidifying the mixture by increasing the temperature of the mixture during and/or after the shaping process by more than 5° C.; and shaping the film to form a soft capsule. Soft capsules produced by this method have starch particles bonded to one another. A device for performing this method comprises a shaping device to enable shaping of the starch material to form a film, and a heating device to perform a heat treatment to destructure the starch during and/or after the shaping. It comprises a rotary die device.