A preparation method of a bionic adhesive material with a tip-expanded microstructural array includes the following steps: machining through-holes on a metal sheet; modifying morphology of a through-hole by electroplating, using the metal sheet in step 1 as an electroplating cathode, and arranging the electroplating cathode and an electroplating anode in parallel to prepare a hyperboloid-like through-hole array assembly, fitting a lower surface of the hyperboloid-like through-hole array assembly tightly to an upper surface of a substrate assembly to prepare a through-hole assembly of a mold; and filling the mold assembly with a polymer, curing, and demolding to obtain the adhesive material with the tip-expanded microstructural array.

A preparation method of a bionic adhesive material with a tip-expanded microstructural array includes the following steps: machining through-holes on a metal sheet; modifying morphology of a through-hole by electroplating, using the metal sheet in step 1 as an electroplating cathode, and arranging the electroplating cathode and an electroplating anode in parallel to prepare a hyperboloid-like through-hole array assembly, fitting a lower surface of the hyperboloid-like through-hole array assembly tightly to an upper surface of a substrate assembly to prepare a through-hole assembly of a mold; and filling the mold assembly with a polymer, curing, and demolding to obtain the adhesive material with the tip-expanded microstructural array.

Reinforcing fibers containing hydrophilic fibers and an adhesive component, wherein at least a part of the surfaces of the hydrophilic fibers have the adhesive component, the adhesive component contains a modified conjugated diene rubber having a hydrogen-bonding functional group in a part of the conjugated diene rubber, and the number of the hydrogen-bonding functional groups in the modified conjugated diene rubber is 2 to 150 per molecule on average; a method for producing the reinforcing fibers; and a molded article using the reinforcing fibers.

Reinforcing fibers containing hydrophilic fibers and an adhesive component, wherein at least a part of the surfaces of the hydrophilic fibers have the adhesive component, the adhesive component contains a modified conjugated diene rubber having a hydrogen-bonding functional group in a part of the conjugated diene rubber, and the number of the hydrogen-bonding functional groups in the modified conjugated diene rubber is 2 to 150 per molecule on average; a method for producing the reinforcing fibers; and a molded article using the reinforcing fibers.

A display unit that includes an image display part and a light-transmitting protective part arranged on the image display part. A cured resin layer is arranged between the display part and the protective part. The cured resin layer can have a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10.sup.7 Pa or less. The cured resin layer can be formed from a resin composition that has a cure shrinkage of 5% or less.

A display unit that includes an image display part and a light-transmitting protective part arranged on the image display part. A cured resin layer is arranged between the display part and the protective part. The cured resin layer can have a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10.sup.7 Pa or less. The cured resin layer can be formed from a resin composition that has a cure shrinkage of 5% or less.

A display unit that includes an image display part and a light-transmitting protective part arranged on the image display part. A cured resin layer is arranged between the display part and the protective part. The cured resin layer can have a transmittance of 90% or higher in the visible range and a storage modulus at 25° C. of 1×10.sup.7 Pa or less. The cured resin layer can be formed from a resin composition that has a cure shrinkage of 5% or less.

Disclosed are an adhesive composition that includes: a first photopolymerization initiator having a maximum absorption wavelength in a range of about 350 nm to about 370 nm and a second photopolymerization initiator having a maximum absorption wavelength in a range of about 380 nm to about 390 nm, and a method of manufacturing a display device.

Disclosed are an adhesive composition that includes: a first photopolymerization initiator having a maximum absorption wavelength in a range of about 350 nm to about 370 nm and a second photopolymerization initiator having a maximum absorption wavelength in a range of about 380 nm to about 390 nm, and a method of manufacturing a display device.

Disclosed are an adhesive composition that includes: a first photopolymerization initiator having a maximum absorption wavelength in a range of about 350 nm to about 370 nm and a second photopolymerization initiator having a maximum absorption wavelength in a range of about 380 nm to about 390 nm, and a method of manufacturing a display device.