Disclosed herein is a high-strength plated steel sheet having a plated layer on the surface of a base steel sheet and containing predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet; and a hard layer consisting of a structure which is mainly composed of martensite and bainite and in which the average grain size of prior austenite is 20 μm or less. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

The high-strength plated steel sheet of the present invention has a plated layer on the surface of a base steel sheet and contains predetermined steel components. The steel sheet includes, in the order from the interface of the base steel sheet and the plated layer towards the base steel sheet: a soft layer having a Vickers hardness that is 90% or less of the Vickers hardness at a portion t/4 of the base steel sheet, where t is a sheet thickness of the base steel sheet: and a hard layer containing martensite, bainite, and ferrite in predetermined ranges. The average depth D of the soft layer is 20 μm or greater, and the average depth d of an internal oxide layer is 4 μm or greater and smaller than D.

A hot-rolled strip steel product having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.025%-0.070% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.050% S, <0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.20% Mo, 0%-0.15% Al, 0%-0.050% Nb, 0.020%-0.20-% V, 0.020%-0.15% Ti, 0%-0.0010% B, remainder Fe and inevitable impurities, wherein the strip steel product has a microstructure comprising of, in terms of volume percentages (vol. %), ferrite ≥90%, wherein the ferrite structure comprises 10%-50% quasi-polygonal ferrite and a reminder of ferrite structure is polygonal ferrite and/or bainite: and wherein the steel strip product has an average ferrite grain size of <10 μm, an average hole expansion ratio of ≥50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ≥660 MPa and a tensile strength of ≥760 MPa.

A wind turbine blade includes a base member formed of FRP and having a blade shape, an intermediate layer arranged on the base member and formed of metal, cermet, ceramic, or a mixture of at least one thereof and resin as a major constituent, and an erosion-resistant overcoat arranged on the intermediate layer and formed of a spray film having a porosity of 5% or lower.

A high-temperature component made of a refractory metal or a refractory metal alloy, includes a coating for increasing thermal emissivity. The coating is formed substantially of tungsten and rhenium, i.e. of at least 55 wt. % rhenium and at least 10 wt. % tungsten, and has a Re3W phase of at least 35 wt. %. A process for producing a high-temperature component having a coating for increasing thermal emissivity, is also provided.

This hot-dip Zn—Al—Mg-based plated steel includes: a steel; and a plating layer formed on a surface of the steel, in which the plating layer contains, as an average composition, Mg: 1 to 10 mass %, Al: 4 to 22 mass %, and a remainder consisting of Zn and impurities, the plating layer includes an (Al—Zn mixed structure) in an area ratio of 10% to 70% in a cross section of the plating layer in a matrix of an (Al/Zn/MgZn.sub.2 ternary eutectic structure), the (Al—Zn mixed structure) includes a first region that has a Zn concentration in a range of 75 mass % or more and less than 85 mass % and a second region that is present inside the first region and has a Zn concentration in a range of 67 mass % or more and less than 75 mass %, and an area ratio of the second region in the (Al—Zn mixed structure) in the cross section of the plating layer is more than 0% and 40% or less.

A sliding member including an overlay capable of realizing good fatigue resistance while preventing interlayer peeling. The sliding member including an overlay formed of an alloy plating film of Bi and Sb, wherein Bi—Sb oxide is formed on a surface of the overlay.

Disclosed are thermoformed component having excellent coating adhesion and a method for manufacturing the same. The thermoformed component comprises a substrate layer and an aluminum coating coated on at least one surface of the substrate layer, wherein the average roughness Ra of a surface of the thermoformed component is between 1.0 μm and 3.0 μm, the peak height and the peak-to-valley height Rt are between 8 μm and 30 μm, and the roughness peak count Rpc is greater than or equal to 50. The thermoformed component has good paintability, good coating adhesion and good corrosion resistance, and is very suitable for automotive parts.

The present disclosure relates to a zinc plated steel sheet having excellent fatigue strength of electrical resistance spot welds and a method for manufacturing the same. According to an aspect of the present disclosure, a zinc plated steel sheet includes a base steel sheet and a zinc-based plating layer formed on a surface of the base steel sheet, wherein a concentration profile of one or two of oxygen, and silicon and manganese measured in a depth direction from the surface of the base steel sheet has a maximum point in the depth direction from the surface, and an absolute value of a difference between a depth at which the maximum point of the concentration profile of oxygen is formed and a depth at which the maximum point of the concentration profile of one of silicon and manganese is formed is 0.5 μm or less.

A high strength and corrosion resistant ferrochrome alloy bulk is disclosed, which comprises, in weight percent: 30-68% Cr, 1.5-8% Ni, 1.6-6% C, and the balance Fe and incidental impurities, of which a Fe/Ni ratio is in a range from 5 to 10 and a Cr/C ratio is in a range between 10 and 33. Experimental data reveal that, samples of the high strength and corrosion resistant ferrochrome alloy bulk all possess hardness above HV400 and excellent corrosion resistance due to the high content of Cr. As a result, experimental data have proved that the high-strength and corrosion-resistant ferrochrome alloy bulk of the present invention has a significant potential to replace conventional high-strength stainless steels, so as to be widely applied in various industrial fields, e.g., aviation, transportation, marine facility components, chemical equipment and pipe fittings, engine parts, turbine blades, valves, bearings, building materials, and so on.