The present application relates to a cerium-tin-based composite oxide catalyst for catalyzing purification of a nitrogen oxide, a preparation method and an application thereof. The catalyst has the following chemical composition: a cerium-tin oxide and an M oxide, wherein the M is selected from any one of or a combination of at least two of P, Ti, Zr, V, Mn, Fe, Cu, Al, Si, Ni, Hf, Nb, Ta, Cr, Mo, W, or Re. According to the present application, a cerium-tin-based composite oxide catalyst having the characteristics such as high catalytic activity, high hydrothermal stability, excellent N.sub.2 generation selectivity, a wide operation temperature window, and adaptation to high space velocity reaction conditions is prepared by means of a non-toxic and harmless raw material and a simple method, and the present application is applicable to a device for catalyzing purification of a mobile source nitrogen oxide represented by diesel vehicle exhaust gas and a fixed source nitrogen oxide represented by flue gas from a coal-fired power plant.

The present application relates to a cerium-tin-based composite oxide catalyst for catalyzing purification of a nitrogen oxide, a preparation method and an application thereof. The catalyst has the following chemical composition: a cerium-tin oxide and an M oxide, wherein the M is selected from any one of or a combination of at least two of P, Ti, Zr, V, Mn, Fe, Cu, Al, Si, Ni, Hf, Nb, Ta, Cr, Mo, W, or Re. According to the present application, a cerium-tin-based composite oxide catalyst having the characteristics such as high catalytic activity, high hydrothermal stability, excellent N.sub.2 generation selectivity, a wide operation temperature window, and adaptation to high space velocity reaction conditions is prepared by means of a non-toxic and harmless raw material and a simple method, and the present application is applicable to a device for catalyzing purification of a mobile source nitrogen oxide represented by diesel vehicle exhaust gas and a fixed source nitrogen oxide represented by flue gas from a coal-fired power plant.

The present invention provides a catalyst for catalytic reduction of an industrial flue gas SO.sub.2 with CO to prepare sulfur, a method for preparing the same and use thereof. A CeO.sub.2 nanocarrier is prepared by using a hydrothermal method, La and Y are loaded as active components, pre-sulfurization is conducted with 6% of SO.sub.2 and 3% of CO, and finally, the catalyst is prepared. The catalyst has high reactivity and sulfur selectivity and strong stability. The by-product sulfur generated by the reaction is recovered with a solvent CS.sub.2, and the solvent CS.sub.2 is recovered by using a distillation process. The preparation method is low in cost, causes no secondary pollution and is high in sulfur recovery rate. The problem of low sulfur production in China at present is solved.

The present invention provides a catalyst for catalytic reduction of an industrial flue gas SO.sub.2 with CO to prepare sulfur, a method for preparing the same and use thereof. A CeO.sub.2 nanocarrier is prepared by using a hydrothermal method, La and Y are loaded as active components, pre-sulfurization is conducted with 6% of SO.sub.2 and 3% of CO, and finally, the catalyst is prepared. The catalyst has high reactivity and sulfur selectivity and strong stability. The by-product sulfur generated by the reaction is recovered with a solvent CS.sub.2, and the solvent CS.sub.2 is recovered by using a distillation process. The preparation method is low in cost, causes no secondary pollution and is high in sulfur recovery rate. The problem of low sulfur production in China at present is solved.

The present invention provides: an interior material having a surface layer which has visible light-responsive photocatalytic activity and which contains two types of titanium oxide microparticles, the two types of titanium oxide microparticles comprising first titanium oxide microparticles, in which a tin component and a transition metal component for enhancing visible light responsiveness (excluding iron group components) are in solid solution, and second titanium oxide microparticles, in which an iron group component is in solid solution; and a method for manufacturing the interior material. The present invention makes it possible to provide an interior material in which visible light-responsive photocatalytic titanium oxide microparticles, which make it possible to easily produce a surface layer (photocatalyst thin film) having high transparency and expressing photocatalytic activity even in response to visible light (400-800 nm) only, are applied onto a surface, whereby it is possible to obtain, under indoor illumination, excellent photocatalytic properties such as an antimicrobial property and a property of breaking down chemical substances in indoor air without adversely affecting the design quality of the article in question.

The present invention provides: an interior material having a surface layer which has visible light-responsive photocatalytic activity and which contains two types of titanium oxide microparticles, the two types of titanium oxide microparticles comprising first titanium oxide microparticles, in which a tin component and a transition metal component for enhancing visible light responsiveness (excluding iron group components) are in solid solution, and second titanium oxide microparticles, in which an iron group component is in solid solution; and a method for manufacturing the interior material. The present invention makes it possible to provide an interior material in which visible light-responsive photocatalytic titanium oxide microparticles, which make it possible to easily produce a surface layer (photocatalyst thin film) having high transparency and expressing photocatalytic activity even in response to visible light (400-800 nm) only, are applied onto a surface, whereby it is possible to obtain, under indoor illumination, excellent photocatalytic properties such as an antimicrobial property and a property of breaking down chemical substances in indoor air without adversely affecting the design quality of the article in question.

The invention is related to a carbon supported catalyst comprising a carbon-comprising support with a BET surface area in a range from 400 m.sup.2/g to 2000 m.sup.2/g, a modifier comprising at least one mixed metal oxide, comprising niobium and titanium, and/or a mixture, comprising niobium oxide and titanium oxide, a catalytically active metal compound, wherein the catalytically active metal compound is platinum or an alloy comprising platinum and a second metal or an intermetallic compound comprising platinum and a second metal, the second metal being selected from the group consisting of cobalt, nickel, chromium, copper, palladium, gold, ruthenium, scandium, yttrium, lanthanum, niobium, iron, vanadium and titanium.

The invention is further related to a process for preparing the carbon supported catalyst.

The invention is related to a carbon supported catalyst comprising a carbon-comprising support with a BET surface area in a range from 400 m.sup.2/g to 2000 m.sup.2/g, a modifier comprising at least one mixed metal oxide, comprising niobium and titanium, and/or a mixture, comprising niobium oxide and titanium oxide, a catalytically active metal compound, wherein the catalytically active metal compound is platinum or an alloy comprising platinum and a second metal or an intermetallic compound comprising platinum and a second metal, the second metal being selected from the group consisting of cobalt, nickel, chromium, copper, palladium, gold, ruthenium, scandium, yttrium, lanthanum, niobium, iron, vanadium and titanium.

The invention is further related to a process for preparing the carbon supported catalyst.

Catalysts for oxidative esterification can be used, for example, fro converting (meth)acrolein to methyl (meth)acrylate. The catalysts are especially notable for high mechanical and chemical stability even over very long time periods, including activity and/or selectivity relatively in continuous operation in media having even a small water content.

Catalysts for oxidative esterification can be used, for example, fro converting (meth)acrolein to methyl (meth)acrylate. The catalysts are especially notable for high mechanical and chemical stability even over very long time periods, including activity and/or selectivity relatively in continuous operation in media having even a small water content.