Disclosed is a follow-up process-omitting type high-strength hot-rolled steel sheet having an excellent yield ratio and a method for manufacturing the same. The hot-rolled steel sheet includes, in percent by weight (wt %), 0.12% or more and less than 0.3% of C, 0.5% or less of Si (excluding 0), 0.1 to 2.5% of Mn, 0.0005 to 0.005% of B, 0.02% or less of P, 0.01% or less of S, and the balance of Fe and inevitable impurities, has a microstructure including at least 95 vol % of martensite, has a yield ratio (yield strength/tensile strength) of 0.75 or more, is manufactured by continuous hot rolling, and is manufactured without performing a follow-up process such as cold rolling and heat treatment.

A method is for manufacturing a high-strength steel sheet having a tensile strength of more than 1100 MPa and a yield strength of more than 700 MPa, a uniform elongation UE of at least 8.0% and a total elongation of at least 10%, made of a steel containing in percent by weight: 0.1%≤C≤0.25%, 4.5%≤Mn≤10%, 1%≤Si≤3%, 0.03%≤Al≤2.5%, the remainder being Fe and impurities resulting from the smelting, the composition being such that CMnIndex=C×(1+Mn/3.5)≤0.6. The method includes annealing a rolled sheet made of said steel by soaking it at an annealing temperature TA higher than the Ac.sub.1 transformation point of the steel but less than 1000° C., cooling the annealed sheet to a quenching temperature QT between 190° C. and 80° C. at a cooling speed sufficient to obtain a structure just after cooling containing martensite and retained austenite, maintaining the steel sheet at an overaging temperature PT between 350° C. and 500° C. for an overaging time Pt of more than 5 s cooling the sheet down to the ambient temperature.

Disclosed is a multi-layer rolled composite board, comprising a transition layer provided between two adjacent composite layers, wherein the transition layer is an anisotropic steel sheet. Also disclosed is a manufacturing method for the multi-layer rolled composite board, the method comprising the following steps: (1) providing a transition layer between adjacent composite layers to assemble a blank, and creating a vacuum between the layers; and (2) performing composite rolling, comprising: heating the blank to 1100-1260° C. and maintaining the temperature for 0.6 h or above, then performing hot rolling at a temperature of Ar3 or above, with the final rolling temperature being controlled to be higher than 820° C., cooling at a speed of 30-100° C./s after rolling, and then coiling, with the coiling temperature being controlled to be 20-750° C. The multi-layer rolled composite board of the present invention can be greatly transformed according to different compositions and processes so as to achieve different strength grades ranging from 150 MPa to 1700 MPa, thereby providing the basis for different specific mechanical properties for the whole steel sheet.

Provided is a high strength steel sheet that has a predetermined chemical composition and is manufactured under optimum conditions, the high strength steel sheet having a steel microstructure including, by area, ferrite: 30% or more and 80% or less, tempered martensite: 3.0% or more and 35% or less, and retained austenite: 8% or more, wherein the quotient of the area fraction of grains of the retained austenite, the grains having an aspect ratio of 2.0 or more and a minor axis length of 1 μm or less, divided by the total area fraction of the retained austenite is 0.3 or more, wherein the quotient of the average Mn content (mass %) in the retained austenite divided by the average Mn content (mass %) in the ferrite is 1.5 or more.

Provided is a high strength steel sheet that has a predetermined chemical composition and is manufactured under optimum conditions, the high strength steel sheet having a steel microstructure including, by area, ferrite: 30% or more and 80% or less, martensite: 5% or more and 35% or less, and retained austenite: 8% or more, wherein the quotient of the area fraction of grains of the retained austenite, the grains having an aspect ratio of 2.0 or more and a minor axis length of 1 μm or less, divided by the total area fraction of the retained austenite is 0.3 or more, wherein the quotient of the average Mn content (mass %) in the retained austenite divided by the average Mn content (mass %) in the ferrite is 1.5 or more.

The steel sheet of the present invention has a steel microstructure containing, in area fraction, martensite: from 20% to 100%, ferrite: from 0% to 80%, and another metal phase: 5% or less, and in which a ratio of a dislocation density in metal phases on a surface of the steel sheet to a dislocation density in the metal phases in a thicknesswise central portion of the steel sheet is from 30% to 80%. The maximum amount of warpage of the steel sheet when the steel sheet is sheared to a length of 1 m in a rolling direction is 15 mm or less.

Provided herein is a high-strength seamless steel pipe, and a method for manufacturing same. A high-strength seamless steel pipe of the present invention has a yield strength of 758 MPa or more, and a K.sub.ILIMIT value of 23.0 MPa√m or more as an evaluation index of sulfide stress corrosion cracking resistance.

Provided is a high strength steel sheet that has a predetermined chemical composition and is manufactured under optimum conditions, the high strength steel sheet having a steel microstructure including, by area, ferrite: 30% or more and 80% or less, tempered martensite: 3.0% or more and 35% or less, and retained austenite: 8% or more, wherein the quotient of the area fraction of grains of the retained austenite, the grains having an aspect ratio of 2.0 or more and a minor axis length of 1 μm or less, divided by the total area fraction of the retained austenite is 0.3 or more, wherein the quotient of the average Mn content (mass %) in the retained austenite divided by the average Mn content (mass %) in the ferrite is 1.5 or more.

The steel sheet of the present invention has a steel microstructure containing, in area fraction, martensite: 20% to 100%, ferrite: 0% to 80%, and another metal phase: 5% or less, in which, on a surface of the steel sheet, a ratio of dislocation density in metal phases at a widthwise edge of the steel sheet to dislocation density in the metal phases at a widthwise center of the steel sheet is 100% to 140%, and, at a thicknesswise center of the steel sheet, a ratio of dislocation density in the metal phases at the widthwise edge of the steel sheet to dislocation density in the metal phases at the widthwise center of the steel sheet is 100% to 140%. The maximum amount of warpage of the steel sheet when the steel sheet is sheared to a length of 1 m in a rolling direction is 15 mm or less.

Provided is an ultra-high-strength reinforcing bar and a method for manufacturing the same are disclosed. In an exemplary embodiment, the ultra-high-strength reinforcing bar includes an amount of 0.10 to 0.45 wt % carbon (C), an amount of 0.5 to 1.0 wt % silicon (Si), an amount of 0.40 to 1.80 wt % manganese (Mn), an amount of 0.10 to 1.0 wt % chromium (Cr), an amount greater than 0 and less than or equal to 0.2 wt % vanadium (V), an amount greater than 0 and less than or equal to 0.4 wt % copper (Cu), an amount greater than 0 and less than or equal to 0.5 wt % molybdenum (Mo), an amount of 0.015 to 0.070 wt % aluminum (Al), an amount greater than 0 and less than or equal to 0.25 wt % nickel (Ni), an amount greater than 0 and less than or equal to 0.1 wt % tin (Sn), an amount greater than 0 and less than or equal to 0.05 wt % phosphorus (P), an amount greater than 0 and less than or equal to 0.03 wt % sulfur (S), an amount of 0.005 to 0.02 wt % nitrogen (N), and the remainder being iron (Fe) and other inevitable impurities.