A steel sheet for the manufacture of a press hardened part is provided, having a composition of: 0.15%≤C≤0.22%, 3.5%≤Mn<4.2%, 0.001%≤Si≤1.5%, 0.020%≤Al≤0.9%, 0.001%≤Cr≤1%, 0.001%≤Mo≤0.3%, 0.001%≤Ti≤0.040%, 0.0003%≤B≤0.004%, 0.001%≤Nb≤0.060%, 0.001%≤N≤0.009%, 0.0005%≤S≤0.003%, 0.001%≤P≤0.020%. A microstructure has less than 50% ferrite, 1% to 20% retained austenite, cementite, such that the surface density of cementite particles larger than 60 nm is lower than 10{circumflex over ( )}7/mm.sup.2, and a complement of bainite and/or martensite, the retained austenite having an average Mn content of at least 1.1*Mn %. Press-hardened steel part obtained by hot forming the steel sheet, and manufacturing methods thereof.

The steel plate has a specific chemical composition, and a microstructure where a volume fraction of martensite at a depth of 1 mm from a surface of the steel plate is 95% or more, and at a depth of 1 mm from a surface of the steel plate, a Vickers hardness at 400° C. is 288 or more, and a Brinell hardness at 25° C. is 360 HBW10/3000 to 490 HBW10/3000.

A steel sheet has a tensile strength of 1310 MPa or higher, a specified chemical composition, and a steel microstructure containing martensite at an area ratio of 70% or more, bainite at an area ratio of 30% or less, and ferrite and retained austenite at a total area ratio of 5% or less, in which, at a ¼ thickness position of the steel sheet, a number density of carbides having long axes of 0.5 μm or more is 60000 carbides/mm.sup.2 or less, in a ¼-to-¾ thickness region of the steel sheet, a number density of inclusion grains having equivalent circle diameters of 4.0 μm or more is 10 grains/mm.sup.2 or more and 30 grains/mm.sup.2 or less, and, in a surface-to-¼ thickness region of the steel sheet, a number density of inclusion grains having equivalent circle diameters of 4.0 μm or more is 27 grains/mm.sup.2 or less.

A steel sheet has a predetermined chemical composition, in which a metallographic structure in a surface layer region ranging from a surface to a position of 20 μm from the surface in a sheet thickness direction consists of ferrite and a secondary phase having a volume fraction of 0.01% to 5.0%, a metallographic structure in an internal region ranging from a position of more than 20 μm from the surface in the sheet thickness direction to a ¼thickness position from the surface in the sheet thickness direction consists of ferrite and a secondary phase having a volume fraction of 2.0% to 10.0%, the volume fraction of the secondary phase in the surface layer region is less than the volume fraction of the secondary phase in the internal region, and in the surface layer region, an average grain size of the secondary phase is 0.01 μm to 4.0 μm, and a texture in which an X.sub.ODF{001}/{111} as the ratio of the intensity of {001} orientation to an intensity of {111} orientation in the ferrite is 0.60 or more and less than 2.00 is included.

A method for producing a high strength steel sheet having a yield strength YS of at least 850 MPa, a tensile strength TS of at least 1180 MPa, a total elongation of at least 14% and a hole expansion ratio HER of at least 30%. The chemical composition of the steel contains: 0.15%≤C≤0.25%, 1.2%≤Si≤1.8%, 2%≤Mn≤2.4%, 0.1%≤Cr≤0.25%, Nb≤0.05%, Ti≤0.05%, Al≤0.50%, the remainder being Fe and unavoidable impurities. The sheet is annealed at an annealing temperature TA higher than Ac3 but less than 1000° C. for more than 30 s, by cooling it to a quenching temperature QT between 275° C. and 325° C., at a cooling speed sufficient to have, just after quenching, a structure consisting of austenite and at least 50% of martensite, the austenite content en.) being such that the final structure can contain between 3% and 15% of residual austenite and between 85 and 97% of the sum of martensite and bainite, without ferrite, heated to a partitioning temperature PT between 420° C. and 470° C. and maintained at this temperature for time between 50 s and 150 s and cooled to the room temperature.

A method for producing a high strength steel sheet having a yield strength YS of at least 850 MPa, a tensile strength TS of at least 1180 MPa, a total elongation of at least 14% and a hole expansion ratio HER of at least 30%. The chemical composition of the steel contains: 0.15%≤C≤0.25%, 1.2%≤Si≤1.8%, 2%≤Mn≤2.4%, 0.1%≤Cr≤0.25%, Nb≤0.05%, Ti≤0.05%, Al≤0.50%, the remainder being Fe and unavoidable impurities. The sheet is annealed at an annealing temperature TA higher than Ac3 but less than 1000° C. for more than 30 s, by cooling it to a quenching temperature QT between 275° C. and 325° C., at a cooling speed sufficient to have, just after quenching, a structure consisting of austenite and at least 50% of martensite, the austenite content en.) being such that the final structure can contain between 3% and 15% of residual austenite and between 85 and 97% of the sum of martensite and bainite, without ferrite, heated to a partitioning temperature PT between 420° C. and 470° C. and maintained at this temperature for time between 50 s and 150 s and cooled to the room temperature.

A steel sheet with a tensile strength (TS) of 1180 MPa or more, a member, and a method for producing them. In a region of the steel sheet within 4.9 μm in the thickness direction, a region with a Si concentration not more than one-third of the Si concentration in the chemical composition of the steel sheet and with a Mn concentration not more than one-third of the Mn concentration in the chemical composition of the steel sheet has a thickness of 1.0 μm or more. The lowest Si concentration L.sub.Si and the lowest Mn concentration L.sub.Mn in the region within 4.9 μm in the thickness direction from the surface of the steel sheet and a Si concentration T.sub.Si and a Mn concentration T.sub.Mn at a quarter thickness position of the steel sheet satisfy the following formula (1):

L.sub.Si+L.sub.Mn≤(T.sub.Si+T.sub.Mn)/4  (1).

The high-strength hot-dip galvanized steel sheet, which includes a hot-dip galvanized coating layer on a surface of the steel sheet, has a component composition containing, in mass %, C: 0.07% to 0.20%, Si: 0.1% to 2.0%, Mn: 2.0% to 3.5%, P: 0.05% or less, S: 0.05% or less, and sol. Al: 0.005% to 0.1%, with the balance being Fe and incidental impurities; and has a steel microstructure containing, in area fraction, 60% or less of ferrite, 40% or more of tempered martensite, and 10% or less of fresh martensite and having a void number density of 1,500/mm.sup.2 or less in a bent portion in the VDA bending test.

A method for producing a steel includes preparing a steel sheet having a chemical composition in % by mass of: C: 0.05 to 0.40%, Si: 0 to 2.0%, Mn: 1.0 to 3.0%, Al: 0.010 to 1.0%, P: more than 0% and 0.100% or less, S: more than 0% and 0.010% or less, N: more than 0% and 0.010% or less, B: 0.0005 to 0.010%, and iron; heating the steel sheet to Ac1 point (° C.) or higher and lower than Ac3 point (° C.)+10° C.; processing the steel sheet by applying a strain of 0.5% or more thereto at 675° C. or higher and lower than Ac3 point+10° C.; holding or gradually cooling the steel sheet at an average cooling rate of 0 to 15° C./sec for 1 second or more and 120 seconds or less; and cooling the steel sheet to Ms point (° C.)−50° C.

A steel sheet for the manufacture of a press hardened part is provided, having a composition of: 0.15%≤C≤0.22%, 3.5%≤Mn<4.2%, 0.001%≤Si≤1.5%, 0.020%≤Al≤0.9%, 0.001%≤Cr≤1%, 0.001%≤Mo≤0.3%, 0.001%≤Ti≤0.040%, 0.0003%≤B≤0.004%, 0.001%≤Nb≤0.060%, 0.001%≤N≤0.009%, 0.0005%≤S≤0.003%, 0.001%≤P≤0.020%. A microstructure has less than 50% ferrite, 1% to 20% retained austenite, cementite, such that the surface density of cementite particles larger than 60 nm is lower than 10{circumflex over ( )}7/mm.sup.2, and a complement of bainite and/or martensite, the retained austenite having an average Mn content of at least 1.1*Mn %. Press-hardened steel part obtained by hot forming the steel sheet, and manufacturing methods thereof.