A blank material is formed from a steel sheet, a first quenching of the blank material is performed, and a second quenching of the blank material is performed after the first quenching. When the first quenching is performed, the blank material is heated to a first temperature of not lower than (Ac3 point—50)° C. nor higher than 1200° C. at an average heating rate of 2° C./sec or more, and the blank material is cooled from the first temperature to a second temperature of 250° C. or lower. When the second quenching is performed, the blank material is heated from the second temperature to a third temperature of not lower than (Ac3 point—50)° C. nor higher than 1200° C. at an average heating rate of 2° C./sec or more, and the blank material is cooled from the third temperature to a fourth temperature of 250° C. or lower. Forming of the blank material is performed in the first quenching or the second quenching or both of the above.

A hot press processing apparatus 1 includes: a heating step of heating a workpiece W; a pressing step of press-molding, by an upper die 11 and a lower die 12, the workpiece W heated in the heating step after loading the workpiece W between the upper die 11 and the lower die 12; and a cooling step of bringing the coolant into contact with a front surface of the workpiece W that is molded and placed in a pressed state by the pressing step, to thereby cool the workpiece W and place the workpiece W in a quenched state. In the hot press processing apparatus 1, the workpiece W molded and placed in the pressed state by the pressing step forms gaps c2 with respect to both of the upper die 11 and the lower die 12 so as to allow deformation at time of the cooling step except for an accuracy-guaranteed section Wr in the workpiece W.

A hot press processing apparatus 1 includes: a heating step of heating a workpiece W; a pressing step of press-molding, by an upper die 11 and a lower die 12, the workpiece W heated in the heating step after loading the workpiece W between the upper die 11 and the lower die 12; and a cooling step of bringing the coolant into contact with a front surface of the workpiece W that is molded and placed in a pressed state by the pressing step, to thereby cool the workpiece W and place the workpiece W in a quenched state. In the hot press processing apparatus 1, the workpiece W molded and placed in the pressed state by the pressing step forms gaps c2 with respect to both of the upper die 11 and the lower die 12 so as to allow deformation at time of the cooling step except for an accuracy-guaranteed section Wr in the workpiece W.

A method for producing a press-mold-hardened part includes providing a steel strip having an aluminium-based coating; applying an inorganic, iron-containing conversion layer to the aluminium-based coating with a layer weight in relation to iron of 3-30 mg/m2; cold-rolling the steel strip to form a flexibly rolled strip with strip sections of different sheet thickness; cutting an initial sheet metal blank out of the flexibly rolled strip, with the blank having different sheet thicknesses with thinnest and thickest sheet sections; press-mold-hardening the initial sheet metal blank to form a part. Alternatively, the cold-rolling can take place before the cutting, and the application of the conversion layer can take place before or after the cutting, or, instead of the cold-rolling, at least two steel strip sections having an aluminium-based coating and different sheet thicknesses can be welded together, where the application of the conversion layer can take place before or after welding.

A method for producing a press-mold-hardened part includes providing a steel strip having an aluminium-based coating; applying an inorganic, iron-containing conversion layer to the aluminium-based coating with a layer weight in relation to iron of 3-30 mg/m2; cold-rolling the steel strip to form a flexibly rolled strip with strip sections of different sheet thickness; cutting an initial sheet metal blank out of the flexibly rolled strip, with the blank having different sheet thicknesses with thinnest and thickest sheet sections; press-mold-hardening the initial sheet metal blank to form a part. Alternatively, the cold-rolling can take place before the cutting, and the application of the conversion layer can take place before or after the cutting, or, instead of the cold-rolling, at least two steel strip sections having an aluminium-based coating and different sheet thicknesses can be welded together, where the application of the conversion layer can take place before or after welding.

The method for heating a metal component to a target temperature, in which the component has a preliminary coating and is passed through a furnace that has at least four zones, which can be respectively adjusted to an individual zone temperature, wherein the component is passed successively through at least an initial heating zone, a plateau zone, a peak heating zone and an end zone and wherein the initial heating zone is adjusted to an initial heating temperature, the plateau zone is adjusted to a plateau temperature, the peak heating zone is adjusted to a peak temperature and the end zone is adjusted to the target temperature, the plateau temperature being chosen such that the temperature of the component in the plateau zone lies in a band around a melting temperature of the preliminary coating which is characterized in that the peak temperature lies by at least 100 K above the target temperature.

A method of manufacturing a hot-stamped part includes: inserting a blank into a heating furnace including a plurality of sections with different temperature ranges; step heating the blank in multiple stages; and soaking the blank at a temperature of about Ac3 to about 1,000° C., wherein in the step of heating the blank, a temperature condition in the heating furnace satisfies the following equation: 0<(Tg−Ti)/Lt<0.025° C./mm, where Tg denotes a soaking temperature (° C.), Ti denotes an initial temperature (° C.) of the heating furnace, and Lt denotes a length (mm) of step heating sections.

A cooling method for a workpiece includes placing entirety of the workpiece in an inner space of a recess provided on a molding surface of a lower mold, pressing or restraining the workpiece by a mold including the lower mold and an upper mold in which a protrusion corresponding to the recess of the lower mold is provided on a molding surface, supplying a liquid coolant to the inner space of the recess through a coolant supply passage provided in at least one of the lower mold and the upper mold by a pump, and discharging air in the inner space of the recess upward through an air escape passage, and cooling the workpiece by immersing the entirety of the workpiece, which has been heated, in the liquid coolant that fills the recess.

A cooling method for a workpiece includes placing entirety of the workpiece in an inner space of a recess provided on a molding surface of a lower mold, pressing or restraining the workpiece by a mold including the lower mold and an upper mold in which a protrusion corresponding to the recess of the lower mold is provided on a molding surface, supplying a liquid coolant to the inner space of the recess through a coolant supply passage provided in at least one of the lower mold and the upper mold by a pump, and discharging air in the inner space of the recess upward through an air escape passage, and cooling the workpiece by immersing the entirety of the workpiece, which has been heated, in the liquid coolant that fills the recess.

A tailor-welded blank is made of two steels, one steel of Alloy A and one steel of Alloy B. Alloy A comprises 0.10-0.50 wt % C, 0.1-0.5 wt % Si, 2.0-8.0 wt % Mn, 0.0-6.0 wt % Cr, 0.0-2.0 wt % Mo, 0.0-0.15 wt % Ti, and 0.0-0.005 wt % B and wherein Alloy B comprises 0.06-0.12 wt % C, 0.1-0.25 wt % Si, 1.65-2.42 wt % Mn, 0.0-0.70 wt % Cr, 0.08-0.40 wt % Mo, 0.0-0.05 wt % V, and 0.01-0.05 wt % Ti.