A thick-wall oil-well steel pipe has a wall thickness of 40 mm or more, excellent SSC resistance and high strength. The thick-wall oil-well steel pipe has a composition containing, in mass %, C: 0.40 to 0.65%, Si: 0.05 to 0.50%, Mn: 0.10 to 1.0%, P: 0.020% or less, S: 0.0020% or less, sol. Al: 0.005 to 0.10%, Cr more than 0.40 to 2.0%, Mo: more than 1.15 to 5.0%, Cu: 0.50% or less, Ni: 0.50% or less, N: 0.007% or less, and O: 0.005% or less. The number of carbide which has a circle equivalent diameter of 100 nm or more and contains 20 mass % or more of Mo is 2 or less per 100 mm.sup.2. The thick-wall oil-well steel pipe has yield strength of 827 MPa or more. A difference between a maximum value and a minimum value of the yield strength in the wall-thickness direction is 45 MPa or less.

A steel product bent by heating to 600° C. or more, specifically a heat treated steel product having high strength and excellent chemical conversion coating ability which has scale with FeO content of 90% or more, having a thickness of 1 μm or less on the surface.

The present invention relates to a apparatus for statically quenching a product (1) coming from a rolling plant, comprising a seat for housing the product (1) so that, when the product (1) is housed there, its main development axis (A) coincides with the positioning axis (Z), a series of nozzles (4) arranged around the positioning axis (Z), along a curvilinear surface (3), open at the bottom, and adjustable so as to dispense a flow which is tangential to the surface of the product (1). The invention also relates to a process for static quenching of the product, implementable by such apparatus.

Provided is a high-strength seamless steel pipe having the composition which contains, by mass %, 0.20 to 0.50% C, 0.05 to 0.40% Si, 0.3 to 0.9% Mn, 0.015% or less P, 0.005% or less S, 0.005 to 0.1% Al, 0.008% or less N, more than 0.6% and 1.7% or less Cr, more than 1.0% and 3.0% or less Mo, 0.01 to 0.30% V, 0.001% or more and less than 0.01% Nb, 0.0003 to 0.0030% B, and 0.0030% or less O (oxygen). The high-strength seamless steel pipe has the microstructure where a volume fraction of a tempered martensitic phase is 95% or more, and prior austenitic grains have a grain size number of 8.5 or more, and a segregation degree index Ps which is defined by a formula Ps=8.1 (X.sub.Si+X.sub.Mn+X.sub.Mo)+1.2X.sub.P is set to less than 65.

To provide an oil-well steel pipe having excellent SSC resistance. The oil-well steel pipe according to the present invention contains, by mass percent, C: 0.15 to 0.35%, Si: 0.1 to 0.75%, Mn: 0.1 to 1.0%, Cr: 0.1 to 1.7%, Mo: 0.1 to 1.2%, Ti: 0.01 to 0.05%, Nb: 0.010 to 0.030%, Al: 0.01 to 0.1%, P: at most 0.03%, S: at most 0.01%, N: at most 0.007%, and O: at most 0.01%, the balance being Fe and impurities. The Ti content and the Nb content in a residue obtained by bromine-methanol extraction satisfy equation (1):
100×[Nb]/([Ti]+[Nb])≦27.5  (1)
where the Ti content (mass %) and the Nb content (mass %) in the residue are substituted for [Ti] and [Nb].

Provided is a high-strength seamless steel pipe having the composition which contains, by mass %, 0.20 to 0.50% C, 0.05 to 0.40% Si, 0.3 to 0.9% Mn, 0.015% or less P, 0.005% or less S, 0.005 to 0.1% Al, 0.008% or less N, 0.6 to 1.7% Cr, 0.4 to 1.0% Mo, 0.01 to 0.30% V, 0.01 to 0.06% Nb, 0.0003 to 0.0030% B, and 0.0030% or less O (oxygen). The high-strength seamless steel pipe has the microstructure where a volume fraction of a tempered martensitic phase is 95% or more, and prior austenitic grains have a grain size number of 8.5 or more, and a segregation degree index Ps which is defined by a formula Ps=8.1 (X.sub.Si+X.sub.Mn+X.sub.Mo)+1.2X.sub.P relating to X.sub.M which is a ratio between a segregated portion content and an average content is set to less than 65.

A pipe system for oil country tubular goods (OCTG) and a method of manufacturing the OCTG pipe system is disclosed. The pipe system includes at least one OCTG pipe having a pipe body, the pipe body having at least one connection end formed in unipartite and materially integral manner with the pipe body for coupling to a second OCTG pipe. The OCTG pipe is formed in seamless fashion from a hardenable steel alloy, and the connection end has a yield strength higher than the yield strength of the pipe body.

Provided is a wire rod that has superior machinability by cutting regardless of the type of tool material and the type of lubricant and even in the case where no lubricant is used. A wire rod for cutting work comprises: a specific chemical composition; and Vickers hardness that satisfies the following expressions (1) and (2) in the case where an average aspect ratio of ferrite grains at a position of ¼ of a diameter from a surface of the wire rod for cutting work is more than 2.8, and satisfies the following expressions (3) and (4) in the case where the average aspect ratio is 2.8 or less,
H.sub.ave≤350  (1)
H.sub.σ≤30  (2)
H.sub.ave≤250  (3)
H.sub.σ≤20  (4).

The seamless steel pipe according to the present disclosure includes a chemical composition consisting of, in mass %, C: 0.030% or less, Si: 1.00% or less, Mn: 1.00% or less, P: 0.030% or less, S: 0.0050% or less, Al: 0.001 to 0.100%, N: 0.0500% or less, O: 0.050% or less, Ni: 3.00 to 6.50%, Cr: more than 10.00 to 13.40%, Mo: 0.50 to 4.00%, V: 0.01 to 1.00%, Ti: 0.010 to 0.300%, and Co: 0.010 to 0.300%, with the balance being Fe and impurities, and satisfying Formula (1), and a microstructure containing, in volume ratio, 80.0% or more of martensite, wherein a depassivation pH of an inner surface is 3.50 or less.

Cr+2.0Mo+0.5Ni+0.5Co≥16.0  (1)

A seamless steel pipe is provided that has a chemical composition which consists of, by mass %, C: 0.10 to 0.20%, Si: 0.05 to 1.0%, Mn: 0.05 to 1.2%, P≤0.025%, S≤0.005%, Cu≤0.20%, N≤0.007%, Ni: 0.20 to 0.50%, Cr: 0.30% or more and less than 0.50%, Mo: 0.30 to 0.50%, Nb: 0.01 to 0.05%, Al: 0.001 to 0.10%, B: 0.0005 to 0.0020%, Ti: 0.003 to 0.050%, V: 0.01 to 0.20%, a total of any one or more elements among Ca, Mg and REM: 0 to 0.025%, and the balance: Fe and impurities, and for which Pcm (=C+(Si/30)+(Mn/20)+(Cu/20)+(Ni/60)+(Cr/20)+(Mo/15)+(V/10)+5B)≤0.30. The steel micro-structure includes, in area %, tempered martensite ≥90%. The tensile strength is 980 MPa or more, and a Charpy impact value at −40° C. using a 2 mm V-notch test specimen is 75 J/cm.sup.2 or more.