Embodiments disclosed herein relate to production of amorphous alloys having compositions of iron, chromium, molybdenum, carbon and boron for usage in additive manufacturing, such as in layer-by-layer deposition to produce multi-functional parts. Such parts demonstrate ultra-high strength without sacrificing toughness and also maintain the amorphous structure of the materials during and after manufacturing processes. An Amorphous alloy composition has a formula Fe.sub.100-(a+b+c+d)Cr.sub.aMo.sub.bC.sub.cB.sub.d, wherein a, b, c and d represent an atomic percentage, wherein: a is in the range of 10 at. % to 35 at. %; b is in the range of 10 at. % to 20 at. %; c is in the range of 2 at. % to 5 at. %; and d is in the range of 0.5% at. % to 3.5 at. %.

This invention relates to a preparation method of rare earth oxide dispersion strengthened fee grain tungsten materials, the mass percent of the rare earth oxide is of 0.1-2%, and the rest ingredient is W. Weigh soluble rare earth salt and tungstate, dissolve into water to made into 50-100 g/L of rare earth salt solution and 150-300 g/L of tungstate solution, respectively. Firstly, add trace alkali in rare earth salt solution to control pH in 7-8, then add organic dispersant and stir to form evenly suspended R(OH).sub.3 particle colloid (R refers to rare earth element). Secondly pour the tungstate solution into the R(OH).sub.3colloid, add trace acid to control pH in 6-7, then add organic dispersant and stir to form tungstic acid micro particles, which wrap around the colloidal particles, forming coprecipitation coating particle colloid. Thirdly, the coprecipitation coating particle colloidal is spray-dried, forming tungsten and rare earth oxide compound precursor powder. Alter that, ultrafine or nanoscale tungsten powder with particle size of 50˜500 nm is obtained through a process of calcination subsequent with hydrogen thermal reduction. Finally, the tungsten powder is subjected to ordinary compression molding and then conventional high temperature sintering. The trace rare earth oxide dispersion strengthened high performance fine grain tungsten materials prepared by this invention, its density is close to full density (98.5% or higher), its grain size is uniform and very fine (average in 5˜10 microns), and the rare earth oxides particles evenly distribute in tungsten intracrystalline or grain, boundary with particle size of 100˜500 nm.

In some examples, a method for additive manufacturing an article, the method including depositing a filament via a filament delivery device to form at least one track of the deposited filament, the at least one track of the deposited filament forming at least a portion of a preform article, wherein the filament includes a sacrificial binder and a powder, wherein the powder includes a plurality of elongated particles with each respective particle defining a longitudinal axis, wherein the longitudinal axes of the plurality of particles are substantially aligned with each other within the at least one track of the deposited filament; removing substantially all the binder from the at least one track of the preform article to form a powder article; and sintering the powder article to form a sintered article.

Mixed powder that contains first hard particles, second hard particles, graphite particles, and iron particles is used to manufacture a sintered alloy. The first hard particle is a Fe—Mo—Cr—Mn based alloy particle, the second hard particle is a Fe—Mo—Si based alloy particle. The mixed powder contains 5 to 50 mass % of the first hard particles, 1 to 8 mass % of the second hard particles, and 0.5 to 1.0 mass % of the graphite particles when total mass of the first hard particles, the second hard particles, the graphite particles, and the iron particles is set as 100 mass %.

Mixed powder that contains first hard particles, second hard particles, graphite particles, and iron particles is used to manufacture a sintered alloy. The first hard particle is a Fe—Mo—Cr—Mn based alloy particle, the second hard particle is a Fe—Mo—Si based alloy particle. The mixed powder contains 5 to 50 mass % of the first hard particles, 1 to 8 mass % of the second hard particles, and 0.5 to 1.0 mass % of the graphite particles when total mass of the first hard particles, the second hard particles, the graphite particles, and the iron particles is set as 100 mass %.

A molding composition contains a powder, a wax, an adhesive component, a molding component, and a plasticizer, in which a melt flow rate of the adhesive component at 190° C. is 200 g/10 min or more, and a density of the plasticizer is 1.0 g/cm.sup.3 or less.

A molding composition contains a powder, a wax, an adhesive component, a molding component, and a plasticizer, in which a melt flow rate of the adhesive component at 190° C. is 200 g/10 min or more, and a density of the plasticizer is 1.0 g/cm.sup.3 or less.

Provided are an apparatus for manufacturing a compound powder, a method of manufacturing an iron-boron compound powder by using the apparatus, a boron alloy powder mixture, a method of manufacturing the boron alloy powder mixture, a combined powder structure, a method of manufacturing the combined powder structure, a steel pipe, and a method of manufacturing the steel pipe The method of manufacturing the boron alloy powder mixture includes: preparing a mixed powder including a boron iron alloy powder and a target powder; heat-treating the mixed powder to boronize at least a portion of the target powder and de-boronize at least a portion of the boron iron alloy powder, thereby de-boronizing the boron iron alloy powder to reduce the melting point of the boron iron alloy powder.

A medical device and a method and process for at least partially forming a medical device, which medical device has improved physical properties. The one or more improved physical properties of the novel metal alloy can be achieved in the medical device without having to increase the bulk, volume and/or weight of the medical device.

Provided is a master alloy for a sputtering target, wherein, when elements constituting the master alloy are following X1, X2, Y1, Y2, Y2, and Y3; specifically, where X1 is one or two types of Ta or W; X2 is at least one type of Ru, Mo, Nb or Hf; Y1 is one or two types of Cr or Mn; Y2 is one or two types of Co or Ni; and Y3 is one or two types of Ti or V, the master alloy comprises any one combination of X1-Y1, X1-Y2, X1-Y3, X2-Y1, and X2-Y2 of the foregoing constituent elements. The present invention consequently yields superior effects of being able to obtain a sintered sputtering target with few defects and having a high-density and uniform alloy composition, and, by using this target, to realize the deposition of an alloy barrier film with uniform quality and few particles at a high speed.