A grain oriented electrical steel sheet includes a base steel sheet, a glass film, and a tension-insulation coating. When a glow discharge emission spectroscopy is conducted from a surface of the glass film toward a depth direction, an analysis starting time Ts, a time T.sup.Al.sub.p at which Al shows a maximum emission intensity, an Al emission intensity F(T.sup.Al.sub.p) at the T.sup.Al.sub.p, a time T.sup.Si.sub.p at which Si shows a maximum emission intensity, and an Al emission intensity F(T.sup.Si.sub.p) at the T.sup.Si.sub.p satisfy 0.05≤F(T.sup.Si.sub.p)/F(T.sup.Al.sub.p)≤0.50 and 2.0≤(T.sup.Al.sub.p−Ts)/(T.sup.Si.sub.p−Ts)≤5.0.

A grain oriented electrical steel sheet includes a base steel sheet, a glass film, and a tension-insulation coating. When a glow discharge emission spectroscopy is conducted from a surface of the glass film toward a depth direction, an analysis starting time Ts, a time T.sup.Al.sub.p at which Al shows a maximum emission intensity, an Al emission intensity F(T.sup.Al.sub.p) at the T.sup.Al.sub.p, a time T.sup.Si.sub.p at which Si shows a maximum emission intensity, and an Al emission intensity F(T.sup.Si.sub.p) at the T.sup.Si.sub.p satisfy 0.05≤F(T.sup.Si.sub.p)/F(T.sup.Al.sub.p)≤0.50 and 2.0≤(T.sup.Al.sub.p−Ts)/(T.sup.Si.sub.p−Ts)≤5.0.

An electric resistance welded steel pipe or tube comprises: a base metal being a steel sheet having a specific chemical composition and an electric resistance weld portion having a bond width of 40×10.sup.−6 m or more and 120×10.sup.−6 m or less, wherein C.sub.0-C.sub.1 is 0.05 mass % or less, where C.sub.0-C.sub.1 is a difference between C.sub.1 in mass % which is a minimum C content of the electric resistance weld portion and Co in mass % which is a C content of the steel sheet, and a depth of a total decarburized layer in each of an inner surface layer and an outer surface layer of the electric resistance welded steel pipe or tube is 50×10.sup.−6 m or less.

An electric resistance welded steel pipe or tube comprises: a base metal being a steel sheet having a specific chemical composition and an electric resistance weld portion having a bond width of 40×10.sup.−6 m or more and 120×10.sup.−6 m or less, wherein C.sub.0-C.sub.1 is 0.05 mass % or less, where C.sub.0-C.sub.1 is a difference between C.sub.1 in mass % which is a minimum C content of the electric resistance weld portion and Co in mass % which is a C content of the steel sheet, and a depth of a total decarburized layer in each of an inner surface layer and an outer surface layer of the electric resistance welded steel pipe or tube is 50×10.sup.−6 m or less.

A method for producing a steel strip with a multiphase structure by which the production of complex geometries with a high energy-absorption capacity and high resistance to edge cracking is provided achieving a high yield strength or high yield-strength ratio and a high elongation at break, comprising producing a rolled steel strip of particular elements, and first annealing the steel strip at a temperature of between 750° C. and 950° C., and subsequently first cooling of the steel strip to a temperature of between 200° C. and 500° C. at an average cooling rate of 2 K/s to 150 K/s, further cooling of the steel strip to a supercooling temperature below 100° C. at an average cooling rate of 1 K/s to 50 K/s, final annealing of the steel strip with a Hollomon-Jaffe parameter, and final cooling of the steel strip to room temperature at an average cooling rate of 1 K/s to 160 K/s.

A method for producing a steel strip with a multiphase structure by which the production of complex geometries with a high energy-absorption capacity and high resistance to edge cracking is provided achieving a high yield strength or high yield-strength ratio and a high elongation at break, comprising producing a rolled steel strip of particular elements, and first annealing the steel strip at a temperature of between 750° C. and 950° C., and subsequently first cooling of the steel strip to a temperature of between 200° C. and 500° C. at an average cooling rate of 2 K/s to 150 K/s, further cooling of the steel strip to a supercooling temperature below 100° C. at an average cooling rate of 1 K/s to 50 K/s, final annealing of the steel strip with a Hollomon-Jaffe parameter, and final cooling of the steel strip to room temperature at an average cooling rate of 1 K/s to 160 K/s.

This hot-stamping formed article includes a steel sheet, all or part of the steel sheet has a predetermined chemical composition, at a ¼ depth position of a sheet thickness from a surface of the steel sheet, a microstructure contains, by vol %, more than 90.0% of martensite, the average value of Vickers hardness in a region that is 0.3 mm in a sheet thickness direction and 0.6 mm in a direction orthogonal to the sheet thickness direction is 670 or more, the standard deviation of the Vickers hardness in the region is 20 or less, and the tensile strength is 2300 MPa or more.

This hot-stamping formed article includes a steel sheet, all or part of the steel sheet has a predetermined chemical composition, at a ¼ depth position of a sheet thickness from a surface of the steel sheet, a microstructure contains, by vol %, more than 90.0% of martensite, the average value of Vickers hardness in a region that is 0.3 mm in a sheet thickness direction and 0.6 mm in a direction orthogonal to the sheet thickness direction is 670 or more, the standard deviation of the Vickers hardness in the region is 20 or less, and the tensile strength is 2300 MPa or more.

There are provided a high-strength hot-rolled steel sheet having a tensile strength of 980 MPa or more and a production method therefor. The high-strength hot-rolled steel sheet has a predetermined component composition and a microstructure containing 75.0% or more by area and less than 97.0% by area of a primary phase composed of an upper bainite phase, the primary phase having an average grain size of 12.0 μm or less, and more than 3.0% by area and 25.0% or less by area of a secondary phase that is a structure composed of one or two of a lower bainite phase and/or a tempered martensite phase, and a martensite phase, in which the number density of grains of the secondary phase having an equivalent circular diameter of 0.5 μm or more is 150,000 grains/mm.sup.2 or less, and the steel sheet has an arithmetic mean surface roughness of 2.00 μm or less.

A grain-oriented electrical steel sheet includes: a silicon steel sheet including Si and Mn; a glass film arranged on a surface of the silicon steel sheet; and an insulation coating arranged on a surface of the glass film, wherein the glass film includes a Mn-containing oxide.