Provided are a hot-dip zinc plated steel material and a method for preparing same, the hot-dip zinc plated steel material comprising: base iron comprising 0.01-1.6 wt % of Si and 1.2-3.1 wt % of Mn; a Zn—Al—Mg alloy plating layer; and an Al-rich layer formed on the interface of the base iron and Zn—Al—Mg alloy plating layer, wherein the rate of occupied surface area of the Al-rich layer is 70% or higher (including 100%).

The present invention can provide light-colored magnetic particles having a zirconium oxide coating layer formed on a magnetic core, and having a silver coating layer formed on the zirconium oxide coating layer, and a part of the surface of the zirconium oxide coating layer is exposed to the outside, but chemical resistance is excellent, and thus the magnetic particles hardly cause a change of magnetic characteristics so as to be suitable for security elements.

High strength precipitation hardening stainless steel alloy is disclosed. The steel alloy has a composition by weight %, about: 30.0% max nickel (Ni), 0.0 to 15.0% cobalt (Co), 25.0% max chromium (Cr), 5.0% max molybdenum (Mo), 5.0% max titanium (Ti), 5.0% max vanadium (V), about 0.5% max lanthanum (La) and/or cerium (Ce), and in balance iron (Fe) and inevitable impurities. The steel alloy provides a unique combination of corrosion resistance, strength and toughness and is a material for aircraft landing gears and structures.

High strength precipitation hardening stainless steel alloy is disclosed. The steel alloy has a composition by weight %, about: 30.0% max nickel (Ni), 0.0 to 15.0% cobalt (Co), 25.0% max chromium (Cr), 5.0% max molybdenum (Mo), 5.0% max titanium (Ti), 5.0% max vanadium (V), about 0.5% max lanthanum (La) and/or cerium (Ce), and in balance iron (Fe) and inevitable impurities. The steel alloy provides a unique combination of corrosion resistance, strength and toughness and is a material for aircraft landing gears and structures.

The present invention relates to a steel for mold, containing: 0.28 mass %≤C≤0.65 mass %, 0.01 mass %≤Si≤0.30 mass %, 1.5 mass %≤Mn≤3.0 mass %, 0.5 mass %≤Cr≤1.4 mass %, 1.9 mass %≤Mo+W/2≤4.0 mass %, 0.2 mass %≤V≤1.0 mass %, and 0.01≤N≤0.10 mass %, with the balance being Fe and inevitable impurities, in which, in a state after quenching and tempering, the steel has: a (Mo, W) carbide having a diameter of 0.2 μm or less being in an amount of 1.2 mass % or more, a ratio (mass ratio) of the amount of the (Mo, W) carbide to an amount of a Cr carbide being 11 or more, and a hardness change of 15 HRC or less.

The present invention relates to a steel for mold, containing: 0.28 mass %≤C≤0.65 mass %, 0.01 mass %≤Si≤0.30 mass %, 1.5 mass %≤Mn≤3.0 mass %, 0.5 mass %≤Cr≤1.4 mass %, 1.9 mass %≤Mo+W/2≤4.0 mass %, 0.2 mass %≤V≤1.0 mass %, and 0.01≤N≤0.10 mass %, with the balance being Fe and inevitable impurities, in which, in a state after quenching and tempering, the steel has: a (Mo, W) carbide having a diameter of 0.2 μm or less being in an amount of 1.2 mass % or more, a ratio (mass ratio) of the amount of the (Mo, W) carbide to an amount of a Cr carbide being 11 or more, and a hardness change of 15 HRC or less.

The present invention relates to a grain-oriented electrical steel sheet including 2.0 to 6.0 wt % of Si, 0.01 wt % or less (excluding 0 wt %) of C, 0.01 wt % or less (excluding 0 wt %) of N, and 0.005 to 0.1 wt % of Co, and including a balance of Fe and other inevitable impurities.

The present invention relates to a grain-oriented electrical steel sheet including 2.0 to 6.0 wt % of Si, 0.01 wt % or less (excluding 0 wt %) of C, 0.01 wt % or less (excluding 0 wt %) of N, and 0.005 to 0.1 wt % of Co, and including a balance of Fe and other inevitable impurities.

Fe-Al-based plated hot-stamped member exhibiting excellent formed part corrosion resistance and post-coating corrosion resistance and manufacturing method. The hot-stamping member includes Fe-Al-based plated layer on one or both surfaces of a base material, the base material has a predetermined steel component, Fe-Al-based plated layer has a thickness of 10 μm or more and 60 μm or less, formed by A, B, C and D layers sequentially from a surface toward the base material, and each of the four layers is a Fe-Al-based intermetallic compound containing Al, Fe, Si, Mn and Cr for predetermined contents with the balance made up of impurities, the D layer further contains Kirkendall voids each of which cross-sectional area is 3 μm.sup.2-30 μm.sup.2 for 10 pieces/6000 μm.sup.2 or more and 40 pieces/6000 μm.sup.2 or less.

Fe-Al-based plated hot-stamped member exhibiting excellent formed part corrosion resistance and post-coating corrosion resistance and manufacturing method. The hot-stamping member includes Fe-Al-based plated layer on one or both surfaces of a base material, the base material has a predetermined steel component, Fe-Al-based plated layer has a thickness of 10 μm or more and 60 μm or less, formed by A, B, C and D layers sequentially from a surface toward the base material, and each of the four layers is a Fe-Al-based intermetallic compound containing Al, Fe, Si, Mn and Cr for predetermined contents with the balance made up of impurities, the D layer further contains Kirkendall voids each of which cross-sectional area is 3 μm.sup.2-30 μm.sup.2 for 10 pieces/6000 μm.sup.2 or more and 40 pieces/6000 μm.sup.2 or less.