Provided is a steel sheet and a method for manufacturing same, the steel sheet, which can be used for automobile parts and the like, having superb bendability, and excellent balance of strength and ductility and of strength and hole expansion ratio. The steel sheet includes: by wt %, C: 0.25 to 0.75%, Si: 4.0% or less, Mn: 0.9 to 5.0%, Al: 5.0% or less, P: 0.15% or less, S: 0.03% or less, N: 0.03% or less, a balance of Fe, and unavoidable impurities; and as microstructures, ferrite which is a soft structure, and tempered martensite, bainite, and retained austenite which are hard structures.

Provided is a steel sheet and a method for manufacturing same, the steel sheet, which can be used for automobile parts and the like, having superb bendability, and excellent balance of strength and ductility and of strength and hole expansion ratio. The steel sheet includes: by wt %, C: 0.25 to 0.75%, Si: 4.0% or less, Mn: 0.9 to 5.0%, Al: 5.0% or less, P: 0.15% or less, S: 0.03% or less, N: 0.03% or less, a balance of Fe, and unavoidable impurities; and as microstructures, ferrite which is a soft structure, and tempered martensite, bainite, and retained austenite which are hard structures.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.

Provided is a steel sheet and a method for manufacturing same, the steel sheet which can be used for automobile parts and the like, having excellent bending workability, and excellent balance of strength and ductility and of strength and hole expansibility.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

Provided is a steel sheet which can be used for automobile parts and the like, and relates to a steel sheet having a superior balance of strength and ductility and strength and hole expansion ratio and superior bending formability, and a method for manufacturing same.

The present disclosure relates to a high-strength hot-dip galvanized steel sheet having excellent surface quality and electrical resistance spot weldability, and a method for manufacturing the same. A galvanized steel sheet according to an aspect of the present disclosure is a galvanized steel sheet including a base steel sheet and a zinc-based plating layer formed on a surface of the base steel sheet, wherein a ratio (a/b) of a hardness of a surface layer portion (a) to a hardness of an internal portion (b) of the base steel sheet may be less than 0.95.

The present disclosure relates to a high-strength hot-dip galvanized steel sheet having excellent surface quality and electrical resistance spot weldability, and a method for manufacturing the same. A galvanized steel sheet according to an aspect of the present disclosure is a galvanized steel sheet including a base steel sheet and a zinc-based plating layer formed on a surface of the base steel sheet, wherein a ratio (a/b) of a hardness of a surface layer portion (a) to a hardness of an internal portion (b) of the base steel sheet may be less than 0.95.

Disclosed is a stainless steel for a fuel cell separator, more specifically, a stainless steel for a fuel cell separator having a low contact resistance. According to an embodiment of the stainless steel for a fuel cell separator disclosed herein, an arithmetic mean summit curvature Ssc of the surface defined according to the ISO 25178 standard is at least 6.0 μm.sup.−1, a root mean square surface slope Sdq is at least 23, and a contact resistance is at most 10 mΩ.Math.cm.sup.2.

Disclosed is a stainless steel for a fuel cell separator, more specifically, a stainless steel for a fuel cell separator having a low contact resistance. According to an embodiment of the stainless steel for a fuel cell separator disclosed herein, an arithmetic mean summit curvature Ssc of the surface defined according to the ISO 25178 standard is at least 6.0 μm.sup.−1, a root mean square surface slope Sdq is at least 23, and a contact resistance is at most 10 mΩ.Math.cm.sup.2.