A method and arrangement for manufacturing hot dip galvanized rolled high strength steel product is presented. The method comprises providing a rolled steel product, heating and annealing the rolled steel product for creating a layer of iron oxide on the surface of the rolled steel product, cooling the rolled steel product, having the iron oxide layer, in a first cooling step to a temperature in a temperature range of 560-600 C. and holding for 3-10 seconds, quenching said rolled steel product, covered with the layer of iron oxide, in a second cooling step by immersing it into a zinc bath comprising aluminium and having a temperature between 440-450 C. for 1-5 seconds and cooling the rolled steel product in a third cooling step to room temperature. An arrangement for implementing the method is also presented.

Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

Zn alloy plated steel material having excellent weldability and processed-part corrosion resistance and a method for production of Zn alloy plated steel material are provided. In the Zn alloy plated steel material comprising base steel material and a Zn alloy plating layer, the Zn alloy plating layer includes, by wt %, Al: 0.1-5.0%, Mg: 0.1-5.0%, as well as a remainder of Zn and inevitable impurities. The Zn alloy plated steel material includes a lower interface layer and an upper interface layer between the base steel material and the Zn alloy plating layer, wherein the lower interface layer is formed on the base steel material and has a dense structure, and the upper interface layer is formed on the lower interface layer and has a network-type or island-type structure.

This insulated wire includes an insulating coating formed on a surface of a conductive wire body, and a soldered portion for electric conduction. The soldered portion is formed by attaching dicarboxylic acid onto a surface of the insulating coating, and by performing solder plating in a state where the dicarboxylic acid is attached onto the surface of the insulating coating. In addition, this method for manufacturing an insulated wire includes a surface treatment step of attaching the dicarboxylic acid onto a surface of an insulating coating which becomes the soldered portion, and a soldering step of performing the solder plating by immersing the surface treated portion of the insulating coating in a heated solder melt.

A method and arrangement for manufacturing hot dip galvanized rolled high strength steel product is presented. The method comprises providing a rolled steel product, heating and annealing the rolled steel product for creating a layer of iron oxide on the surface of the rolled steel product, cooling the rolled steel product, having the iron oxide layer, in a first cooling step to a temperature in a temperature range of 560-600 C. and holding for 3-10 seconds, quenching said rolled steel product, covered with the layer of iron oxide, in a second cooling step by immersing it into a zinc bath comprising aluminium and having a temperature between 440-450 C. for 1-5 seconds and cooling the rolled steel product in a third cooling step to room temperature. An arrangement for implementing the method is also presented.

Provided is a method of manufacturing a zinc-plated steel sheet. The method includes: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; and zinc plating the annealed steel sheet by dipping in a molten zinc plating bath. Further provided is a method of manufacturing a hot-press part including: coating a metal on the steel sheet on a steel sheet; annealing the metal coated steel sheet; zinc plating the annealed steel sheet by dipping in a molten zinc plating bath; heating the zinc-plated steel sheet; and press forming the heated steel sheet.

A steel sheet with a metallic coating is provided. A composition of the metallic coating includes from 2.0 to 24.0% by weight of zinc, from 7.1 to 12.0% by weight of silicon, optionally from 1.1 to 8.0% by weight of magnesium, and optionally additional elements chosen from Pb, Ni, Zr, or Hf. The content by weight of each additional element is less than 0.3%. A balance of the composition is aluminum, unavoidable impurities and residual elements. A ratio Al/Zn is from 4.0 to 6.0.

A method for coating a metal substrate, such as a steel strip, is disclosed. The method comprises vapor or electro-depositing an alloy control material, as described herein, onto the substrate and passing the substrate through a bath of molten coating material and forming a coating of the coating material onto the deposited alloy control material.

A steel sheet with a metallic coating is provided. A composition of the metallic coating includes from 2.0 to 24.0% by weight of zinc, from 7.1 to 12.0% by weight of silicon, optionally from 1.1 to 8.0% by weight of magnesium, and optionally additional elements chosen from Pb, Ni, Zr, or Hf. The content by weight of each additional element is less than 0.3%. A balance of the composition is aluminum, unavoidable impurities and residual elements. A ratio Al/Zn is from 4.0 to 6.0.

Provided is a ZnAlMg alloy coated checkered steel sheet having on the sheet surface thereof convex part and flat part, wherein: the coating layer has a predetermined chemical composition, and when observing a cross section of cutting edge orthogonal to a longitudinal direction of the convex part and taken along a sheet thickness direction at a central part in the longitudinal direction of the convex part, a layer thickness ratio of the coating layer of the flat part on left and right of the convex part (layer thickness of left coating layer/layer thickness of right coating layer) is from 0.2 to 5.0, and a convex height T?t, where T is a sheet thickness of the substrate checkered steel sheet at the convex part and t is a sheet thickness of the substrate checkered steel sheet at the flat part, and a gap height x between a stationary surface and a sheet surface of the coated checkered steel sheet opposite to the stationary surface in a case in which the coated checkered steel sheet is placed in a stationary position satisfy the following Formulas 1 and 2 below.

x/(T?t)?1.5Formula 1:

0.5<T?t?tFormula 2: