Disclosed herein are laser-assisted metal-organic chemical vapor deposition devices and methods of use thereof.

Disclosed are a semiconductor structure and a manufacturing method therefor, solving a problem that a surface of an epitaxial layer is not easy to flatten as the epitaxial layer has a large stress. The semiconductor structure includes: a substrate; a patterned AlN/AlGaN seed layer on the substrate; and an AlGaN epitaxial layer formed on the patterned AlN/AlGaN seed layer.

Methods and wafers for low etch pit density, low slip line density, and low strain indium phosphide are disclosed and may include an indium phosphide single crystal wafer having a diameter of 4 inches or greater, having a measured etch pit density of less than 500 cm.sup.−2, and having fewer than 5 dislocations or slip lines as measured by x-ray diffraction imaging. The wafer may have a measured etch pit density of 200 cm.sup.−2 or less, or 100 cm.sup.−2 or less, or 10 cm.sup.−2 or less. The wafer may have a diameter of 6 inches or greater. An area of the wafer with a measured etch pit density of zero may at least 80% of the total area of the surface. An area of the wafer with a measured etch pit density of zero may be at least 90% of the total area of the surface.

Methods and wafers for low etch pit density, low slip line density, and low strain indium phosphide are disclosed and may include an indium phosphide single crystal wafer having a diameter of 4 inches or greater, having a measured etch pit density of less than 500 cm.sup.−2, and having fewer than 5 dislocations or slip lines as measured by x-ray diffraction imaging. The wafer may have a measured etch pit density of 200 cm.sup.−2 or less, or 100 cm.sup.−2 or less, or 10 cm.sup.−2 or less. The wafer may have a diameter of 6 inches or greater. An area of the wafer with a measured etch pit density of zero may at least 80% of the total area of the surface. An area of the wafer with a measured etch pit density of zero may be at least 90% of the total area of the surface.

A system for manufacturing one or more single crystals of a semiconductor material by physical vapor transport (PVT) includes a reactor having an inner chamber adapted to accommodate a PVT growth structure for growing the one or more single crystals inside. The reactor accommodates the PVT growth structure in an orientation with a growth direction of the one or more single crystals inside the PVT growth structure substantially horizontal with respect to a direction of gravity or within an angle from horizontal of less than a predetermined value.

Provided is an aluminum nitride film in which, aluminum nitride crystal grains containing a metal element differing from aluminum and substituting for aluminum are main crystal grains of a polycrystalline film formed of crystal grains, and a concentration of the metal element in a grain boundary between the aluminum nitride crystal grains in at least one region of first and second regions corresponding to both end portions of the polycrystalline film in a film thickness direction of the polycrystalline film is higher than a concentration of the metal element in a center region of the aluminum nitride crystal grain in the at least one region, and is higher than a concentration of the metal element in a grain boundary between the aluminum nitride crystal grains in a third region located between the first region and the second region in the film thickness direction of the polycrystalline film.

The present invention includes: transferring a C-plane sapphire thin film 1t having an off-angle of 0.5-5° onto a handle substrate composed of a ceramic material having a coefficient of thermal expansion at 800 K that is greater than that of silicon and less than that of C-plane sapphire; performing high-temperature nitriding treatment on the GaN epitaxial growth substrate 11 and covering the surface of the C-plane sapphire thin film 1t with a surface treatment layer 11a made of AlN; having GaN grow epitaxially on the surface treatment layer 11a; ion-implanting a GaN film 13; pasting and bonding together the GaN film-side surface of the ion-implanted GaN film carrier and a support substrate 12; performing peeling at an ion implantation region 13.sub.ion in the GaN film 13 and transferring a GaN thin film 13a onto the support substrate 12; and obtaining a GaN laminate substrate 10.

An indium phosphide substrate, the phosphide substrate has an angle θ on the main surface side of 0°<θ≤120° for all of the planes A, the indium phosphide substrate has edge rounds on the main surface side and a surface side opposite to the main surface; wherein a chamfered width X.sub.f from the wafer edge on the main surface side is 50 μm or more to 130 μm or less; wherein a chamfered width X.sub.b from the wafer edge on the surface side opposite to the main surface is 150 μm or more to 400 μm or less; and wherein the indium phosphide substrate has a thickness of 330 μm or moreto 700 μm or less.

An indium phosphide substrate, the phosphide substrate has an angle θ on the main surface side of 0°<θ≤120° for all of the planes A, the indium phosphide substrate has edge rounds on the main surface side and a surface side opposite to the main surface; wherein a chamfered width X.sub.f from the wafer edge on the main surface side is 50 μm or more to 130 μm or less; wherein a chamfered width X.sub.b from the wafer edge on the surface side opposite to the main surface is 150 μm or more to 400 μm or less; and wherein the indium phosphide substrate has a thickness of 330 μm or moreto 700 μm or less.

A gallium nitride vapor phase epitaxy apparatus capable of doping magnesium is provided. The apparatus is used in vapor phase epitaxy not using organic metal as a gallium raw material. The apparatus comprises a reactor vessel and a wafer holder. The apparatus comprises a first raw material gas supply pipe configured to supply a first raw material gas containing gallium. The apparatus comprises a second raw material gas supply pipe configured to supply a second raw material gas, which contains nitrogen and configured to react with the first raw material gas. The apparatus comprises a third raw material gas supply pipe configured to supply a third raw material gas containing magnesium. The third raw material gas supply pipe is configured capable of placing a magnesium-based oxide on its supply path. The apparatus comprises a first heating unit configured to heat the magnesium-based oxide in a first temperature range.