The present invention pertains to a phosphate cement composition and process for making such composition. More particularly, it pertains to a phosphate cement coating and process for making the coating for application to a given substrate.

A composition for artificial marble, of the present invention comprises: a binder resin; an inorganic filler excluding zinc oxide; and zinc oxide, wherein the zinc oxide has a size ratio (B/A), in which peak A is a 370 nm to 390 nm region and peak B is a 450 nm to 600 nm region, of approximately 0.01 to 1 during photoluminescence measurement, and has a BET surface area of approximately 10 m.sup.2/g or less.

A composition for artificial marble, of the present invention comprises: a binder resin; an inorganic filler excluding zinc oxide; and zinc oxide, wherein the zinc oxide has a size ratio (B/A), in which peak A is a 370 nm to 390 nm region and peak B is a 450 nm to 600 nm region, of approximately 0.01 to 1 during photoluminescence measurement, and has a BET surface area of approximately 10 m.sup.2/g or less.

The present invention provides a composition for forming a casting mold or a mold liner, comprising solid particles of CaO, SiO, MgO, Al.sub.2O.sub.3 having an average particle size of 20 to 60 μm.

The present invention provides a composition for forming a casting mold or a mold liner, comprising solid particles of CaO, SiO, MgO, Al.sub.2O.sub.3 having an average particle size of 20 to 60 μm.

The present disclosure relates generally to building materials, such as building boards, having improved strength and reduced shrinkage. More particularly, the present disclosure provides building compositions comprising Struvite-K (KMgPO.sub.4.6H.sub.2O), Syngenite (K.sub.2Ca(SO.sub.4).sub.2.H.sub.2O), and one or more silicate additives suitable for use in building materials.

The present disclosure relates generally to building materials, such as building boards, having improved strength and reduced shrinkage. More particularly, the present disclosure provides building compositions comprising Struvite-K (KMgPO.sub.4.6H.sub.2O), Syngenite (K.sub.2Ca(SO.sub.4).sub.2.H.sub.2O), and one or more silicate additives suitable for use in building materials.

A foamed lightweight monolithic refractory castable is provided. The castable includes one or more refractory aggregates as a main constituent, one or more foaming additives in a range of 0.1 wt % to 3.0 wt %, one or more cellulosic powder air-entraining additives in a range of 0.005 wt % to 2.0 wt %, one or more binders in a range of 1 wt % to 40 wt %, and one or more superplasticizers in a range of 0.05 wt % to 0.5 wt %. The refractory aggregates include at least one of alumina and silica. The foaming additives include at least one of alkylbenzene sulfonates, alkene sulfonates, and hydroxylalkane sulfates. The superplasticizers include at least one of sodium polyacrylates, naphthalene sulfonates, polyethylene glycols, polycarboxylates, polyacrylates, and polycarboxylate ethers.

A foamed lightweight monolithic refractory castable is provided. The castable includes one or more refractory aggregates as a main constituent, one or more foaming additives in a range of 0.1 wt % to 3.0 wt %, one or more cellulosic powder air-entraining additives in a range of 0.005 wt % to 2.0 wt %, one or more binders in a range of 1 wt % to 40 wt %, and one or more superplasticizers in a range of 0.05 wt % to 0.5 wt %. The refractory aggregates include at least one of alumina and silica. The foaming additives include at least one of alkylbenzene sulfonates, alkene sulfonates, and hydroxylalkane sulfates. The superplasticizers include at least one of sodium polyacrylates, naphthalene sulfonates, polyethylene glycols, polycarboxylates, polyacrylates, and polycarboxylate ethers.

Disclosed are a method for separately preparing light magnesium oxide and calcium oxide by using dolomite and an application thereof in preparation of a calcium-magnesium composite expanding agent. In the method for preparing light magnesium oxide and calcium oxide, based on the difference in decomposition temperature between magnesium carbonate and calcium carbonate during the calcination and decomposition of dolomite and the difference in the weight of the materials after decomposition, the effective separation of magnesium oxide and calcium oxide is realized by a one-step method, thus separately preparing light magnesium oxide and light calcium oxide. The calcium-magnesium composite expanding agent is prepared by using the foregoing light magnesium oxide and calcium oxide. On the one hand, the present invention solves the problem of the limited origin of the light magnesium oxide raw material of the magnesium expanding component in the calcium-magnesium composite expanding agent.