Corrosion mitigating cement compositions and methods for their preparation are provided. The cement compositions are derived from self-cementing pozzolans and chemical accelerators, retarders, mechanical strength modifiers and corrosion inhibitors. The corrosion inhibitors include boron compounds such as boric acid. Concretes prepared using the cement compositions possess low conductivity and a conductivity which further decreases with aging.

Disclosed are an organic binder-based coating; a composite gypsum board containing face and back cover sheets, an outside surface of the back cover sheet bearing the coating; and a method of preparing composite board where the back cover sheet contains the coating on its outer surface. The coating is formed from a composition comprising an alkaline silicate, a solid filler, and optionally, a borate. An enhancing layer can also be applied to the back cover sheet.

Disclosed are an organic binder-based coating; a composite gypsum board containing face and back cover sheets, an outside surface of the back cover sheet bearing the coating; and a method of preparing composite board where the back cover sheet contains the coating on its outer surface. The coating is formed from a composition comprising an alkaline silicate, a solid filler, and optionally, a borate. An enhancing layer can also be applied to the back cover sheet.

A dry mortar, in particular a cementitious tile adhesive using fibers. A method improves the slip resistance, the flexibility, and/or the consistency of a dry mortar mixed up with water. Moreover, a structure, in particular a floor, a wall or a ceiling, includes a cover element, in particular a tile, whereby the cover element is fixed to the structure with a dry mortar mixed up with water.

A dry mortar, in particular a cementitious tile adhesive using fibers. A method improves the slip resistance, the flexibility, and/or the consistency of a dry mortar mixed up with water. Moreover, a structure, in particular a floor, a wall or a ceiling, includes a cover element, in particular a tile, whereby the cover element is fixed to the structure with a dry mortar mixed up with water.

A multi-component inorganic capsule anchoring system can be used for chemically fastening anchors, bolts, screw anchors, screw bolts, and post-installed reinforcing bars in mineral substrates. The multi-component inorganic capsule anchoring system contains a curable powdery ground-granulated blast-furnace slag-based component A, and an initiator component B in aqueous-phase for initiating a curing process. The powdery ground-granulated blast-furnace slag-based component A contains further silica dust. The component B contains an alkali-silicate component and optionally a plasticizer.

A multi-component inorganic capsule anchoring system can be used for chemically fastening anchors, bolts, screw anchors, screw bolts, and post-installed reinforcing bars in mineral substrates. The multi-component inorganic capsule anchoring system contains a curable powdery ground-granulated blast-furnace slag-based component A, and an initiator component B in aqueous-phase for initiating a curing process. The powdery ground-granulated blast-furnace slag-based component A contains further silica dust. The component B contains an alkali-silicate component and optionally a plasticizer.

The present invention provides means capable of imparting high temporal stability to a hardening aid solution which serves as a raw material and capable of imparting high strength and high quality stability to a hardened body of the self-hardening material, in the hardened body of the self-hardening material that contains a ceramic powder containing Si element at least on the surface thereof. The present invention relates to a hardening aid solution containing Si element, an alkali, and a dispersing medium, wherein the dispersing medium contains water; a dissolution concentration of the Si element is 20000 mass ppm or more; the number of moles of the alkali present in 1 kg of the dispersing medium is 2 mol/kg or more; an absolute value of an amount of change in a dissolution concentration of Si element in a solution obtained by diluting the hardening aid solution by 2 times based on the mass using an aqueous KOH solution having a concentration of 3 mol/L is 2000 mass ppm or less, between before and after a heat dissolution test including heating the solution at a solution temperature of 80° C. for 5 hours, and then allowing the solution to stand in an ambient environment at 25° C. for 1 hour; and the hardening aid solution is used for hardening a powder containing a ceramic powder containing Si element at least on the surface thereof.

The present invention provides means capable of imparting high temporal stability to a hardening aid solution which serves as a raw material and capable of imparting high strength and high quality stability to a hardened body of the self-hardening material, in the hardened body of the self-hardening material that contains a ceramic powder containing Si element at least on the surface thereof. The present invention relates to a hardening aid solution containing Si element, an alkali, and a dispersing medium, wherein the dispersing medium contains water; a dissolution concentration of the Si element is 20000 mass ppm or more; the number of moles of the alkali present in 1 kg of the dispersing medium is 2 mol/kg or more; an absolute value of an amount of change in a dissolution concentration of Si element in a solution obtained by diluting the hardening aid solution by 2 times based on the mass using an aqueous KOH solution having a concentration of 3 mol/L is 2000 mass ppm or less, between before and after a heat dissolution test including heating the solution at a solution temperature of 80° C. for 5 hours, and then allowing the solution to stand in an ambient environment at 25° C. for 1 hour; and the hardening aid solution is used for hardening a powder containing a ceramic powder containing Si element at least on the surface thereof.

This invention discloses a double-liquid grouting slurry, its technology and application for super large diameter underwater shield engineering under high water pressure condition. The materials of slurry I are: 35-45 parts of cement clinker; 15-25 parts of slag; 24-35 parts of fly ash; 15-25 parts of steel slag; 5-15 parts of bentonite; 4-10 parts of limestone tailing; 0.3-2.0 parts of water reducing agent; 0.5-2.5 parts of cellulose. The materials of slurry II are: 0.2-3.8 parts of short-cut fiber; 96-99 parts of sodium silicate solution; 0.8-4.8 parts of viscous polymers. This invention generates the double-liquid slurry preparation process including crushing-screening-milling-group mixing-grouped mixing at different speeds, the volume ratio of slurry I and II is 1:1-10:1 during grouting, and the slurry is injected into the shield void through the six-point position technology at the shield tail and 3+2+1 segment splicing synchronous grouting techniques.