The present disclosure relates to the manufacture of ceramic products by aqueous gelcasting. Exemplary ceramic products include sanitary ware, such as toilets and sinks. The process includes a slurrying step, a mixing step, a molding step involving aqueous gelcasting, a drying step, a glazing step, and a firing step.

A preparation method for improving light efficiency and stability of light storing ceramics is provided. Calcium ethanol solution is added into titanium precursor solution firstly and oleic acid dispersant is added, pure water and the light storing powder are subsequently added to obtain a light-storing powder-calcium titanate gel, and dried, crushed and sieved to obtain xerogel powder. Glass matrix material, sieved xerogel powder and another dispersant are placed into a granulator, and directly mechanically stirred and granulated after adding pure water. A plasticizer is added after stirring 4˜8 h, and continuously stirred for 1˜3 h to obtain a mixture, pressing, drying and firing. Calcium titanate is manually introduced to protect the light-storing powder from hydrolysis or high-temperature oxidation. It can also change the propagation path of fluorescence inside ceramics, improve light absorption and fluorescence output efficiency and is conducive to ceramic molding.

What are described are a process for producing an insulating product for the refractory industry or an insulating material as intermediate for production of such a product, and a corresponding insulating material/insulating product. Likewise described are the use of a matrix encapsulation process in the production of an insulating product for the refractory industry and a corresponding insulating product and/or an insulating material as intermediate for production of such a product.

A bonded abrasive article includes elongate shaped abrasive particles. The elongate shaped abrasive particles comprise an elongate shaped ceramic body having opposed first and second ends joined to each other by at least two longitudinal sidewalls. At least one of the at least two longitudinal sidewalls is concave along its length. At least one of the first and second ends is a fractured surface.

Shot-peening method. Projecting a powder onto a surface. The powder includes sintered particles, more than 95 wt % of the particles are beads. The powder has, in wt % based on the oxides: —ZrO.sub.2 partially stabilized with CeO.sub.2 and Y.sub.2O.sub.3: balance to 100%, CeO.sub.2 and Y.sub.2O.sub.3 present, in mol % according to the sum of ZrO.sub.2, CeO.sub.2 and Y.sub.2O.sub.3, CeO.sub.2: 2.5-11 mol % and Y.sub.2O.sub.3: 0.5-2 mol %, —Al.sub.2O.sub.3; 3-50%—additive chosen from CaO, manganese oxides, ZnO, praseodymium oxides, SrO, copper oxides, 0.2-6% Nd.sub.2O.sub.3, BaO, iron oxides, and mixtures thereof: CaO being less than 2%, —elements other than ZrO.sub.2, CeO.sub.2, Y.sub.2O.sub.3, Al.sub.2O.sub.3, CaO, manganese oxides, ZnO, praseodymium oxides, ≤5% SrO, copper oxides, Nd.sub.2O.sub.3, BaO, and iron oxides: manganese oxides, praseodymium oxides, copper oxides and iron oxides being expressed as MnO, Pr.sub.6O.sub.11, CuO and Fe.sub.2O.sub.3, respectively, and a relative density greater than 95%.

Reaction mixtures, gel compositions that are a polymerized product of the reaction mixtures, shaped gel articles that are formed within a mold cavity and that retain the size and shape of the mold cavity upon removal from the mold cavity, and sintered articles prepared from the shaped gel articles are provided. The sintered article has a shape identical to the mold cavity (except in regions where the mold cavity was overfilled) and to the shaped articles but reduced in size proportional to the amount of isotropic shrinkage. Methods of forming the sintered articles also are provided.

The present invention provides a zirconia sintered body containing a fluorescent agent and having excellent translucency and excellent strength. The present invention also provides a zirconia shaped body and a zirconia calcined body from which the zirconia sintered body can be obtained. The present invention relates to a zirconia sintered body comprising a fluorescent agent, wherein the zirconia sintered body comprises 4.5 to 9.0 mol % yttria, and has a crystal grain size of 180 nm or less, and a three-point flexural strength of 500 MPa or more. The present invention relates to a zirconia shaped body comprising a fluorescent agent, wherein the zirconia shaped body comprises 4.5 to 9.0 mol % yttria, and has a three-point flexural strength of 500 MPa or more after being sintered at 1,100° C. for 2 hours under ordinary pressure, and a crystal grain size of 180 nm or less after being sintered at 1,100° C. for 2 hours under ordinary pressure. The present invention relates to a zirconia calcined body comprising a fluorescent agent, wherein the zirconia calcined body comprises 4.5 to 9.0 mol % yttria, and has a three-point flexural strength of 500 MPa or more after being sintered at 1,100° C. for 2 hours under ordinary pressure, and a crystal grain size of 180 nm or less after being sintered at 1,100° C. for 2 hours under ordinary pressure.

Ceramic particles for use in a solar power tower and methods for making and using the ceramic particles are disclosed. The ceramic particle can include a sintered ceramic material formed from a mixture of a raw material and MnO. The sintered ceramic material can include about 0.01 wt % to about 10 wt % MnO, about 0.1 wt % to about 20 wt % Fe.sub.2O.sub.3, and about 0.01 wt % to about 10 wt % Mn.sub.2O.sub.3. The ceramic particle can have a size from about 8 mesh to about 170 mesh.

Various shaped abrasive particles are disclosed. Each shaped abrasive particle includes a body having at least one major surface and a side surface extending from the major surface.

The present disclosure relates to the manufacture of ceramic products by aqueous gelcasting. Exemplary ceramic products include sanitary ware, such as toilets and sinks. The process includes a slurrying step, a mixing step, a molding step involving aqueous gelcasting, a drying step, a glazing step, and a firing step.