The invention relates to a sinter blank (1) for producing a dental prosthesis in at least one sintering process, the sinter blank (1) including at least one product area (2), from which the dental prosthesis is produced, and at least one strut (3) that is to be removed after the sintering process, the strut (3) having at least one sliding knob (4) for supporting the strut (3) on a base surface (5) during the sintering process.

A method of manufacturing ceramic tape includes a step of directing a tape of partially-sintered ceramic into a furnace. The tape is partially-sintered such that grains of the ceramic are fused to one another yet the tape still includes at least 10% porosity by volume, where the porosity refers to volume of the tape unoccupied by the ceramic. The method further includes steps of conveying the tape through the furnace and further sintering the tape as the tape is conveyed through the furnace. The porosity of the tape decreases during the further sintering step.

(i) a step of disposing a powder that includes an absorber absorbing light of a wavelength included in a laser beam to be irradiated and silicon dioxide as a main component; (ii) a step of sintering or melting and solidifying the powder by irradiating the powder with a laser beam; and (iii) a step of heat-treating a shaped object formed by repeating the steps (i) and (ii) at 1470° C. or more and less than 1730° C.

A method for manufacturing a ceramic article including (i) a step of irradiating a powder mainly containing a ceramic material with an energy beam to sinter or melt and solidify the powder into a solidified portion, wherein the step is repeated a predetermined number of times to sequentially bond the resulting solidified portions together to obtain a ceramic modeling object, (ii) a step of allowing the shaped ceramic object to absorb a metal component-containing liquid that contains inorganic particles containing a metal element; and (iii) a step of heating the shaped ceramic object that has absorbed the metal component-containing liquid.

A method for producing a ceramic complex includes: preparing a raw material mixture that contains 5% by mass or more and 40% by mass or less of first rare earth aluminate fluorescent material particles containing an activating element and a first rare earth element different from the activating element, 0.1% by mass or more and 32% by mass or less of oxide particles containing a second rare earth element, and the balance of aluminum oxide particles, relative to 100% by mass of the total amount of the first rare earth aluminate fluorescent material particles, the oxide particles, and the aluminum oxide particles; preparing a molded body of the raw material mixture; and obtaining a sintered body by calcining the molded body in a temperature range of 1,550° C. or higher and 1,800° C. or lower.

A ceramic tube contains yttrium oxide as a main component, in which the section height difference (Rδc) of the roughness profile of an inner peripheral surface, which represents a difference between a section level at a load length ratio of 25% in the roughness profile and a section level at load length ratio of 75% in the roughness profile, is 2 μm or less and a coefficient of variation of the section height difference (Rδc) is 0.05 to 0.6.

A cordierite-based sintered body according to the present invention contains cordierite as a main component and silicon nitride or silicon carbide. The cordierite-based sintered body preferably has a thermal expansion coefficient less than 2.4 ppm/° C. at 40° C. to 400° C., an open porosity of 0.5% or less, and an average grain size of 1 μm or less.

A method of forming a ceramic matrix composite (CMC) component having an engineered surface includes applying a surface slurry comprising first particulate solids in a liquid carrier to an outer surface of a ceramic fiber preform. The surface slurry is dried to remove the liquid carrier, and thus a surface slurry layer comprising the first particulate solids is formed on the outer surface. The surface slurry layer is polished to a predetermined thickness and/or surface finish. After polishing, a ceramic tape comprising second particulate solids is applied to the surface slurry layer, and pressure is applied to attach the ceramic tape to the surface slurry layer and to induce consolidation of the ceramic tape and the surface slurry layer. Thus, a multilayer surface region comprising the surface slurry layer and a ceramic tape layer is formed on the ceramic fiber preform. The ceramic fiber preform and the multilayer surface region are infiltrated with a molten material, and, upon cooling, a CMC component having an engineered surface is formed.

A power module substrate includes an insulating substrate and a metal plate. The metal plate is joined to the insulating substrate with a brazing material in between. As to surface roughness of a lateral surface of the metal plate in a thickness direction, the surface roughness of at least a corner part farthest from a center of the metal plate in plan view is larger than the surface roughness of plane parts sandwiching the corner part.

A sintered yttrium oxide body having a total impurity level of 40 ppm or less, a density of not less than 4.93 g/cm3, wherein the sintered yttrium oxide body has at least one surface comprising at least one pore, wherein no pore is larger than 5 μm in diameter. A process for making the sintered yttrium oxide body is also disclosed.