Provided is a photosensitizer that can make a compound having a polymerizable group be efficiently cured by irradiation with an active energy ray. A photosensitizer comprising graphene, the graphene having a number average molecular weight (Mn) in terms of polystyrene of 500 or more and 1,000,000 or less, the number average molecular weight measured by gel permeation chromatography.

A polysulfide coating composition includes an aliphatic, aromatic or cycloaliphatic material with at least 2 thiol groups; an aliphatic, aromatic or cycloaliphatic, acryl, polyester or polysiloxane-based material with at least two epoxy groups; and a catalyst. The coating provides a durable cavitation- and erosion-resistant coating for the rudders of ships, and is also suitable for sound-damping applications.

A curable composition that can be cured at low temperature in a short time regardless of the type of epoxy compound that is mixed therewith, and has a long pot life; an adhesive comprising said curable composition; a method for producing a fiber-reinforced composite material that uses the curable composition; and a fiber-reinforced composite material containing a matrix comprising the curable composition. A curing agent mixture composition that can be cured at low temperature and in a short time, and provides the curable composition with a long pot life. An epoxy compound (A) and an imidazole compound (B) are blended in with the curable composition. In addition, the imidazole compound (B) and at least one type of crosslinking agent (C) are blended in with the curing agent mixture composition.

The present invention provides an epoxy resin-based curable composition which may be used as a structural adhesive for an automobile. Particularly, the present invention provides an epoxy resin-based curable composition having excellent low-temperature curability, while maintaining good storage stability and good adhesion. The present invention relates to a curable composition comprising an epoxy resin, a urea-based curing accelerator (A) and an amine-based curing agent (B) having a pyrazine ring.

An object of the present invention is to provide: a heat-curable composition capable of yielding a cured article in which crack generation during a heating-cooling cycle can be inhibited; a dry film thereof; and a printed wiring board comprising the cured article. The heat-curable composition is characterized by comprising a semisolid or a solid epoxy compound and a curing accelerator that is made miscible with the epoxy compound when heated at 130 to 220° C. The dry film comprises a resin layer formed from this heat-curable composition, and the printed wiring board comprises a cured article obtained from the heat-curable composition or the dry film.

A method i for forming an epoxidized polymer is provided. The method may include mixing an epoxidized plant oil with a synthetic epoxy resin and crosslinking the epoxidized plant oil and the synthetic epoxy resin using a curing agent. The epoxidized plant oil may be formed via: converting plant oil triglycerides to fatty amide alcohols via aminolysis using primary or secondary amines, converting the fatty amide alcohols to epoxidized fatty amide alcohols, and reacting the epoxidized fatty amide alcohols with vinyl monomers to obtain epoxidized plant oil monomers.

Elastomers are formed by curing a reaction mixture that includes an polyepoxide-terminated polyether having a linear or branched polyether chain that has a molecular weight of at least 2000, at least two epoxide groups that has an epoxide equivalent weight of at least 400 2) a curing agent containing at least one polythiol compound having at least two thiol groups and an equivalent weight per thiol group of up to 500, and 3) at least one base catalyst.

Provided is a one-pack type adhesive which contains (A) an epoxy resin, (B) a curing agent, (C) a curing accelerator, (D) an inorganic filler and (E) a polycarbodiimide compound, and wherein: the curing agent (B) contains at least one amine-based curing agent; the curing accelerator (C) contains at least one capsule type curing accelerator; the inorganic filler (D) contains at least one flake-like inorganic filler; and the content of the inorganic filler (D) is 10-200 parts by mass relative to 100 parts by mass of the epoxy resin (A).

A high-CTI and halogen-free epoxy resin composition for copper-clad plates and uses thereof is provided. The formula of the high-CTI and halogen-free epoxy resin composition for copper-clad plates comprises 100˜140 parts of halogen-free phosphorous epoxy resin, 10˜35 parts of dicyclopentadiene phenolic epoxy resin, 32˜60 parts of benzoxazine, 1˜5 parts of phenolic resin, 0.05˜0.5 parts of accelerants; and 25˜70 parts of fillers, by weight. The copper-clad plates, prepared according to embodiments of the present invention, can reach the requirements of high CTI (CTI≧500V), high heat resistance(Tg≧150 ° C., PCT, 2 h>6 min) and the level of flame retardance of UL-94 V0, and they are widely used in the electronic materials of electric machines, electric appliances, white goods and so on.

Provided are: an epoxy resin composition for fiber-reinforced composite materials, which has a good balance between storage stability and fast curing properties at high levels; a prepreg; and an epoxy resin composition which exhibits excellent mechanical characteristics as a fiber-reinforced composite material. A resin composition which contains an epoxy resin, dicyandiamide, an imidazole compound and an acidic compound, while satisfying the following conditions (a)-(c): (d) The time until the heat flow rate reaches the peak top after the epoxy resin composition reaches 100° C. is 25 minutes or less as measured by a differential scanning calorimeter at an isothermal temperature of 100° C. in a nitrogen gas stream. (e) The time until the heat flow rate reaches the peak top after the epoxy resin composition reaches 60° C. is 15 hours or more as measured by a differential scanning calorimeter at an isothermal temperature of 60° C. in a nitrogen gas stream. (f) The ratio of the number of epoxy groups to the number of imidazole rings in the epoxy resin composition is from 25 to 90 (inclusive).