A fluororesin composition is provided. The fluororesin composition comprises the following constituents: (A) a first fluororesin, which is polytetrafluoroethylene (PTFE) resin; (B) a first filler, which is a flat glass fiber; and (C) particles of a second fluororesin, which are coated with polysiloxane,
wherein, the particle size of the polysiloxane-coated particles of second fluororesin ranges from 0.2 μm to 80 μm, and the melting point of the second fluororesin is lower than the melting point of the first fluororesin.

A fluororesin composition is provided. The fluororesin composition comprises the following constituents: (A) a first fluororesin, which is polytetrafluoroethylene (PTFE) resin; (B) a first filler, which is a flat glass fiber; and (C) particles of a second fluororesin, which are coated with polysiloxane,
wherein, the particle size of the polysiloxane-coated particles of second fluororesin ranges from 0.2 μm to 80 μm, and the melting point of the second fluororesin is lower than the melting point of the first fluororesin.

A polymer optical fibre (POF) (30) for transmitting light of wavelength, λi, between two separate elements of an active implantable medical device (AIMD), includes a core (31) which is cylindrical and made of a cyclic olefin polymer (COP) or copolymer (COC), having a core refractive index at the wavelength, λi, n_core, A cladding (32) which has a cladding refractive index at the wavelength, λi, n_clad<n_core, and which is made of a cladding copolymer including monomers of tetrafluoroethylene, hexafluoropropylene and vinylidene fluoride. The cladding being itself enclosed in a coating (33) which is made of a coating polymer formed of one of the monomers of the cladding copolymer. The POF has a numerical aperture, NA, at the wavelength, λi, of at least 0.5.

A polymer optical fibre (POF) (30) for transmitting light of wavelength, λi, between two separate elements of an active implantable medical device (AIMD), includes a core (31) which is cylindrical and made of a cyclic olefin polymer (COP) or copolymer (COC), having a core refractive index at the wavelength, λi, n_core, A cladding (32) which has a cladding refractive index at the wavelength, λi, n_clad<n_core, and which is made of a cladding copolymer including monomers of tetrafluoroethylene, hexafluoropropylene and vinylidene fluoride. The cladding being itself enclosed in a coating (33) which is made of a coating polymer formed of one of the monomers of the cladding copolymer. The POF has a numerical aperture, NA, at the wavelength, λi, of at least 0.5.

A polymer optical fibre (POF) (30) for transmitting light of wavelength, λi, between two separate elements of an active implantable medical device (AIMD), includes a core (31) which is cylindrical and made of a cyclic olefin polymer (COP) or copolymer (COC), having a core refractive index at the wavelength, λi, n_core, A cladding (32) which has a cladding refractive index at the wavelength, λi, n_clad<n_core, and which is made of a cladding copolymer including monomers of tetrafluoroethylene, hexafluoropropylene and vinylidene fluoride. The cladding being itself enclosed in a coating (33) which is made of a coating polymer formed of one of the monomers of the cladding copolymer. The POF has a numerical aperture, NA, at the wavelength, λi, of at least 0.5.

In a first aspect, the present invention relates to a process improvement additive suitable for polymer processing, wherein this process improvement additive comprises a carrier polymer, a binding component and one or more fluoropolymers and wherein this process improvement additive further comprises one or more zeolites. In a second aspect, the present invention relates to a method for processing a polymer, wherein a process improvement additive is added to the polymer prior to processing and wherein this process improvement additive comprises a carrier polymer, a binding component, one or more fluoropolymers and one or more zeolites.

In a first aspect, the present invention relates to a process improvement additive suitable for polymer processing, wherein this process improvement additive comprises a carrier polymer, a binding component and one or more fluoropolymers and wherein this process improvement additive further comprises one or more zeolites. In a second aspect, the present invention relates to a method for processing a polymer, wherein a process improvement additive is added to the polymer prior to processing and wherein this process improvement additive comprises a carrier polymer, a binding component, one or more fluoropolymers and one or more zeolites.

In a first aspect, a transparent fluoropolymer film includes, a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer, and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5. In a second aspect, a transparent multilayer film includes a polymeric substrate film and a fluoropolymer film. The fluoropolymer film includes a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5.

In a first aspect, a transparent fluoropolymer film includes, a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer, and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5. In a second aspect, a transparent multilayer film includes a polymeric substrate film and a fluoropolymer film. The fluoropolymer film includes a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5.

In a first aspect, a transparent fluoropolymer film includes, a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer, and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5. In a second aspect, a transparent multilayer film includes a polymeric substrate film and a fluoropolymer film. The fluoropolymer film includes a vinyl fluoride polymer, 2 to 8 wt % of an acrylate polymer and 0.1 to 4 wt % of a triazine UV absorber. After heating at 100° C. for 96 hours, the transparent fluoropolymer film has a 340 nm absorbance of at least 1.5.