This invention relates to drag reducing agents used in case of transportation of crude oil products, in particular, to solid dry poly(meth)acrylate with dry poly alpha-olefins powders based agents. The technical result of the solution involves the preparation of an effective, fast-dissolving, stable solid dry drag reducing agent suitable for use in heavy crude oil. The drag reducing agents compositions have better drag reducing performance in heavy crude applications as compared with traditional drag reducing slurries is also disclosed, which consists of the following components, wt%: a mixture of at least two drag reducing polymers, from 65 to 90 a separating agent from 3 to 25 anti-agglomerating agent from 3 to 25 a surfactant from 3 to 25,where the first polymer is poly(meth)acrylate, the second polymer is poly alpha-olefin, the ratio of the polyacrylate weight and polyalphaolefin weight varies in the range from 2:1 to 5:1.

A composition including a solution at least one acrylic adhesive and particles of a cross-linked polymer having a carboxylate-group density between 2.0 and 12.0 meq/g and an average pore size between 0.005 and 1.0 μm, usable in particular for creating an adhesive matrix suitable for any device, for example for medical aims such as a patch, a film, a strip or a dressing, preferably a dressing, or suitable for any device of the functional textile type such as a sports item.

A composition including a solution at least one acrylic adhesive and particles of a cross-linked polymer having a carboxylate-group density between 2.0 and 12.0 meq/g and an average pore size between 0.005 and 1.0 μm, usable in particular for creating an adhesive matrix suitable for any device, for example for medical aims such as a patch, a film, a strip or a dressing, preferably a dressing, or suitable for any device of the functional textile type such as a sports item.

A coating material for the production of a UV-curing primer coating. The coating material includes 60 to 80 wt.-% of at least one difunctional, alcoxylated acrylate monomer, 5 to 15 wt.-% of at least one acrylate oligomer, 5 to 15 wt.-% of at least one carbonyl-functional acrylate and/or at least one methacrylate oligomer or 5 to 15 wt.-% of at least one polyethylene glycol acrylate and/or at least one polyethylene glycol methacrylate, and 1 to 10 wt.-% of at least one photoinitiator, each based on a total weight of the coating material.

A coating material for the production of a UV-curing primer coating. The coating material includes 60 to 80 wt.-% of at least one difunctional, alcoxylated acrylate monomer, 5 to 15 wt.-% of at least one acrylate oligomer, 5 to 15 wt.-% of at least one carbonyl-functional acrylate and/or at least one methacrylate oligomer or 5 to 15 wt.-% of at least one polyethylene glycol acrylate and/or at least one polyethylene glycol methacrylate, and 1 to 10 wt.-% of at least one photoinitiator, each based on a total weight of the coating material.

The invention relates to a waterproofing composition with high resistance to different weather conditions and improved insulating and anti-impact properties and which is easy to apply and more durable, and to materials based on same. The composition comprises acrylic resins, water, polymeric particulates and additives.

The invention relates to a waterproofing composition with high resistance to different weather conditions and improved insulating and anti-impact properties and which is easy to apply and more durable, and to materials based on same. The composition comprises acrylic resins, water, polymeric particulates and additives.

Disclosed is a low-temperature curable composition comprising: (A) at least one curable component selected from an epoxy resin and a blocked isocyanate, and (B) an amine-based latent curing agent, wherein a temperature peak of a reaction of the amine-based latent curing agent (B) with a bisphenol A type epoxy resin is between 70° C. and 110° C.

Disclosed is a low-temperature curable composition comprising: (A) at least one curable component selected from an epoxy resin and a blocked isocyanate, and (B) an amine-based latent curing agent, wherein a temperature peak of a reaction of the amine-based latent curing agent (B) with a bisphenol A type epoxy resin is between 70° C. and 110° C.

A coating for a medical device is described. The coating comprises: a surface layer; and optionally a base layer; wherein the surface layer comprises a polymer chain attached to an anti-clotting group, wherein the anti-clotting group is selected from a sulfonic acid group, a sulfonamide group, a sulfamic acid group, a hydrogen sulfate group and a conjugate base thereof. Also described is a medical device comprising the coating, and uses and methods involving the coating and the medical device.