A chromium-free insulation coating composition includes 100 parts by weight of a phosphate solution, 1-5 parts by weight of molybdate, 50-150 parts by weight of silica sol, 3-13 parts by weight of selenium dioxide, 1-10 parts by weight of metal oxide and/or metal hydroxide, 5-15 parts by weight of organic acid, 1-6 parts by weight of boric acid, and 100-300 parts by weight of water.

A coated strip or sheet including: a steel strip or sheet, a zinc or zinc alloy coating on the steel strip or sheet, a coating system for inhibiting corrosion, and a top coat, wherein the coating system includes a corrosion inhibitive composition that includes graphene and graphene stacks including 2-20 layers of graphene and a coupling agent including an organofunctional siloxane coupled to graphene and the graphene stacks.

Provided is a chemical conversion agent that, with respect to an aluminum metal material, etc., contributes to superior corrosion and moisture resistance, contributes to superior adhesion with a laminate film, and contributes to superior hydrofluoric acid and alkali resistance. The chemical conversion agent includes: one or more type of metal element (A) selected from a group comprising of zirconium, titanium, and hafnium; vanadium element (B); and a resin (C). The resin (C) includes a polyvinyl alcohol resin (C1). The ratio (Wa/Wb) of the weight-based total content (Wa) of the metal element (A) relative to the weight-based content (Wb) of vanadium element (B) is 0.1-15, and the ratio ((Wa+Wb)/Wc1) of the weight-based total content (Wa+Wb) of the metal element (A) and the vanadium element (B) relative to the weight-based total content (Wc1) of the polyvinyl alcohol resin (C1) is 0.25-15.

A method of making cerium citrate includes combining cerium carbonate and citric acid to produce cerium citrate and carbon dioxide. The cerium citrate is substantially free of negative ions other than citrate. The cerium citrate can be used in a corrosion inhibitor composition.

The present disclosure relates to a composition comprising an expanded and micronized volcanic glass (EMVG) and at least one chemical agent, wherein the at least one chemical agent is coated on the surface of the volcanic glass. The present disclosure also relates to an improved process to remove mineral impurities and to coat the surface of the EMVG. The disclosed composition can be used a functional reinforcing filler to improve the mechanical properties of plastic.

The present invention relates to a composition comprising (A) at least one carboxy-functional polyester having an acid number in the range from 20 to 250 mg KOH/g, prepared using at least one difunctional monomer (a1) with aliphatic groups having 12 to 70 carbon atoms between the functional groups, and also (B) at least one synthetic layered hydroxide, where the at least one layered hydroxide (B) is prepared in the presence of the polyester (A). The present invention further relates to the preparation of the composition and also to the use of the composition as coating material.

The disclosed technology relates to corrosion or rust preventive coating compositions and methods of their use. The compositions comprise a rust preventative composition, optionally including a diluent, and a quaternary ammonium salt.

A corrosion resistant article including an aluminum substrate and a corrosion-inhibiting cerium based corrosion inhibitor corrosion inhibiting additive on the aluminum substrate, the corrosion inhibiting additive comprising an anodic corrosion inhibitor and a cathodic corrosion inhibitor, the anodic corrosion inhibitor greater than 25 wt % of the total inhibitor.

One or more techniques are disclosed for a method for functionalized a graphitic material comprising the steps of: 1) providing a graphitic material; 2) providing a first molecule comprising a first group, a spacer, and a second group; 3) providing a second molecule comprising a third group, a spacer, and a fourth group, wherein the third group is a different group from the first group; and 4) bonding the first molecule and the second molecule to the graphitic material. Also disclosed is a tunable material composition comprising the functionalized carbon nanotubes or functionalized graphene prepared by the methods described herein.

A process of making a dense, cohesive and uniform aluminum oxide coating on a metallic substrate includes electrodepositing polynuclear aluminum oxide hydroxide clusters from a polynuclear aluminum oxide hydroxide cluster solution on a metallic substrate to form a precursor coating, and post-treating the precursor coating to form a final aluminum oxide coating on the metallic substrate.