A method for forming a polyethylene and alumina nanocomposite coating on a substrate is described. The method may use microparticles of UHMWPE with nanoparticles of alumina to form a powder mixture, which is then applied to a heated steel substrate to form the nanocomposite coating. The nanocomposite coating may have a Vickers hardness of 10.5-12.5 HV.

A method for forming a polyethylene and alumina nanocomposite coating on a substrate is described. The method may use microparticles of UHMWPE with nanoparticles of alumina to form a powder mixture, which is then applied to a heated steel substrate to form the nanocomposite coating. The nanocomposite coating may have a Vickers hardness of 10.5-12.5 HV.

A floor coating, which is prepared from 55-70% by weight of an epoxy-modified polyurethane resin, 5-10% by weight of Al.sub.2O.sub.3, 10-25% by weight of SiC, 0.4-1% by weight of a leveling agent, 0.3-1% by weight of a dispersant, 5-10% by weight of a solvent and 0.2-0.8% by weight of a curing agent. A degree of polymerization of the epoxy-modified polyurethane resin is 80-100. A scratch-resistant floor and a preparation method thereof are also disclosed herein.

Disclosed are stable penetration primer or wood stain formulations. The formulation may comprise a) an aqueous polymer dispersion comprising a polymer produced by free-radically initiated emulsion polymerization of at least one ethylenically unsaturated strong acid monomer with a pKa less than 4 (in water at 20° C.) and at least one ethylenically unsaturated weak acid monomer with a pKa of 4 or greater (in water at 20° C.); and b) at least one water-soluble alkali metal silicate, at least one water-soluble alkali metal or alkaline earth metal alkyl siliconate, or a mixture thereof.

A reflective paint's liquid mixture includes 42.4-71.3 weight percent of a liquid solvent, 14.4-28.3 weight percent of a binder fully dissolved in the liquid solvent, and 13.8-29.3 weight percent of light scattering particles that are insoluble in the liquid solvent and are of a size ranging from 100 nanometers to 200 nanometers. The binder is selected from potassium bromide, sodium chloride, potassium chloride, sodium bromide, cesium chloride, and rubidium chloride. The light scattering particles are selected from hafnium oxide and yttrium oxide. The reflective paint is particularly useful as a surface coating for a variety of structures that must support cryogenic temperatures. It can be used in any application to act as a broadband reflector of the Sun's radiation in the wavelength band from approximately 0.21 microns to 9 microns and beyond.

A reflective paint's liquid mixture includes 42.4-71.3 weight percent of a liquid solvent, 14.4-28.3 weight percent of a binder fully dissolved in the liquid solvent, and 13.8-29.3 weight percent of light scattering particles that are insoluble in the liquid solvent and are of a size ranging from 100 nanometers to 200 nanometers. The binder is selected from potassium bromide, sodium chloride, potassium chloride, sodium bromide, cesium chloride, and rubidium chloride. The light scattering particles are selected from hafnium oxide and yttrium oxide. The reflective paint is particularly useful as a surface coating for a variety of structures that must support cryogenic temperatures. It can be used in any application to act as a broadband reflector of the Sun's radiation in the wavelength band from approximately 0.21 microns to 9 microns and beyond.

The disclosure provides a ceiling tile including a curable coating composition including 10-50 vol. % inorganic binder, based on the total volume of solids in the dry coating composition, wherein the inorganic binder is an alkali metal silicate or an alkaline earth metal silicate and 50-90 vol. % inorganic filler, based on the total volume of solids in the coating composition, wherein the binder and the filler are not the same and the coating is substantially free of an organic polymeric binder. The ceiling tiles have a backing side and an opposing facing side, and a cured coating layer disposed on the backing side of the panel, the backing side being directed to a plenum above the fibrous panel in a suspended ceiling tile, the cured coating layer including the curable coating composition of the disclosure.

The disclosure provides a ceiling tile including a curable coating composition including 10-50 vol. % inorganic binder, based on the total volume of solids in the dry coating composition, wherein the inorganic binder is an alkali metal silicate or an alkaline earth metal silicate and 50-90 vol. % inorganic filler, based on the total volume of solids in the coating composition, wherein the binder and the filler are not the same and the coating is substantially free of an organic polymeric binder. The ceiling tiles have a backing side and an opposing facing side, and a cured coating layer disposed on the backing side of the panel, the backing side being directed to a plenum above the fibrous panel in a suspended ceiling tile, the cured coating layer including the curable coating composition of the disclosure.

A photoluminescent coating material which contains: a hydrocarbon-based solvent (A) that has an aniline point of 40° C. or higher; a resin (B1) that is incompatible with the hydrocarbon-based solvent (A); a solvent (C) that is compatible with the hydrocarbon-based solvent (A) and the resin (B1) while having a lower boiling point than the hydrocarbon-based solvent (A); and a scale-like aluminum (D).

The present embodiments relate to an antifouling article comprising polyurethane and medetomidine, or an enantiomer or salt thereof, from 0.1% by weight of the antifouling article and present in a polymer matrix of the polyurethane.