The present invention relates to an activated lignin composition, its manufacture and its use thereof. It also relates to a resin comprising lignin, its manufacture and use.

The present invention relates to a method for manufacturing a wet glued wood article, as well as a wet glued article obtainable by said method and also uses of a wet glued article, wherein the method comprises the following steps: a) providing two actively never-dried or slightly dried wood pieces comprising at least one surface each which has a superficial layer having a thickness of least 2-3 wood cells; b) drying said surfaces of said wood pieces so that the moisture content of said superficial layer is below the fibre saturation point, providing a dried surface on each of the said wood pieces; c) applying a gluing agent on said dried surface of one of the wood pieces, thus providing a glue surface; d) bringing the dried surfaces together so that said glue surface touches the dried surface on the other wood piece, thus providing a wet glued wood article.

The present invention relates to a method for manufacturing a wet glued wood article, as well as a wet glued article obtainable by said method and also uses of a wet glued article, wherein the method comprises the following steps: a) providing two actively never-dried or slightly dried wood pieces comprising at least one surface each which has a superficial layer having a thickness of least 2-3 wood cells; b) drying said surfaces of said wood pieces so that the moisture content of said superficial layer is below the fibre saturation point, providing a dried surface on each of the said wood pieces; c) applying a gluing agent on said dried surface of one of the wood pieces, thus providing a glue surface; d) bringing the dried surfaces together so that said glue surface touches the dried surface on the other wood piece, thus providing a wet glued wood article.

The present disclosure describes surface formulations that form a layer on surfaces and comprise a phenol selected from: (I), (II), (III), (IV) or (V), with detailed descriptions of variables herein.

##STR00001##

The present disclosure describes surface formulations that form a layer on surfaces and comprise a phenol selected from: (I), (II), (III), (IV) or (V), with detailed descriptions of variables herein.

##STR00001##

The present invention relates to a method for increasing the reactivity of lignin, wherein the method comprises the following steps: a) forming, under heating at a temperature of 71-94 C., an aqueous dispersion comprising alkali and lignin, wherein the alkali comprises a hydroxide of an alkali metal; and b) heating the dispersion formed in step a) at a temperature of 50-95 C. for producing alkalated lignin.

The present invention relates to a method for increasing the reactivity of lignin, wherein the method comprises the following steps: a) forming, under heating at a temperature of 71-94 C., an aqueous dispersion comprising alkali and lignin, wherein the alkali comprises a hydroxide of an alkali metal; and b) heating the dispersion formed in step a) at a temperature of 50-95 C. for producing alkalated lignin.

The embodiments described herein generally relate to methods and chemical compositions of phenolic epoxy systems. In one embodiment, a composition comprising a phenolic epoxy resin system includes an epoxy resin component and an alkoxylated phenol-aldehyde novolac resin.

The embodiments described herein generally relate to methods and chemical compositions of phenolic epoxy systems. In one embodiment, a composition comprising a phenolic epoxy resin system includes an epoxy resin component and an alkoxylated phenol-aldehyde novolac resin.

Most processes currently being proposed and/or used for the production of lignin from kraft or soda black liquors are capable of producing two main types of lignin: high residual content (HRC) lignin and low residual content (LRC) lignin. Surprisingly, it was discovered that HRC lignin, is a suitable ingredient in alkaline adhesives, particularly wood adhesives of the phenolic type (e.g. resole resins). This biomaterial is environmentally green and remarkably low cost, which makes it an industrially viable material to be used as a novel and major ingredient in phenolic adhesives for the manufacture of exterior grade plywood, laminated veneer lumber, oriented strand board (OSB) and other wood productsthis was successfully demonstrated in a number of laboratory experiments as well as several different mill trials. The composition, preparation and application of such wood adhesives are hereby disclosed.