The present invention provides a resin composition comprising maleimide-containing pre-polymerized resin and article made therefrom. The resin composition comprises: 100 weight parts of vinyl-containing polyphenylene ether resin; 35 to 45 weight parts of bis(vinylphenyl)ethane; and 30 to 60 weight parts of maleimide-containing pre-polymerized resin; wherein the maleimide-containing pre-polymerized resin is obtained by pre-polymerization of aromatic maleimide resin and long chain maleimide resin. The articles made from the resin composition improve at least one characteristic of glass transition temperature variation, copper foil peeling strength, percentage of thermal expansion, coefficient of thermal expansion and surface appearance.

The present disclosure relates to an adhesive resin composition for bonding semiconductors, including: a thermoplastic resin; a thermosetting resin; a curing agent; and a compound having a specific structure, and an adhesive film for semiconductors including the same.

The present disclosure relates to an adhesive resin composition for bonding semiconductors, including: a thermoplastic resin; a thermosetting resin; a curing agent; and a compound having a specific structure, and an adhesive film for semiconductors including the same.

The present application provides a resin component, and a prepreg and a circuit material using the same. The resin component comprises unsaturated polyphenylene ether resin, polyolefin resin, terpene resin and an initiator. When the total weight of the unsaturated polyphenylene ether resin, polyolefin resin and terpene resin is defined as 100 parts by weight, the terpene resin is in an amount of 3-40 parts by weight. The polyolefin resin is one or a combination of at least two selected from the group consisting of unsaturated polybutadiene resin, SBS resin and styrene butadiene resin. The present application discloses that the resulting resin composition has good film-forming properties, adhesion and dielectric properties through the coordination of unsaturated polyphenylene ether resin, unsaturated polyphenylene ether resin, polyolefin resin and terpene resin, and the circuit boards using the same have higher interlayer peel strength and lower dielectric loss.

The present application provides a resin component, and a prepreg and a circuit material using the same. The resin component comprises unsaturated polyphenylene ether resin, polyolefin resin, terpene resin and an initiator. When the total weight of the unsaturated polyphenylene ether resin, polyolefin resin and terpene resin is defined as 100 parts by weight, the terpene resin is in an amount of 3-40 parts by weight. The polyolefin resin is one or a combination of at least two selected from the group consisting of unsaturated polybutadiene resin, SBS resin and styrene butadiene resin. The present application discloses that the resulting resin composition has good film-forming properties, adhesion and dielectric properties through the coordination of unsaturated polyphenylene ether resin, unsaturated polyphenylene ether resin, polyolefin resin and terpene resin, and the circuit boards using the same have higher interlayer peel strength and lower dielectric loss.

The present application provides a resin component, and a prepreg and a circuit material using the same. The resin component comprises unsaturated polyphenylene ether resin, polyolefin resin, terpene resin and an initiator. When the total weight of the unsaturated polyphenylene ether resin, polyolefin resin and terpene resin is defined as 100 parts by weight, the terpene resin is in an amount of 3-40 parts by weight. The polyolefin resin is one or a combination of at least two selected from the group consisting of unsaturated polybutadiene resin, SBS resin and styrene butadiene resin. The present application discloses that the resulting resin composition has good film-forming properties, adhesion and dielectric properties through the coordination of unsaturated polyphenylene ether resin, unsaturated polyphenylene ether resin, polyolefin resin and terpene resin, and the circuit boards using the same have higher interlayer peel strength and lower dielectric loss.

The present application provides a circuit material and a circuit board containing the same. The circuit material comprises a conductive metal layer and a dielectric substrate layer, and an adhesive layer arranged therebetween, wherein the adhesive layer is made of a material which comprises an adhesive composition comprising a resin component and a non-resin component, wherein the resin component is composed of unsaturated polyphenylene ether resin, SBS resin and maleimide resin; and the non-resin component comprises an initiator; and the adhesive layer is obtained by applying the adhesive composition dissolved in a solvent onto the surface of the conductive metal layer or the dielectric substrate layer in the form of a solution, or by applying to a release material and removing the release material after partially curing or completely curing.

The present application provides a circuit material and a circuit board containing the same. The circuit material comprises a conductive metal layer and a dielectric substrate layer, and an adhesive layer arranged therebetween, wherein the adhesive layer is made of a material which comprises an adhesive composition comprising a resin component and a non-resin component, wherein the resin component is composed of unsaturated polyphenylene ether resin, SBS resin and maleimide resin; and the non-resin component comprises an initiator; and the adhesive layer is obtained by applying the adhesive composition dissolved in a solvent onto the surface of the conductive metal layer or the dielectric substrate layer in the form of a solution, or by applying to a release material and removing the release material after partially curing or completely curing.

The present application provides a circuit material and a circuit board containing the same. The circuit material comprises a conductive metal layer and a dielectric substrate layer, and an adhesive layer arranged therebetween, wherein the adhesive layer is made of a material which comprises an adhesive composition comprising a resin component and a non-resin component, wherein the resin component is composed of unsaturated polyphenylene ether resin, SBS resin and maleimide resin; and the non-resin component comprises an initiator; and the adhesive layer is obtained by applying the adhesive composition dissolved in a solvent onto the surface of the conductive metal layer or the dielectric substrate layer in the form of a solution, or by applying to a release material and removing the release material after partially curing or completely curing.

A filler-containing film that holds fillers and a fine solid in an insulating resin layer and a predetermined arrangement of the fillers is repeated as viewed in a plan view has a proportion of 300% or less where the proportion is a repeat pitch of the fillers after thermocompression bonding to that before thermocompression bonding during thermocompression bonding under a predetermined thermocompression bonding condition with the filler-containing film held between smooth surfaces. A method of producing the filler-containing film includes the steps of: forming an insulating resin layer on a release substrate; pushing fillers from a surface on a side opposite to the release substrate of the insulating resin layer; and layering the insulating resin layer containing the fillers pushed and another insulating resin layer. This filler-containing film suppresses disorder of arrangement of fillers during thermocompression bonding of the film to an article.