A high-strength cold-rolled steel sheet comprises: a chemical composition that contains C, Si, Mn, P, S, N, Al, Ti, Nb, and B with a balance consisting of Fe and inevitable impurities, and satisfies [mol % N]/[mol % Ti]<1; and a steel microstructure in which: an area fraction of ferrite is 30% or more and 60% or less; a total area fraction of tempered martensite and bainite is 35% or more and 65% or less; an area fraction of quenched martensite is 15% or less; an area fraction of retained austenite is 1% or more and 10% or less; an area fraction of low-Mn ferrite having a Mn concentration of 0.8×[% Mn] or less is 5% or more and 40% or less; a result of subtracting the area fraction of the low-Mn ferrite from the area fraction of the ferrite is 10% or more; an area fraction of a residual microstructure is less than 3%; and an average grain size of the low-Mn ferrite is 10 μm or less.

Disclosed in the present invention is a manufacturing method for a carbon steel and austenitic stainless-steel rolling clad plate, comprising the steps of: (1) obtaining a blank material of a carbon steel layer and a blank material of a stainless-steel layer; (2) assembling blank materials; (3) cladding and rolling; (4) cold rolling; (5) first annealing; and (6) second annealing. The carbon steel and austenitic stainless-steel rolling clad plate has two unique annealing processes, so that the clad plate has the performance advantages of the austenitic stainless-steel and the carbon steel. In addition, further disclosed in the present invention is a carbon steel and austenitic stainless-steel rolling clad plate manufactured by this method.

The present disclosure relates to a zinc plated steel sheet having excellent fatigue strength of electrical resistance spot welds and a method for manufacturing the same. According to an aspect of the present disclosure, a zinc plated steel sheet includes a base steel sheet and a zinc-based plating layer formed on a surface of the base steel sheet, wherein a concentration profile of one or two of oxygen, and silicon and manganese measured in a depth direction from the surface of the base steel sheet has a maximum point in the depth direction from the surface, and an absolute value of a difference between a depth at which the maximum point of the concentration profile of oxygen is formed and a depth at which the maximum point of the concentration profile of one of silicon and manganese is formed is 0.5 μm or less.

The present invention provides a tin blackplate for processing and a method for manufacturing the same.

The tin blackplate according to an exemplary embodiment of the present invention comprises: in % by weight, 0.0005 to 0.005% of carbon (C), 0.15 to 0.60% of manganese (Mn), 0.01 to 0.06% of aluminum (AI), 0.0005 to 0.004% of nitrogen (N), 0.0005 to 0.003% of boron (B), 0.01 to 0.035% of titanium (Ti), and the balance being iron (Fe) and inevitable impurities, and satisfies the following Formula 1.

4.8≤([Ti]+[Al])/[N]−[B]≤12.5  [Equation 1]

In this case, in Equation 1, [Ti], [Al], [N], and [B] mean each value obtained by dividing the content (% by weight) of Ti, Al, N, and B in the blackplate by each atomic weight thereof.

An embodiment of the present invention provides steel for hot forming, a hot-formed member, and methods for manufacturing same, the steel comprising, by wt %, 0.06-0.1% of C, 0.05-0.6% of Si, 0.6-2% of Mn, 0.05% or less of P, 0.02% or less of S, 0.01-0.1% of Al, 0.01-0.8% of Cr, 0.01-0.5% of Mo, 0.02% or less of N, and the remainder of Fe and inevitable impurities, wherein an alloy factor represented by relational expression 1 below is 7 or more, and the number of carbides having a circular equivalent diameter of 0.5 μm or greater is 10.sup.5/mm.sup.2 or less.

Alloy factor=I(Mn)×I(Si)×I(Cr)×I(Mo)  [Relational expression 1] where the I values for the components are I(Mn)=3.34×Mn+1, I(Si)=0.7×Si+1, I(Cr)=2.16×Cr+1, and I(Mo)=3×Mo+1, respectively, and the content of each component is expressed as wt %.

This steel sheet has a specific chemical composition, the tensile strength is 1300 MPa or more, the ratio (R/t) of the limit bend radius to the sheet thickness is less than 3.5, when a depth position of 30 μm from the surface in the sheet thickness direction is defined as a position A and a depth position of ¼ of the sheet thickness from the surface in the sheet thickness direction is defined as a position B, the number density of AIN at the position A is 3000 pieces/mm.sup.2 or more and 6000 pieces/mm.sup.2 or less, a metallographic structure at the position B includes 90% or more of martensite by volume percentage, and the hardness at the position A is 1.20 times or higher than the hardness at the position B.

The present invention relates to high-strength medium manganese steel for warm stamping, which contains 3-10 wt % of manganese (Mn), 0.05-0.3 wt % of carbon (C), and 0.1-1.0 wt % of silicon (Si) as components thereof, with the balance being iron (Fe) and unavoidably contained impurities. The present invention performs heat treatment at the low austenitizing temperature of medium manganese steel, and thus has the effect of reducing the high thermal energy consumption of the prior art hot stamping process. Furthermore, the present invention does not require an additional temperature process, and can obtain high strength by only slow cooling such as air cooling outside a mold without performing cooling at high rate inside the mold, and thus has the effects of simplifying a process and improving manufacturing efficiency.

The entirety or a part of this hot stamped product includes, as a chemical composition, by mass %, C: 0.001% or more and less than 0.080%, Si: 2.50% or less, Mn: 0.01% or more and less than 0.50%, P: 0.200% or less, S: 0.0200% or less, sol.Al: 0.001% to 2.500%, N: 0.0200% or less, Cr: 0.30% or more and less than 2.00%, and a remainder: Fe and impurities, in which a metallographic structure contains, by vol %, ferrite: more than 60.0%, martensite: 0% or more and less than 10.0%, and bainite: 0% or more and less than 20.0%, a tensile strength is less than 700 MPa, and ΔTS, which is a decrease in the tensile strength after a heat treatment at 170° C. for 20 minutes, is 100 MPa or less.

Provided is a plated steel material which can be used for an automobile, a household appliance, a building material, and the like and, more particularly, to a zinc alloy plated steel material having excellent corrosion resistance after being processed and a method for manufacturing the same.

Disclosed are high-strength ferritic stainless steel STS430, which has a yield strength of 350 MPa or greater and can be applied to a clamp of a vehicle or a common hose, and a manufacturing method thereof. The high-strength ferritic stainless steel for a clamp, according to one embodiment of the present invention, comprises, by weight, 0.04-0.1% of C, 0.2-0.6% of Si, 0.01-1.5% of Mn, 14.0-18.0% of Cr, 0.005-0.2% of Al, 0.005-0.2% of V, 0.02-0.1% of N, and the remainder as Fe and inevitable impurities, satisfies Expressions (1) and (2), and has at least 2.5×10.sup.6 precipitates having a mean diameter of 0.5 μm or less per mm.sup.2. (1) 0.35%≤Si+Al+V≤0.6% (2) 0.09%≤C+N≤0.12%