Provided is an oriented electrical steel sheet including a groove existing on the surface of the electrical steel sheet and a forsterite layer formed on a part or all of the surface of the electrical steel sheet, in which forsterite which is extended from the forsterite layer and penetrates to a base steel sheet in an anchor form is present on the surface of the side of the groove.

A method of production non grain-oriented Fe—Si steel sheet is provided. The method includes the steps of melting a steel composition that contains in weight percentage: C≤0.006, 2.0≤Si≤5.0, 0.1≤Al≤3.0, 0.1≤Mn≤3.0, N≤0.006, 0.04≤Sn≤0.2, S≤0.005, P≤0.2, Ti≤0.01, the balance being Fe and other inevitable impurities, casting said melt into a slab, reheating said slab, hot rolling said slab, coiling said hot rolled steel, optionally annealing the hot rolled steel, cold rolling, annealing and cooling the cold rolled steel down to room temperature.

An object of the present invention is to provide magnesium oxide for an annealing separator which is useful for obtaining grain-oriented electromagnetic steel sheets with excellent magnetic properties and insulating properties. To resolve the above object, an aspect of the present invention resides in magnesium oxide for an annealing separator which has a BET specific surface area of 12.0×10.sup.3 to 25.0×10.sup.3 m.sup.2.Math.kg.sup.−1 and a Blaine specific surface area of 2.0×10.sup.3 to 7.0×10.sup.3 m.sup.2.Math.kg.sup.−1.

A non-oriented electrical steel sheet according to one embodiment of the invention has a chemical composition represented by C: 0.0030% or less, Si: 2.00% or less, Al: 1.00% or less, Mn: 0.10% to 2.00%, S: 0.0030% or less, one or more selected from the group consisting of Mg, Ca, Sr, Ba, Nd, Pr, La, Ce, Zn, and Cd: 0.0003% or greater and less than 0.0015% in total, a parameter Q represented by Q=[Si]+2×[Al]−[Mn]: 2.00 or less; Sn: 0.00% to 0.40%, Cu: 0.00% to 1.00%, and a remainder: Fe and impurities, and a parameter R represented by R−(I.sub.100+I.sub.310+I.sub.411+I.sub.521)/(I.sub.111+I.sub.211+I.sub.332+I.sub.221) is 0.80 or greater.

A non-oriented electrical steel sheet according to an embodiment of the present invention includes, in wt%, Si: 2.2 to 4.5 %, Mn: 0.5 % or less (excluding 0 %), AI: 0.001 to 0.5 %, Sn: 0.07 to 0.25 %, and N: 0.0010 to 0.0090 %, and the balance of Fe and inevitable impurities.

A surface layer portion existing in an inner direction from a surface of the steel sheet and a central portion existing inside the surface layer portion are included, and the central portion includes N at 0.005 wt% or less, and the surface layer portion further includes N at 0.001 wt% or more compared to the central portion; and the surface layer portion has an average grain size of 60 .Math.m or less, while the central portion has an average grain size of 70 to 300 .Math.m.

A method for manufacturing a grain-oriented electrical steel sheet according to an embodiment of the present invention comprises the steps of: hot-rolling a slab to prepare a hot-rolled sheet, the slab containing, in wt %, 2.0 to 6.0% of Si, 0.04 to 0.12% of Mn, 0.001 to 0.022% of N, 0.027 to 0.060% of C, 0.01 to 0.08% of Nb, 0.01% or less of Ti, and the balance of Fe and other inevitable impurities; cold-rolling the hot-rolled sheet to prepare a cold-rolled sheet; and subjecting the primarily recrystallization-annealed cold-rolled sheet to secondary recrystallization annealing.

An exemplary embodiment in the present disclosure provides a grain-oriented electrical steel sheet containing, by wt %: 3.0 to 4.5% of Si; 0.05 to 0.2% of Mn; 0.015 to 0.035% of Al; 0.0015% or less (excluding 0%) of C; 0.0015% or less (excluding 0%) of N; 0.0015% or less (excluding 0%) of S; and a balance of Fe and other unavoidable impurities, wherein the grain-oriented electrical steel sheet satisfies the following Relational Expressions 1 and 2:

(W.sub.13/50/W.sub.17/50)≤0.57  [Relational Expression 1]

(W.sub.15/50/W.sub.17/50)≤0.76  [Relational Expression 2] where Wx/y represents a core loss value under conditions in which a magnitude of an applied magnetic field is x/10 T and a frequency is y Hz.

A method for producing an austempered steel is provided. The method includes subjecting a steel alloy having a silicon content of 1.5 to 4.4 weight percent and a carbon content of 0.3 to 0.8 weight percent to continuous cooling followed by annealing. The cooling rate is initially sufficiently fast to prevent predominant formation of proeutectoid ferrite or pearlite, while subsequently at intermediate temperatures, the cooling rate is sufficiently slow to allow a transformation of the austenite to mainly ausferrite during cooling. The annealing is able to complete the transformation of carbon enriched austenite to ausferrite and to temper any martensite previously formed. The method results in the cost-efficient production of one or more continuously cooled and annealed austempered steel components or semi-finished products having mainly an ausferritic microstructure.

Provided is a grain-oriented electrical steel sheet that has excellent magnetic properties and can be manufactured by secondary recrystallization orientation control using coil annealing with high productivity. A grain-oriented electrical steel sheet comprises a specific chemical composition, wherein an average value of a deviation angle (α.sup.2+β.sup.2).sup.1/2 calculated from a deviation angle α from ideal Goss orientation around an ND rotation axis and a deviation angle β from ideal Goss orientation around a TD rotation axis is 5.0° or less, and an area ratio R.sub.β of crystal grains with β≤0.50° is 20% or less.

A grain-oriented electrical steel sheet includes: a base steel sheet having a predetermined chemical composition; a glass coating provided on the surface of the base steel sheet; and a tension-applying insulation coating provided on the surface of the glass coating, in which linear thermal strains having, a predetermined angle (φ) with respect to a transverse direction which is a direction orthogonal to a rolling direction are periodically formed on the surface of the tension-applying insulation coating at predetermined intervals along the rolling direction, a full width at half maximum F1 on the linear thermal strain and a full width at half maximum F2 at an intermediate position between the two linear thermal strains adjacent to each other satisfy 0.00<(F1−F2)/F2≤0.15, the width of the linear thermal strain is 10 μm or more and 300 μm or less, and in the base steel sheet, an orientation distribution angle γ around a rolling direction axis of secondary recrystallization grains, an orientation distribution angle α around an axis parallel to a normal direction, and an orientation distribution angle β around an axis perpendicular to each of the RD axis and the ND axis in units of ° satisfy 1.0≤γ≤8.0 and 0.0≤(α.sup.2+β.sup.2).sup.0.5≤10.0.