A hot-rolled strip steel product is described having a chemical composition consisting of, in terms of weight percentages (wt. %): 0.030%-0.10% C, 0%-1.10% Si, 0.50%-2.0% Mn, <0.020% P, <0.010% S,<0.010% N, 0%-0.60% Cr, 0%-0.20% Ni, 0%-0.25% Cu, 0%-0.30% Mo, 0%-0.15% Al, 0%-0.10% Nb, 0.10%-0.30% V, <0.020% Ti, 0%-0.0010% B, remainder being Fe and inevitable impurities, wherein the hot rolled strip steel product has a a microstructure comprising, in terms of volume percentages (vol. %), ferrite≥90, wherein the ferrite structure comprises bainite, at least 50% of polygonal ferrite and at most 10% quasi-polygonal ferrite, and wherein the steel strip product has an average hole expansion ratio≥50%, a yield strength (Rp0.2%) longitudinal to rolling direction of ≥660 MPa and a tensile strength≥760 MPa.

A steel for mining chain and a manufacturing method thereof, wherein the steel has compositions by weight percentage: C: 0.20-0.28%, Si: 0.01-0.40%, Mn: 0.50-1.50%, P≤0.015%, S≤0.005%, Cr: 0.30-2.00%, Ni: 0.50-2.00%, Mo: 0.10-0.80%, Cu: 0.01-0.30%, Al: 0.01-0.05%, Nb: 0.001-0.10%, V: 0.001-0.10%, H≤0.00018%, N≤0.0150%, O≤0.0020%, and the balance is Fe and inevitable impurities. The manufacturing method comprises steps of smelting, refining and vacuum treatment, casting, heating, forging or rolling, and quenching and tempering heat treatment processes. The steel in the present invention has high strength and good impact toughness, good elongation and reduction of area. The steel can also resist stress corrosion cracking and have good weather resistance, wear resistance and fatigue resistance, which can be used in scenarios where the steel having high strength and toughness is required, such as construction machinery and marine engineering.

A steel for mining chain and a manufacturing method thereof, wherein the steel has compositions by weight percentage: C: 0.20-0.28%, Si: 0.01-0.40%, Mn: 0.50-1.50%, P≤0.015%, S≤0.005%, Cr: 0.30-2.00%, Ni: 0.50-2.00%, Mo: 0.10-0.80%, Cu: 0.01-0.30%, Al: 0.01-0.05%, Nb: 0.001-0.10%, V: 0.001-0.10%, H≤0.00018%, N≤0.0150%, O≤0.0020%, and the balance is Fe and inevitable impurities. The manufacturing method comprises steps of smelting, refining and vacuum treatment, casting, heating, forging or rolling, and quenching and tempering heat treatment processes. The steel in the present invention has high strength and good impact toughness, good elongation and reduction of area. The steel can also resist stress corrosion cracking and have good weather resistance, wear resistance and fatigue resistance, which can be used in scenarios where the steel having high strength and toughness is required, such as construction machinery and marine engineering.

The invention relates to a process for producing an at least partly quenched and tempered sheet steel component, where the process comprises the following steps: providing a sheet steel, at least partly austenitizing the sheet steel at a temperature of at least Ac1, at least partly hardening the at least partly austenitized sheet steel to give an at least partly hardened sheet steel component, where the at least partly austenitized sheet steel is cooled to a temperature below Ms, at least partly annealing the at least partly hardened sheet steel component at a temperature of less than Ac1 for producing an at least partly quenched and tempered sheet steel component. A further subject of the invention is an at least partly quenched and tempered sheet steel component.

The invention relates to a process for producing an at least partly quenched and tempered sheet steel component, where the process comprises the following steps: providing a sheet steel, at least partly austenitizing the sheet steel at a temperature of at least Ac1, at least partly hardening the at least partly austenitized sheet steel to give an at least partly hardened sheet steel component, where the at least partly austenitized sheet steel is cooled to a temperature below Ms, at least partly annealing the at least partly hardened sheet steel component at a temperature of less than Ac1 for producing an at least partly quenched and tempered sheet steel component. A further subject of the invention is an at least partly quenched and tempered sheet steel component.

The present invention provides wear-resistant steel which has high hardness while having wear resistance and high impact toughness at low temperature, and a manufacturing method therefor.

Provided herein is a dual-phase stainless steel having excellent carbon dioxide corrosion resistance, excellent sulfide stress corrosion cracking resistance, and excellent sulfide stress cracking resistance. The dual-phase stainless steel contains, in mass %, C: 0.03% or less, Si: 1.0% or less, Mn: 0.10 to 1.5%, P: 0.030% or less, S: 0.005% or less, Cr: 20.0 to 30.0%, Ni: 5.0 to 10.0%, Mo: 2.0 to 5.0%, Cu: 2.0 to 6.0%, N: less than 0.07%, and the balance Fe and unavoidable impurities, and has a structure that is 20 to 70% austenite phase, and 30 to 80% ferrite phase in terms of a volume fraction.

Provided herein is a dual-phase stainless steel having excellent carbon dioxide corrosion resistance, excellent sulfide stress corrosion cracking resistance, and excellent sulfide stress cracking resistance. The dual-phase stainless steel contains, in mass %, C: 0.03% or less, Si: 1.0% or less, Mn: 0.10 to 1.5%, P: 0.030% or less, S: 0.005% or less, Cr: 20.0 to 30.0%, Ni: 5.0 to 10.0%, Mo: 2.0 to 5.0%, Cu: 2.0 to 6.0%, N: less than 0.07%, and the balance Fe and unavoidable impurities, and has a structure that is 20 to 70% austenite phase, and 30 to 80% ferrite phase in terms of a volume fraction.

The entirety or a part of this hot stamped product includes, as a chemical composition, by mass %, C: 0.001% or more and less than 0.080%, Si: 2.50% or less, Mn: 0.01% or more and less than 0.50%, P: 0.200% or less, S: 0.0200% or less, sol.Al: 0.001% to 2.500%, N: 0.0200% or less, Cr: 0.30% or more and less than 2.00%, and a remainder: Fe and impurities, in which a metallographic structure contains, by vol %, ferrite: more than 60.0%, martensite: 0% or more and less than 10.0%, and bainite: 0% or more and less than 20.0%, a tensile strength is less than 700 MPa, and ΔTS, which is a decrease in the tensile strength after a heat treatment at 170° C. for 20 minutes, is 100 MPa or less.

The entirety or a part of this hot stamped product includes, as a chemical composition, by mass %, C: 0.001% or more and less than 0.080%, Si: 2.50% or less, Mn: 0.01% or more and less than 0.50%, P: 0.200% or less, S: 0.0200% or less, sol.Al: 0.001% to 2.500%, N: 0.0200% or less, Cr: 0.30% or more and less than 2.00%, and a remainder: Fe and impurities, in which a metallographic structure contains, by vol %, ferrite: more than 60.0%, martensite: 0% or more and less than 10.0%, and bainite: 0% or more and less than 20.0%, a tensile strength is less than 700 MPa, and ΔTS, which is a decrease in the tensile strength after a heat treatment at 170° C. for 20 minutes, is 100 MPa or less.