A MgO layer is formed using a process flow wherein a Mg layer is deposited at a temperature <200° C. on a substrate, and then an anneal between 200° C. and 900° C., and preferably from 200° C. and 400° C., is performed so that a Mg vapor pressure >10.sup.−6 Torr is reached and a substantial portion of the Mg layer sublimes and leaves a Mg monolayer. After an oxidation between −223° C. and 900° C., a MgO monolayer is produced where the Mg:O ratio is exactly 1:1 thereby avoiding underoxidized or overoxidized states associated with film defects. The process flow may be repeated one or more times to yield a desired thickness and resistance×area value when the MgO is a tunnel barrier or Hk enhancing layer. Moreover, a doping element (M) may be added during Mg deposition to modify the conductivity and band structure in the resulting MgMO layer.

The present invention relates to a superconductive rare-earth metal oxyhydride material and a method for producing the material. The method comprising the steps of: —first the formation on a substrate of a layer of an oxygen free rare-earth metal hydride with a predetermined thickness using a physical vapor deposition process; and —second exposing the rare-earth metal hydride layer to oxidative agent for oxidation where the oxygen reacts with the rare-earth metal hydride that results with obtaining rare-earth metal oxyhydride, the oxidation being below a predetermined limit defined by a measured transparency being less than 10%.

A method of reducing junction resistance variation for junctions in quantum information processing devices fabricated using two-step deposition processes. In one aspect, a method includes providing a dielectric substrate, forming a first resist layer on the dielectric substrate, forming a second resist layer on the first resist layer, and forming a third resist layer on the second resist layer. The first resist layer includes a first opening extending through a thickness of the first resist layer, the second resist layer includes a second opening aligned over the first opening and extending through a thickness of the second resist layer, and the third resist layer includes a third opening aligned over the second opening and extending through a thickness of the third resist layer.

Method for producing a photochromic material and a component including the photochromic material, where the method comprises the steps of:-first the formation on a substrate of a layer of an essentially oxygen free metal hydride with a predetermined thickness using a physical vapor deposition process; and -second exposing the metal hydride layer to oxygen where the oxygen reacts with the metal hydride, resulting in a material with photochromic properties.

Provided are a method for preparing a high-performance wafer-level lead sulfide near infrared photosensitive thin film. Firstly, a surface of the selected substrate material is cleaned; next, a vaporized oxidant is introduced into a vacuum evaporation chamber under a high background vacuum degree, and a PbS thin film is deposited on the clean substrate surface to obtain a microstructure with medium particle, loose structure and consistent orientation. Finally, under a given temperature and pressure, a high-performance wafer-level PbS photosensitive thin film is obtained by sensitizing the film prepared at step S2 using iodine vapor carried by a carrier gas. This preparation method is simple, low-cost and repeatable. The PbS photosensitive thin film has a high photoelectric detection rate. The 600K blackbody room temperature peak detection rate is >8×1010 Jones. The corresponding non-uniformity in a wafer-level photosensitive surface is <5%, satisfying the requirements of preparation of a PbS Mega-pixel-level array imaging system.

A method for dielectric filling of a feature on a substrate yields a seamless dielectric fill with high-k for narrow features. In some embodiments, the method may include depositing a metal material into the feature to fill the feature from a bottom of the feature wherein the feature has an opening ranging from less than 20 nm to approximately 150 nm at an upper surface of the substrate and wherein depositing the metal material is performed using a high ionization physical vapor deposition (PVD) process to form a seamless metal gap fill and treating the seamless metal gap fill by oxidizing/nitridizing the metal material of the seamless metal gap fill with an oxidation/nitridation process to form dielectric material wherein the seamless metal gap fill is converted into a seamless dielectric gap fill with high-k dielectric material.

Provided is a carrier-attached metal foil which can suppress the number of foreign matter particles on the surface of a metal layer to enhance circuit formability, and can keep stable releasability even after heating at a high temperature of 240° C. or higher (for example, 260° C.) for a long period of time. The carrier-attached metal foil includes a carrier, a release functional layer provided on the carrier, the release functional layer including a metal oxynitride, and a metal layer provided on the release functional layer.

A transparent substrate provided with a multilayer film includes: a transparent substrate having two main surfaces; and a multilayer film obtained by laminating a metal oxide layer and a silicon oxide layer in order on at least one of the main surfaces of the transparent substrate. SiO.sub.x in at least one silicon oxide layer in the multilayer film satisfies a relationship 1.55≤x<2.00. The multilayer film has a luminous transmittance of 20% to 89% and a resistance value of 10.sup.4 Ω/sq or higher. x in SiO.sub.x is a value determined by depth direction composition analysis in X-ray photoelectron spectroscopy (XPS) using argon ion sputtering. When the silicon oxide layer is an outermost layer, the value of x is determined excluding a point where a sputtering time is 0 minute.

A preparation method for a high-refractive index hydrogenated silicon film, a high-refractive index hydrogenated silicon film, a light filtering lamination and a light filtering piece. The method includes: (a) by magnetic controlled Si target sputtering, Si deposits on a base body, forming a silicon film, which (b) forms an oxygenic hydrogenated silicon film in environment of active hydrogen and active oxygen, the amount of active oxygen accounts for 4%-99% of the total amount of active hydrogen and active oxygen, or, a nitric hydrogenated silicon film in environment of active hydrogen and active nitrogen, the amount of active nitrogen accounts for 5%-20% of the total amount of active hydrogen and active nitrogen. Sputtering and reactions are separately conducted, Si first deposits on the base body by magnetic controlled Si target sputtering, and then plasmas of active hydrogen and active oxygen/nitrogen react with silicon for oxygenic or nitric SiH.

The embodiments herein relate to electrochromic stacks, electrochromic devices, and methods and apparatus for making such stacks and devices. In various embodiments, an anodically coloring layer in an electrochromic stack or device is fabricated to include nickel tungsten tantalum oxide (NiWTaO). This material is particularly beneficial in that it is very transparent in its clear state.