An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ultrastable cementitious material and a process for making the tile backer board.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ultrastable cementitious material and a process for making the tile backer board.

A catalyst fibrous structure having a catalyst metal carried on a fibrous structure, wherein (a) a Log differential micropore volume distribution curve thereof obtained by measurement using a mercury intrusion technique has a peak having a maximum micropore diameter in the range of from 0.1 m to 100 m: (b) a Log, differential micropore volume at the peak is 0.5 mL/g or more; and (c) an amount of a catalyst metal compound and a binder carried per unit volume is 0.05 g/mL or more. Also, a production method for producing a catalyst fibrous structure.

A catalyst fibrous structure having a catalyst metal carried on a fibrous structure, wherein (a) a Log differential micropore volume distribution curve thereof obtained by measurement using a mercury intrusion technique has a peak having a maximum micropore diameter in the range of from 0.1 m to 100 m: (b) a Log, differential micropore volume at the peak is 0.5 mL/g or more; and (c) an amount of a catalyst metal compound and a binder carried per unit volume is 0.05 g/mL or more. Also, a production method for producing a catalyst fibrous structure.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from .sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 to 300 pounds of force and an insulation R value from 1 to 40, the ultra-stable structural laminate of a cementious material with a nano-molecular veneer and a foam component catalytically reacted into an expanded closed cell foam having a thickness from .sup.th inch to 8 inches, a density from 1.5 pounds/cubic foot to 3 pounds/cubic foot that self-adheres to the cementitious material forming an ultra-stable structural laminate with fire resistance and a lateral nail pull strength from 44 pounds to 300 pounds of force, an insulation R value from 1 to 40, a resistance to seismic impact for earthquakes over 3.1 on the Richter Scale, a break point from 7 lbs/inch to 100 lbs/inch; and a resistance to wind shear equivalent to a 15 mph downburst.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ulstrastable cementitious material and a process for making the tile backer board.

An ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer. A process to make the ultrastable cementitious material. A tile backer board incorporating the ulstrastable cementitious material and a process for making the tile backer board.

A method of excluding particles entrained in formation fluids includes introducing a tubular into a wellbore, forming a sand control device formed from a curable inorganic cementitious mixture infused with an engineered degradable material about the tubular, introducing an external stimulus onto the sand control device causing the degradable material to dissolve, and flowing formation fluids through the sand control device into the tubular.

A method of forming a sand control device comprising: infusing a curable inorganic mixture with a degradable material configured to disintegrate upon exposure to an external stimuli; forming the curable inorganic mixture infused with the degradable material about a tubular; and curing the curable inorganic mixture infused with the degradable material.