A dielectric ceramic composition and a multilayer ceramic electronic component are provided, the dielectric ceramic composition includes a barium titanate base material main component and a subcomponent, a microstructure after sintering includes a first crystal grain including 3 or less domain boundaries and a second crystal grain including 4 or more domain boundaries, and an area ratio of the second crystal grain to the total crystal grains is 20% or less.

Disclosed herein are embodiments of composite hexagonal ferrite materials formed from a combination of Y phase and Z phase hexagonal ferrite materials. Advantageously, embodiments of the material can have a high resonant frequency as well as a high permeability. In some embodiments, the materials can be useful for magnetodielectric antennas.

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material and methods of manufacturing. The hexagonal ferrite material can be Y-phase strontium hexagonal ferrite material. In some embodiments, strontium can be substituted out for a trivalent or tetravalent ion composition including potassium, thereby providing for advantageous properties.

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material and methods of manufacturing. The hexagonal ferrite material can be Y-phase strontium hexagonal ferrite material. In some embodiments, strontium can be substituted out for a trivalent or tetravalent ion composition including potassium, thereby providing for advantageous properties.

Disclosed herein are doped perovskite oxides. The doped perovskite oxides may be used as a cathode material in an electrochemical cell to electrochemically generate ammonia from N.sub.2. The doped perovskite oxides may be combined with nitride compounds, for instance iron nitride, to further increase the efficiency of the ammonia production.

Provided is a ferrite sintered magnet including a ferrite phase having a magnetoplumbite-type crystal structure. x, y, and m satisfy the following Equations (1), (2), and (3) when composition of the ferrite sintered magnet is represented by R.sub.1-xA.sub.xFe.sub.m-yCo.sub.y, where R denotes at least one kind of element selected from rare earth elements including Y and A denotes Ca or Ca and elements including at least one kind selected from Sr or Ba. The content of B in the ferrite sintered magnet is from 0.1% to 0.6% by mass in terms of B.sub.2O.sub.3.

0.2≤x≤0.8  (1)

0.1≤y≤0.65  (2)

3≤m≤14  (3)

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material and methods of manufacturing. The hexagonal ferrite material can be Y-phase strontium hexagonal ferrite material. In some embodiments, strontium can be substituted out for a trivalent or tetravalent ion composition including potassium, thereby providing for advantageous properties.

A sintered ferrite magnet having a composition of metal elements of Ca, R, A, Fe and Co, which is represented by the general formula of Ca.sub.1−x−yR.sub.xA.sub.yFe.sub.2n−zCo.sub.z, wherein R is at least one of rare earth elements indispensably including La; A is Sr and/or Ba; x, y, z and n represent the atomic ratios of Ca, R, A, Fe and Co; 2n represents a molar ratio expressed by 2n=(Fe+Co)/(Ca+R+A); and x, y, z and n meet the conditions of 0.15≤x≤0.35, 0.05≤y≤0.40, (1−x−y)>y, 0<z≤0.18, and 7.5≤(2n−z)<11.0.

Provided is a red mud-based composite calcium ferrite and a preparation method and use thereof. The preparation method of the red mud-based composite calcium ferrite includes the following steps: mixing red mud and a calcium source, and roasting an obtained mixture in an oxygen-containing atmosphere to obtain the red mud-based composite calcium ferrite; where the calcium source is selected from the group consisting of lime and calcium carbonate. In the present disclosure, the composite calcium ferrite is prepared using a solid waste red mud, with a greatly reduced cost of raw materials; on the other hand, compared with traditional calcium ferrite, the composite calcium ferrite mainly has phase structures of CaFe.sub.2O.sub.4, Ca.sub.2FeAlO.sub.5, and Ca.sub.2Fe.sub.2O.sub.5. Therefore, the composite calcium ferrite has a lower melting point, a higher lime dissolution efficiency, and better fluxing and dephosphorization effects during primary smelting and refining of molten steel, and has broad prospects for use in industry.

Disclosed herein are embodiments of an enhanced resonant frequency hexagonal ferrite material and methods of manufacturing. The hexagonal ferrite material can be Y-phase strontium hexagonal ferrite material. In some embodiments, sodium can be added into the crystal structure of the hexagonal ferrite material in order to achieve high resonance frequencies while maintaining high permeability.