A cubic boron nitride sintered material includes: more than or equal to 50 volume % and less than 80 volume % of cubic boron nitride grains; and more than 20 volume % and less than or equal to 50 volume % of a binder phase, and when an oxygen content is measured in a direction perpendicular to an interface between cubic boron nitride grains using TEM-EDX, a first region having an oxygen content larger than an average value of an oxygen content of a cubic boron nitride grain exists, the interface exists in the first region, and a length of the first region along the direction perpendicular to the interface is more than or equal to 0.1 nm and less than or equal to 10 nm.

A method of forming a shaped abrasive particle including extruding a mixture into a form, applying a dopant material to an exterior surface of the form, and forming a precursor shaped abrasive particle from the form.

A superabrasive compact and a method of making the superabrasive compact are disclosed. A superabrasive compact may include a plurality of polycrystalline superabrasive particles made of surface functionalized superabrasive particles. The surface functionalized superabrasive particles may have halogens or organic moiety instead of hydrogen.

A method of forming a cutting element comprises forming a first material comprising discrete coated particles within a container. The first material is pressed to form a first green structure comprising interbonded coated particles. A second material comprising additional discrete coated particles is formed over the first green structure within the container. The second material is pressed to form a second green structure comprising additional interbonded coated particles. The first green structure and the second green structure are sintered to form a multi-layered cutting table. Additional methods of forming a cutting element, a cutting element, and an earth-boring tool are also described.

A method of manufacturing a silicon-containing oxide-coated aluminum nitride particle; a method of manufacturing a heat dispersing resin composition containing the silicon-containing oxide-coated aluminum nitride particle; and the silicon-containing oxide-coated aluminum nitride particle. The method of manufacturing includes: a first step of covering the surface of the aluminum nitride particle with an organic silicone compound including a specific structure; and a second step of heating the aluminum nitride particle covered with the organic silicone compound at a temperature of 300° C. or more and less than 1000° C., wherein the content of carbon atoms in the silicon-containing oxide-coated aluminum nitride particle is less than 1000 ppm by mass.

A dielectric assembly solid dielectric elements within a liquid or solid matrix material. The dielectric assembly may be manufactured by pressing a dielectric powder to form pressed dielectric elements, sintering the pressed dielectric elements to form the solid dielectric elements, and assembling the solid dielectric elements within the matrix material to form the dielectric assembly. The solid dielectric elements can be specifically oriented (e.g., in one or more tiled layers) or randomly oriented, and the dielectric assemblies can be molded and/or machined into desired 3D geometries. The dielectric assemblies can be relatively large (e.g., >1 mm.sup.3) while having bulk dielectric constants higher than conventional slurries and composites formed of dielectric powder in a liquid or solid matrix.

An object of the present invention is to provide zirconium oxide nanoparticles that have excellent dispersibility in a polar solvent and are capable of increasing a core concentration in a dispersion liquid. Zirconium oxide nanoparticles according to the present invention are coated with at least one compound selected from the group consisting of R.sup.1—COOH, (R.sup.1O).sub.3-n—P(O)—(OH).sub.n, (R.sup.1).sub.3-n—P(O)—(OH).sub.n, (R.sup.1O)—S(O)(O)—(OH), R.sup.1—S(O)(O)—(OH), and (R.sup.1).sub.4-m—Si(R.sup.4).sub.m, wherein R.sup.1 represents a group comprising a carbon atom and at least one element selected from the group consisting of an oxygen atom, a nitrogen atom, and a sulfur atom, and having the total number of carbon atoms, oxygen atoms, nitrogen atoms, and sulfur atoms of 8 or less; R.sup.4 represents a halogen atom or —OR.sup.2, and R.sup.2 represents a hydrogen atom or an alkyl group; and n represents 1 or 2, and m represents an integer of 1 to 3.

An electro-conductive B.sub.4C—TiB.sub.2 has a microstructure in which large B.sub.4C grains are coated by small TiB.sub.2 grains. The composite ceramic includes 10˜30% by volume of TiB.sub.2. A method for preparing the electro-conductive B.sub.4C—TiB.sub.2 composite ceramic includes: (1) weighing B.sub.4C, TiC, and amorphous B powder; (2) mixing evenly and drying thoroughly the powders; and (3) loading the mixed powder into a graphite mold; and placing the graphite mold in a spark plasma sintering furnace for sintering under vacuum, where the sintering is performed at 2000° C. and 50 MPa for 5˜20 min.

The present invention relates to a composite material comprising wollastonite fibres embedded within a ceramic matrix. The wollastonite fibres are bonded to the ceramic matrix by a glassy bonding phase comprising a glass component comprising at least 80 wt % of oxides of calcium, silicon and aluminium. The material is used in the processing of molten metal, e.g. as a pump, degasser, flux injector or scrap submergence device.

A silicon carbide flow reactor fluidic module comprises a monolithic closed-porosity silicon carbide body and a tortuous fluid passage extending through the silicon carbide body, the tortuous fluid passage lying within two or more layers with the silicon carbide body, the tortuous passage having an interior surface, the interior surface having a surface roughness of less than 10 μm Ra. A method of forming the fluidic module is also disclosed.