A piezoelectric composition including manganese and a complex oxide having a perovskite structure represented by a general formula ABO.sub.3, wherein an A site element in the ABO.sub.3 is potassium or potassium and sodium, a B site element in the ABO.sub.3 is niobium, a concentration distribution of the manganese has a variation, and the variation shows a CV value of 35% or more and 440% or less.

A method for manufacturing a sintered product from a three-dimensional object as a solution includes: a preparation step S11, a degreasing step S12, and a sintering step S13. In S11, a multilayer made of an ink containing inorganic particles and an organic material is formed to prepare a three-dimensional object. S12 includes: a first degreasing step of heating the three-dimensional object under an inert gas atmosphere at a first average degreasing temperature (T1) for a first heating time to degrease the organic material; and a second degreasing step of heating the three-dimensional object degreased in the first degreasing step, under an inert gas atmosphere at a second average degreasing temperature (T2) higher than Ti for a second heating time to degrease the organic material. In S13, the three-dimensional object degreased in the second degreasing step is sintered at an average sintering temperature higher than T2 to obtain a sintered product.

A three-dimensional shaped object producing method is provided that includes: forming a layer from secondary particles (51) including a binder resin and primary particles containing at least a ceramic material; and applying a liquid that dissolves the binder resin on the formed layer. The liquid contains a solvent having a boiling point of 100° C. or higher and 210° C. or lower, a relative energy difference (RED) between the binder resin and the solvent is 1.0 or less, and the secondary particles (51) have a loose bulk density of 25% or higher and 55% or lower.

Provided is a sintered body that has high heat dissipation and from which light can be emitted when excited by an excitation light source, a light emitting device, a wavelength conversion member, and a method for manufacturing the sintered body.

The sintered body includes aluminum nitride and europium, has a thermal diffusivity of 27.0 mm.sup.2/s or greater as measured by a laser flash method at 25° C., and emits green light when excited by an excitation light source.

A dielectric ceramic composition contains dielectric particles containing a main component represented by a composition formula (Ba.sub.1-x-ySr.sub.xCa.sub.y).sub.m(Ti.sub.1-zZr.sub.z)O.sub.3 and grain boundaries present between the dielectric particles. The values of m, x, y, and z in the composition formula are all molar ratios. In the composition formula, 0.9≤m≤1.4, 0≤x<1.0, 0<y≤1.0, 0.9≤(x+y)≤1.0, and 0.9≤z≤1.0 are satisfied. The dielectric particles contain specific structural particles having a predetermined intragranular structure, and each of the specific structural particles intragranularly includes a first region and a second region having different Ca concentrations from each other. C2/C1 is less than 0.8 in which C1 is an average value of the Ca concentration in the first region and C2 is an average value of the Ca concentration in the second region.

The invention belongs to the field of electronic ceramics and its manufacturing, in particular to the modified NiO-Ta.sub.2O.sub.5-based microwave dielectric ceramic material sintered at low temperature and its preparation method. It is guided by ion doping modification, not only considering the substitution of ions with similar radius, such as Zn.sup.2+ replacing Ni.sup.2+ ions, V.sup.5+ replacing Ta.sup.5+ ions; Meanwhile, the selected doped oxide still has the property of low melting point. Therefore, the microwave dielectric properties of NiO-Ta.sub.2O.sub.5-based ceramic material can be improved and the appropriate sintering temperature can be reduced. In the invention, by adjusting the molar content of each raw material, the NiO-Ta.sub.2O.sub.5-based ceramic material with low-temperature sintering, stable temperature and excellent microwave dielectric property is directly synthesized at one time, which can be widely applied to the technical field of LTCC.

It is described a process for producing transparent ceramic bodies with at least two zones having different garnet composition, in particular in which one of said zones has composition Y.sub.3AI.sub.5O.sub.12. The invention is especially useful for the production of transparent ceramic bodies having preset complex shapes and/or a controlled complex distribution of doping ions.

It is described a process for producing transparent ceramic bodies with at least two zones having different garnet composition, in particular in which one of said zones has composition Y.sub.3AI.sub.5O.sub.12. The invention is especially useful for the production of transparent ceramic bodies having preset complex shapes and/or a controlled complex distribution of doping ions.

A temperature-stable modified NiO—Ta.sub.2O.sub.5-based microwave dielectric ceramic material and a preparation method thereof are provided. Using ion doping modification to form solid solution structure is an important measure to adjust microwave dielectric properties, especially the temperature stability. Based on formation rules of the solid solution, ion replacement methods are designed including Ni.sup.2+ ions are replaced by Cu.sup.2+ ions, and (Ni.sub.1/3Ta.sub.2/3).sup.4+ composite ions are replaced by [(Al.sub.1/2Nb.sub.1/2).sub.ySn.sub.1-y].sup.4+ composite ions, which considers that cations with similar ionic radii to Ni.sup.2+ and Ta.sup.5+ ions can be introduced into the NiTa.sub.2O.sub.6 ceramic for doping under the same coordination environment (coordination number=6), and therefore a ceramic material with the NiTa.sub.2O.sub.6 solid solution structure can be obtained. The microwave dielectric ceramic material with excellent temperature stability and low loss is finally prepared by adjusting molar contents of each of doped ions, and its microwave dielectric properties are excellent.

A temperature-stable modified NiO—Ta.sub.2O.sub.5-based microwave dielectric ceramic material and a preparation method thereof are provided. Using ion doping modification to form solid solution structure is an important measure to adjust microwave dielectric properties, especially the temperature stability. Based on formation rules of the solid solution, ion replacement methods are designed including Ni.sup.2+ ions are replaced by Cu.sup.2+ ions, and (Ni.sub.1/3Ta.sub.2/3).sup.4+ composite ions are replaced by [(Al.sub.1/2Nb.sub.1/2).sub.ySn.sub.1-y].sup.4+ composite ions, which considers that cations with similar ionic radii to Ni.sup.2+ and Ta.sup.5+ ions can be introduced into the NiTa.sub.2O.sub.6 ceramic for doping under the same coordination environment (coordination number=6), and therefore a ceramic material with the NiTa.sub.2O.sub.6 solid solution structure can be obtained. The microwave dielectric ceramic material with excellent temperature stability and low loss is finally prepared by adjusting molar contents of each of doped ions, and its microwave dielectric properties are excellent.