Core particles produced in situ or introduced as preformed core particles are coated with a layer of carbon. Non-carbon as well as some carbon-based core materials can be utilized. The resulting carbon coated particles can find applications in rubber products, for instance as reinforcement for tire components.

Core particles produced in situ or introduced as preformed core particles are coated with a layer of carbon. Non-carbon as well as some carbon-based core materials can be utilized. The resulting carbon coated particles can find applications in rubber products, for instance as reinforcement for tire components.

A coating material containing an oxyfluoride of yttrium and having a Fisher diameter of 1.0 to 10 μm and a tap density TD to apparent density AD ratio, TD/AD, of 1.6 to 3.5. The coating material preferably has a pore volume of pores with a diameter of 100 μm or smaller of 1.0 cm.sup.3/g or less as measured by mercury intrusion porosimetry. A coating containing an oxyfluoride of yttrium and having a Vickers hardness of 200 HV0.01 or higher. The coating preferably has a fracture toughness of 1.0×10.sup.2 Pa.Math.m.sup.1/2 or higher.

An article includes a ceramic-based substrate and a barrier layer on the ceramic-based substrate. The barrier layer includes a matrix phase and a network of gettering particles in the matrix phase. The gettering particles have an average maximum dimension between about 30 and 70 microns. The gettering particles have maximum dimensions that range from about 1 to 100 microns, and a dispersion of barium-magnesium alumino-silicate particles in the matrix phase. A composite material and a method of applying a barrier layer to a substrate are also disclosed.

A heat dissipation member includes a thermal radiation ceramic material, and the thermal radiation ceramic material contains silicon nitride and boron nitride as main components. The ratio of the mass of boron nitride to the mass of silicon nitride and boron nitride is 10 mass % to 40 mass %.

Proposed are a part having a corrosion-resistant layer that minimizes peeling off and particle generation of a porous ceramic layer, a manufacturing process apparatus having the same, and a method of manufacturing the part.

Proposed are a part having a corrosion-resistant layer that minimizes peeling off and particle generation of a porous ceramic layer, a manufacturing process apparatus having the same, and a method of manufacturing the part.

An alumina-ceramic-based electrical insulator, to a method for producing the insulator, and to a vacuum tube includes the insulator. The electrical insulator is for insulating two electrodes of a vacuum tube through which a charged particle beam flows, the electrical insulator being formed of an alumina-based ceramic. The ceramic comprises a vitreous phase of between 2% and 8% by weight into which at least one metal oxide is diffused from a face of the electrical insulator.

An alumina-ceramic-based electrical insulator, to a method for producing the insulator, and to a vacuum tube includes the insulator. The electrical insulator is for insulating two electrodes of a vacuum tube through which a charged particle beam flows, the electrical insulator being formed of an alumina-based ceramic. The ceramic comprises a vitreous phase of between 2% and 8% by weight into which at least one metal oxide is diffused from a face of the electrical insulator.

An environmental barrier coating, comprising a substrate containing silicon; an environmental barrier layer applied to said substrate; said environmental barrier layer comprising a rare earth composition.