The present invention relates to a nitrogen-doped sulfide-based solid electrolyte for all-solid batteries. The a nitrogen-doped sulfide-based solid electrolyte for all-solid batteries includes a compound with an argyrodite-type crystal structure represented by the following Formula 1:

Li.sub.aPS.sub.bN.sub.cX.sub.d  [Formula 1]

wherein 6≤a≤7, 3≤b≤6, 0≤c≤1, 0≤d≤2, and

each X is the same or different halogen atom selected from the group consisting of chlorine (Cl), bromine (Br), and iodine (I).

The present invention relates to a nitrogen-doped sulfide-based solid electrolyte for all-solid batteries. The a nitrogen-doped sulfide-based solid electrolyte for all-solid batteries includes a compound with an argyrodite-type crystal structure represented by the following Formula 1:

Li.sub.aPS.sub.bN.sub.cX.sub.d   [Formula 1] wherein 6≤a≤7, 3<b<6, 0<c≤1, 0<d≤2, and each X is the same or different halogen atom selected from the group consisting of chlorine (Cl), bromine (Br), and iodine (I).

The invention relates to a batch for producing an unshaped refractory ceramic product, to a method for producing an unshaped refractory ceramic product, and to an unshaped refractory ceramic product produced by the method.

A composite material containing a matrix and a fibrous reinforcement, in particular a textile embedded in the matrix. The matrix includes a geopolymer of the poly(phospho-sialate) type having the following formula I: (1) (—P—O—Si—O—Al—O—).sub.n in which n is greater than 2. The matrix further includes zirconium covalently bonded to the matrix, especially in the —ZrO form and/or in the —O—Zr—O form. The matrix has a melting temperature greater than 700° C., especially equal to or greater than 1200° C.

Disclosed are product (e.g., board), slurry, and methods relating to an uncooked starch that can be used to enhance strength in one or more gypsum layers in the board. The uncooked starch has a hot water viscosity of from about 20 BU to about 300 BU according to the HWVA method, and/or a mid-range peak viscosity of from about 120 Brabender Units to about 1000 Brabender Units.

Disclosed herein is a doped perovskite barium stannate material, which has a chemical general formula of BaA.sub.xB.sub.xSn.sub.1-2xO.sub.3, where A is at least one of In, Y, Bi and La; B is at least one of Nb and Ta, and 0<x≤0.025. The doped perovskite barium stannate material disclosed in the invention has a high dielectric constant, low dielectric loss and good temperature-stability, and it can be used not only as low-frequency ceramic capacitor dielectrics, but also as microwave dielectric ceramics because of its excellent microwave dielectric properties, implying the potential application in the field of microwave communication. What's more, disclosed is a method to prepare the doped perovskite barium stannate material and the application of the doped perovskite barium stannate material in a low-frequency ceramic capacitor or microwave communication dielectric ceramics.

A ceramic particle includes a core and a modification layer. The core is made of magnesium or a magnesium alloy. The core has a diameter of 30-100 μm. The modification layer covers an outer surface of the core. The modification layer includes calcium and phosphorus. A method for producing a ceramic particle includes providing a core made of magnesium or a magnesium alloy and having a diameter of 30-100 μm. A calcium salt and a phosphorus salt are dissolved in a solvent. A chelating agent is added into the solvent to form a modifying solution. The core is added into the modifying solution to form a modification layer on an outer surface of the core in a temperature range of 5-40° C. The modification layer includes calcium and phosphorus.

The present invention relates to a paste-type composition for a fused deposition modeling (FDM) 3D printer comprising: a ceramic powder including CaO and SiO.sub.2; and a binder solution, wherein the composition may be injected into the FDM 3D printer in the form of a paste to rapidly manufacture a molded article without a melting process and may precisely implement a variety of geometries to be utilized as a biological replacement for medical use.

This document describes processes for preparing ceramics, especially lithium-based ceramics. The ceramics produced by this process and their use in electrochemical applications are also described as well as electrode materials, electrodes, electrolyte compositions, and electrochemical cells comprising them.

A method of making a ceramic composite comprises forming a wet ceramic composition comprising a plurality of discrete ceramic components and a fluxing agent dissolved in a solvent. At least a portion of the solvent is removed from the wet ceramic composition to form a dried ceramic composition comprising the plurality of discrete ceramic components coated with the fluxing agent. The dried ceramic composition is sintered to form the ceramic composite, the sintering being carried out at a sinter temperature sufficient to fuse the discrete ceramic components at bridging sites formed where two or more of the discrete ceramic components coated with fluxing agent are in physical contact.