The present invention is directed to a method for producing a silicon nitride sintered material, the method including heating a molded article, which contains a silicon nitride powder having a β phase ratio of 80% or more, a dissolved oxygen content of 0.2% by mass or less, and a specific surface area of 5 to 20 m.sup.2/g, and a sintering auxiliary containing a compound having no oxygen bond, and which has an overall oxygen content controlled to be 1 to 15% by mass and an aluminum element overall content controlled to be 800 ppm or less, to a temperature of 1,200 to 1,800° C. in an inert gas atmosphere under a pressure of 0 MPa.Math.G or more and less than 0.1 MPa.Math.G to sinter the silicon nitride.

In the present invention, there can be provided a method for producing a silicon nitride sintered material, which method is advantageous in that a silicon nitride sintered material having high thermal conductivity can be obtained even when using a silicon nitride powder having a high β phase ratio and conducting calcination under normal pressure or substantially normal pressure.

A ferrite sintered magnet 100 comprises M-type ferrite crystal grains 4 having a hexagonal structure, two-crystal grain boundaries 6a formed between two of the M-type ferrite crystal grains 4, and multiple-crystal grain boundaries 6b surrounded by three or more of the M-type ferrite crystal grains 4. This ferrite sintered magnet 100 contains at least Fe, Ca, B, and Si, and contains B in an amount of 0.005 to 0.9 mass % in terms of B.sub.2O.sub.3, the two-crystal grain boundaries 6a and the multiple-crystal grain boundaries 6b contain Si and Ca, and in a cross-section parallel to a c-axis of the ferrite sintered magnet, when the number of multiple-crystal grain boundaries 6b having a maximum length of 0.49 to 5 μm per cross-sectional area of 76 μm.sup.2 is N, N is 7 or less.

A phosphor plate including: a complex containing an α-sialon phosphor and a sintered body containing spinel represented by a general formula M.sub.2xAl.sub.4-4xO.sub.6-4x (where M represents at least one of Mg, Mn, and Zn, and 0.2<x<0.6). In addition, there is provided a light emitting device including: a group III nitride semiconductor light emitting element; and the phosphor plate provided on one surface of the group III nitride semiconductor light emitting element. Further, there is provided a method for manufacturing the phosphor plate.

Disclosed herein is a sintered ceramic body comprising from 90% to 99.9% by volume of polycrystalline yttrium aluminum garnet (YAG) as measured using XRD and image processing methods and a volumetric porosity of from 0.1 to 4% as calculated from density measurements performed in accordance with ASTM B962-17. The sintered ceramic body may have a total purity of 99.99% and greater and a grain size of from 0.3 to 8 μm. A method of making the sintered ceramic body is also disclosed.

A ceramic powder material containing a garnet-type compound containing Li, wherein the ceramic powder material has a pore volume of 0.4 mL/g or more and 1.0 mL/g or less.

A Li ion conductor having a composition different from a conventional composition is provided. The Li ion conductor contains at least one selected from a group Q consisting of Ga, V, and Al, Li, La and O. A part of an Li site is optionally substituted with a metal element D, a part of an La site is optionally substituted with a metal element E, and parts of Ga, V and Al sites are optionally substituted with a metal element J. A mole ratio of an amount of Li to a total amount of La, the element E, Ga, V, Al, and the element J is not lower than 8.1/5 and not higher than 9.5/5. A mole ratio of a total amount of Ga, V, and Al to a total amount of La and the element E is not lower than 1.1/3 and not higher than 2/3.

Disclosed are: damage-resistant ECMCs that need to work and remain elastic between minus 120° C. and positive 300° C.; ECMCs that need to be able to contain a flame of 1900° C. for more than 90 minutes; and composite structures, especially highly stressed structures. One of the characteristic problems of ceramic matrices is their fragility. Indeed, when a fracture starts, it propagates easily in the matrix. Disclosed are elastic ceramic matrix composites (ECMCs), for which: the ceramic matrix is split into solid “ceramic microdomains” (CMDs); the CMDs are connected to one another by a dense network of “elastic microelements” (EMEs); and the bonds between the EMEs and the CMDs are strong chemical bonds, preferably covalent.

A ferrite sintered magnet 100 comprises M-type ferrite crystal grains 4 having a hexagonal crystal structure, two-crystal grain boundaries 6a formed between two of the M-type ferrite crystal grains 4, and multiple-crystal grain boundaries 6b surrounded by three or more of the M-type ferrite crystal grains 4. This ferrite sintered magnet 100 contains at least Fe, Ca, B, and Si, and contains B in an amount of 0.005 to 0.9 mass % in terms of B.sub.2O.sub.3, the two-crystal grain boundaries 6a and the multiple-crystal grain boundaries 6b contain Si and Ca, and in a cross-section parallel to a c-axis of the ferrite sintered magnet, when the number of multiple-crystal grain boundaries having a maximum length of 0.088 or more and less than 0.49 μm per cross-sectional area of 76 μm.sup.2 is P, P is 8 or more.

A powder intended for the manufacture of a sintered dental article, The powder has a chemical analysis such that, as weight percentages based on the oxides: Al.sub.2O.sub.3: 0.2%, oxides other than ZrO.sub.2, HfO.sub.2, Yb.sub.2O.sub.3, Y.sub.2O.sub.3 and Al.sub.2O.sub.3: <0.5%, and ZrO.sub.2+HfO.sub.2+Yb.sub.2O.sub.3+Y.sub.2O.sub.3: balance to 100%, with HfO.sub.2<2%. The contents of Yb.sub.2O.sub.3 and Y.sub.2O.sub.3, as molar percentages based on the sum of ZrO.sub.2, HfO.sub.2, Yb.sub.2O.sub.3 and Y.sub.2O.sub.3, being such that Yb.sub.2O.sub.3≥1%, 0.5%≤Y.sub.2O.sub.3<2%, and Yb.sub.2O.sub.3+Y.sub.2O.sub.3≤5.5%. The powder has a specific surface area of greater than or equal to 5 m.sup.2/g and less than or equal to 16 m.sup.2/g. The powder has a median size of greater than or equal to 0.1 μm and less than or equal to 0.7 μm.

A zirconia powder in which when a stabilizer is Y.sub.2O.sub.3, a content thereof is 1.4 mol % or more and less than 2.0 mol %; when the stabilizer is Er.sub.2O.sub.3, a content thereof is 1.4 mol % or more and 1.8 mol % or less; when the stabilizer is Yb.sub.2O.sub.3, a content thereof is 1.4 mol % or more and 1.8 mol % or less; and when the stabilizer is CaO, a content thereof is 3.5 mol % or more and 4.5 mol % or less; and in a range of 10 nm or more and 200 nm or less in a pore distribution, a peak top diameter of a pore volume distribution is 20 nm or more and 120 nm or less, a pore volume is 0.2 ml/g or more and less than 0.5 ml/g, and a pore distribution width is 30 nm or more and 170 nm or less.