A high strength ceramic body for use in a regenerative burner media bed, comprising a generally spherical refractory portion and a plurality of irregular aggregate portions distributed randomly throughout the generally spherical portion. The aggregate portions are selected from the group comprising tabular alumina, white fused alumina, mullite, chamotte, and combinations thereof. The generally spherical portion has a porosity of less than 1 percent and is more than 99.5 weight percent alumina.

A molding tool made of carbon or graphite, namely a casting mold or a casting core for the processing of molten metal or to a molding tool for the processing of molten glass, such as for example a blow mold and a method for producing the molding tool.

A ceramic honeycomb structure including large numbers of flow paths partitioned by porous cell walls; (a) the cell walls having porosity of 55-65%; and (b) in a pore diameter distribution in the cell walls measured by mercury porosimetry, (i) a pore diameter at a cumulative pore volume corresponding to specific percentages of the total pore volume being within specific ranges and satisfying specific relationships; (ii) the difference of a logarithm of the pore diameter at a cumulative pore volume corresponding to 20% of the total pore volume and a logarithm of the pore diameter at 80% being 0.39 or less; and (iii) the volume of pores of more than 100 m being 0.05 cm.sup.3/g or less.

Sintered product having a chemical analysis such that, in mass percentages: SiO.sub.2 content is greater than 0.2% and less than 2%, and CaO content is greater than 0.1% and less than 1.5%, and MgO content is less than 0.3%, and alumina and other elements being the complement at 100%, the content of other elements being less than 1.5%, having a relative density greater than 90%, comprising, for more than 90% of its volume, a stack of ceramic platelets (10) laid flat, all of said platelets having an average thickness less than 3 m, more than 95% by number of said platelets each containing more than 95% by mass of alumina, having a width (l) greater than 81 mm.

The invention relates to a use of a refractory material for contact with a liquid metal or alloy, a method for the manufacture of an article made of said material, the article so obtained and a method of use of said article. The refractory material is obtained from a mixture comprising from 0 wt. % to 40 wt. % of aggregates and/or fmes of zirconia; from 10 wt. % to 50 wt. % of aggregates and/or fmes of alumina; and from 20 wt. % to 50 wt. % of aggregates and/or fines of mullite; formed into a desired shape and then subjected to a heating treatment at a temperature of from 750 C. to 1500 C.

A solid composite material combining: an inorganic pigment in the form of discrete particles each comprising a colored core and a coating adapted to allow light to pass through and a matrix based on metalloid or metal oxide, said matrix being adapted to allow light to pass through.

An article comprises a first member comprising a first carbon composite; and a second member disposed on the first member and comprising a second carbon composite and a reinforcing agent, wherein the second member has a gradient in the weight ratio of the second carbon composite to the reinforcing agent, and wherein the first member has one or more of the following properties different than those of the second member: elasticity; corrosion resistance; erosion resistance; or hardness.

A ceramic honeycomb structure including large numbers of flow paths partitioned by porous cell walls; (a) the cell walls having porosity of 55-65%; and (b) in a pore diameter distribution in the cell walls measured by mercury porosimetry, (i) pore diameters at cumulative pore volumes corresponding to specific percentages of the total pore volume being within specific ranges and satisfying specific relationships; (ii) the difference of a logarithm of the pore diameter at a cumulative pore volume corresponding to 20% of the total pore volume and a logarithm of the pore diameter at 80% being 0.39 or less; and (iii) the volume of pores of more than 100 m being 0.05 cm.sup.3/g or less.

A solid composite material (16) combining: an inorganic pigment (10) in the form of discrete particles each comprising a colored core and a coating adapted to allow light to pass through; and a matrix (12) based on metalloid or metal oxide, said matrix being adapted to allow light to pass through.

A method for forming a self-healing ceramic matrix composite (CMC) component includes depositing a first self-healing particulate material in a first region of a CMC preform of the CMC component and depositing a second self-healing particulate material having a different chemical composition than the first self-healing particulate material in a second region of the CMC preform distinct from the first region.