A method of forming a composite cutter for a downhole drilling tool is described. The method includes: mixing a polycrystalline diamond powder and a cubic boron nitride powder with a molar ratio between 0.1 and 0.9 to form a catalyst-free composite mixture; placing the catalyst-free composite mixture into a mold configured in a shape of a cutter; exposing the catalyst-free composite mixture to an ultra-high-pressure, high-temperature treatment including a pressure between 11 Gigapascals (GPa) and 20 GPa, and a temperature between 1300 Kelvins (K) and 2600 K to form a solid composite body; and cooling the solid composite body to form the composite cutter.

An object of the present invention is to provide an IGZO sputtering target capable of improving uniformity for at least one property selected from the number of microcracks in the structure, the number of pores in the sintered body structure, and surface roughness.

The IGZO sputtering target according to the present invention has an oxide sintered body, the oxide sintered body comprising indium (In), gallium (Ga), zinc (Zn) and unavoidable impurities, wherein, on a surface of the oxide sintered body, a lightness difference ΔL* satisfies ΔL*<3.0, in which the ΔL* is obtained by subtracting lightness Lc*at a central portion on the surface from lightness Le* at a position of 10 mm from an end portion to the central portion side on the surface, and wherein the oxide sintered body has a relative density of 97.0% or more.

A multilayer ceramic electronic component includes: a ceramic body including a dielectric layer having a main component represented by (Ba.sub.1-xCa.sub.x)(Ti.sub.1-y)(Zr, Sn, Hf).sub.y)O.sub.3 (where, 0≤x≤1, 0≤y≤0.5), and having a plurality of grains and grain boundaries disposed between the plurality of grains, and including first and second internal electrodes alternately stacked with the dielectric layer interposed therebetween; a first external electrode; and a second external electrode, wherein the dielectric layer includes a triple point in contact with three grain boundaries and a secondary phase of Si disposed inside the triple point, wherein a dispersion of an Si content at an interface between the dielectric layer and the internal electrode may be 1% by weight or less.

Set forth herein are garnet material compositions, e.g., lithium-stuffed garnets and lithium-stuffed garnets doped with alumina, which are suitable for use as electrolytes and catholytes in solid state battery applications. Also set forth herein are lithium-stuffed garnet thin films having fine grains therein. Disclosed herein are novel and inventive methods of making and using lithium-stuffed garnets as catholytes, electrolytes and/or anolytes for all solid state lithium rechargeable batteries. Also disclosed herein are novel electrochemical devices which incorporate these garnet catholytes, electrolytes and/or anolytes. Also set forth herein are methods for preparing novel structures, including dense thin (<50 um) free standing membranes of an ionically conducting material for use as a catholyte, electrolyte, and, or, anolyte, in an electrochemical device, a battery component (positive or negative electrode materials), or a complete solid state electrochemical energy storage device. Also, the methods set forth herein disclose novel sintering techniques, e.g., for heating and/or field assisted (FAST) sintering, for solid state energy storage devices and the components thereof.

Setter plates are fabricated from Li-stuffed garnet materials having the same, or substantially similar, compositions as a garnet Li-stuffed solid electrolyte. The Li-stuffed garnet setter plates, set forth herein, reduce the evaporation of Li during a sintering treatment step and/or reduce the loss of Li caused by diffusion out of the sintering electrolyte. Li-stuffed garnet setter plates, set forth herein, maintain compositional control over the solid electrolyte during sintering when, upon heating, lithium is prone to diffuse out of the solid electrolyte.

The present invention provides a method for making a high strength, small grain size ceramic having a trans-granular fracture mode by rapid densification of a green body and subsequent cooling of the densified ceramic. The ceramic may include dislocations, defects, dopants, and/or secondary phases that are formed as a result of the process and resulting in stress fields capable of redirecting or arresting cracks within the material. This ceramic can maintain transparency from ultraviolet to mid-wave infrared.

The invention relates to the field of ceramics and concerns a method for use in displays of electronic devices with high mechanical stress, for example. The object of the present invention is to provide a method by means of which thin ceramic parts having thicknesses of substantially <1 mm with high transparency are produced. The object is achieved by a method for producing thin transparent ceramic parts, in which ceramic powders are mixed together with a solvent and a monomer and a photoinitiator, and at least 0.0005% by mass of a photoinitiator is added, the mixture is subsequently introduced into a mould, then the mixture is irradiated for at least 1 min with light which has a wavelength for activating the photoinitiator, the moulded body is subsequently removed from the mould and dried, and then the debinding and sintering of the moulded body is carried out.

In an embodiment a conversion element includes a first phase and a second phase, wherein the first phase comprises lutetium, aluminum, oxygen and a rare-earth element, wherein the second phase comprises Al.sub.2O.sub.3 single crystals, and wherein the conversion element comprises at least one groove.

A composite ceramic including: a lithium garnet major phase; and a grain growth inhibitor minor phase, as defined herein. Also disclosed is a method of making composite ceramic, pellets and tapes thereof, a solid electrolyte, and an electrochemical device including the solid electrolyte, as defined herein.

The present application relates to a magnesium oxide based dielectric ceramics with ultrahigh dielectric breakdown strength and a preparation method thereof. The composition of the magnesium oxide based dielectric ceramic material comprises: (1−x)MgO—xAl.sub.2O.sub.3, wherein 0<x≤0.12 and x is a mole percentage. The material has a specific composite structure with magnesium aluminate spinel acting as a second phase surrounding a principal crystalline phase, MgO.