C04B2235/786
Black sintered body and method for producing the same
A sintered body includes a solid solution containing cobalt and iron, with the balance being zirconia. The total content of cobalt in terms of CoO and iron in terms of Fe.sub.2O.sub.3 is more than 0.1 wt % and less than 3.0 wt %, and the proportion of cobalt regions larger than 5.5 μm.sup.2 in an elemental map obtained using an electron probe microanalyzer is 25% or less.
Ceramic
The present invention relates to a ceramic, to a process for preparing the ceramic and to the use of the ceramic as a dielectric in a capacitor.
GRAIN-GRADE ZIRCONIA TOUGHENED ALUMINA CERAMIC SUBSTRATE AND METHOD FOR PREPARING THE SAME
A grain-grade zirconia toughened alumina ceramic substrate and a method for preparing the same. The ceramic substrate is prepared from alumina power (main phase) and zirconia powder (secondary phase) in a binary azeotrope of anhydrous ethanol and butanone in the presence of magnesia-alumina spinel powder (as sintering aid), phosphate ester (as dispersant), polyvinyl butyral (as binder) and dibutyl phthalate (as plasticizer). In a mixture of the alumina power and the zirconia powder, a volume percentage of the alumina power is 82.44-96.7%, and a volume percentage of the zirconia powder is 3.30-17.56%. The magnesia-alumina spinel powder is 0.1-4.0% by weight of the mixture of the alumina power and the zirconia powder. A particle size ratio of the alumina powder to the zirconia powder is 2.415-4.444.
LIQUID CONTACT MEMBER, METHOD FOR PRODUCING SAME, MEMBER FOR ANALYZERS, ANALYZER, SLIDING MEMBER, AND SLIDING DEVICE
Object
To provide a liquid contact member having high hydrophilicity and exhibiting high dirt removal efficiency by cleaning.
Solution
A liquid contact member includes a ceramic including a plurality of crystal grains and a grain boundary phase, and the concentration of silicon on a liquid contact surface of the ceramic is higher than that of silicon on a virtual internal surface parallel to the liquid contact surface.
Ferrite sintered magnet and rotary electrical machine comprising the same
A ferrite sintered magnet 100 comprises M-type ferrite crystal grains 4 having a hexagonal structure, two-crystal grain boundaries 6a formed between two of the M-type ferrite crystal grains 4, and multiple-crystal grain boundaries 6b surrounded by three or more of the M-type ferrite crystal grains 4. This ferrite sintered magnet 100 contains at least Fe, Ca, B, and Si, and contains B in an amount of 0.005 to 0.9 mass % in terms of B.sub.2O.sub.3, the two-crystal grain boundaries 6a and the multiple-crystal grain boundaries 6b contain Si and Ca, and in a cross-section parallel to a c-axis of the ferrite sintered magnet, when the number of multiple-crystal grain boundaries 6b having a maximum length of 0.49 to 5 μm per cross-sectional area of 76 μm.sup.2 is N, N is 7 or less.
PHOSPHOR PLATE, LIGHT EMITTING DEVICE, AND METHOD FOR MANUFACTURING PHOSPHOR PLATE
A phosphor plate including: a complex containing an α-sialon phosphor and a sintered body containing spinel represented by a general formula M.sub.2xAl.sub.4-4xO.sub.6-4x (where M represents at least one of Mg, Mn, and Zn, and 0.2<x<0.6). In addition, there is provided a light emitting device including: a group III nitride semiconductor light emitting element; and the phosphor plate provided on one surface of the group III nitride semiconductor light emitting element. Further, there is provided a method for manufacturing the phosphor plate.
MULTILAYER COIL COMPONENT
A multilayer coil component includes a multilayer body in which a plurality of insulating layers are stacked in a stacking direction and a coil inside, and outer electrodes on surfaces of the multilayer body and electrically connected to the coil. The insulating layers have a magnetic phase having spinel structure containing at least Fe, Ni, Zn, and Cu and a non-magnetic phase containing at least Si. When grain sizes D50 and D90 of crystal grains constituting the magnetic phase are respectively defined as equivalent-area circle diameters of 50% and 90% on a cumulative sum basis in a cumulative distribution of equivalent-area circle diameters of the crystal grains, the grain size D50 is from 50 nm to 750 nm, and the grain size D90 is from 200 nm to 1500 nm.
Dielectric ceramic composition and ceramic electronic components
Provided is a dielectric ceramic composition including a first component and a second component, wherein the first component comprises an oxide of Ca of 0.00 mol % to 35.85 mol % an oxide of Sr of 0.00 mol % to 47.12 mol %, an oxide of Ba of 0.00 mol % to 51.22 mol %, an oxide of Ti of 0.00 mol % to 17.36 mol %, an oxide of Zr of 0.00 mol % to 17.36 mol %, an oxide of Sn of 0.00 mol % to 2.60 mol %, an oxide of Nb of 0.00 mol % to 35.32 mol %, an oxide of Ta of 0.00 mol % to 35.32 mol %, and an oxide of V of 0.00 mol % to 2.65 mol %, and the second component includes at least (a) an oxide of Mn of 0.005% by mass to 3.500% by mass and (b) an oxide of Cu and/or an oxide of Ru.
CaO-ZrO2 Composition, Method for Producing CaO-ZrO2 Composition, and CaO-ZrO2-Containing Refractory Material and Casting Nozzle
Provided is a ZrO.sub.2—CaO—C based refractory material which is capable of maintaining high adhesion resistance over a long period of time, while exhibiting significant slaking resistance, and suppressing self-fluxing, i.e., exhibiting corrosion-erosion resistance. The refractory material comprises a CaO—ZrO.sub.2 composition containing a CaO component in an amount of 40% by mass to 60% by mass, wherein a mass ratio of the CaO component to a ZrO.sub.2 component is 0.67 to 1.5, and wherein the CaO—ZrO.sub.2 composition includes a eutectic microstructure of CaO crystals and CaZrO.sub.3 crystals, wherein a width of each of the CaO crystals observable in a cross-sectional microstructure is 50 μm or less.
PLASMA RESISTANT YTTRIUM ALUMINUM OXIDE BODY
Disclosed herein is a sintered ceramic body comprising from 90% to 99.9% by volume of polycrystalline yttrium aluminum garnet (YAG) as measured using XRD and image processing methods and a volumetric porosity of from 0.1 to 4% as calculated from density measurements performed in accordance with ASTM B962-17. The sintered ceramic body may have a total purity of 99.99% and greater and a grain size of from 0.3 to 8 μm. A method of making the sintered ceramic body is also disclosed.