The present invention relates to a modifier useful for modifying a polymer, a method for preparing a modified and conjugated diene-based polymer using the same, and a modified and conjugated diene-based polymer prepared thereby. In the modified and conjugated diene-based polymer, a hydroxyl group and a silyl group are combined, and the affinity thereof with a silica-based filler may be excellent. Accordingly, a rubber composition including the modified and conjugated diene-based polymer may have excellent processability, and as a result, molded articles (for example, tires) manufactured from the rubber composition may have excellent tensile strength, abrasion resistance, and viscoelasticity properties.

A polyurethane-ionomer hybrid resin composition for a golf ball cover having excellent elastic reaction force and backspin performance comprises 100 parts by weight of a modified ionomer having a number average molecular weight in a range of 1,000 to 2,400, provided as a reaction product generated by a reaction among a polyol including hydroxyl groups on opposing ends of the polyol, a monomer of acrylic acid or methacrylic acid having 2 to 3 functional groups, and zirconia, and modified in such a manner that a polyester oligomer in a zirconia complex state and a zirconia filled state is added to an ionomer resin to be reacted, and a portion of unsaturated carboxylic acid of an ionomer is neutralized to be zirconium and additionally polymerized to be the polyester oligomer; 20 to 40 parts by weight of a block polyurethane prepolymer with respect to 100 parts by weight of the modified ionomer; 70 to 100 parts by weight of the ionomer with respect to 100 parts by weight of the modified ionomer; and 1 to 10 parts by weight of a chain extender with respect to 100 parts by weight of the block polyurethane prepolymer.

A polyurethane-ionomer hybrid resin composition for a golf ball cover having excellent elastic reaction force and backspin performance comprises 100 parts by weight of a modified ionomer having a number average molecular weight in a range of 1,000 to 2,400, provided as a reaction product generated by a reaction among a polyol including hydroxyl groups on opposing ends of the polyol, a monomer of acrylic acid or methacrylic acid having 2 to 3 functional groups, and zirconia, and modified in such a manner that a polyester oligomer in a zirconia complex state and a zirconia filled state is added to an ionomer resin to be reacted, and a portion of unsaturated carboxylic acid of an ionomer is neutralized to be zirconium and additionally polymerized to be the polyester oligomer; 20 to 40 parts by weight of a block polyurethane prepolymer with respect to 100 parts by weight of the modified ionomer; 70 to 100 parts by weight of the ionomer with respect to 100 parts by weight of the modified ionomer; and 1 to 10 parts by weight of a chain extender with respect to 100 parts by weight of the block polyurethane prepolymer.

Provided herein is a two-component adhesive composition showing excellent adhesive strength after heat and humidity exposure.

Provided is a coating composition containing: a hydroxyl group-containing resin (A), a curing agent (B), and cellulose nanocrystal particles (C), where a viscosity (V.sub.1) measured under conditions of a temperature of 25 C. and a shear rate of 1500 sec.sup.1 is in a range from 10 to 70 mPa.Math.s, and a viscosity (V.sub.2) measured under conditions of a temperature of 25 C. and a shear rate of 0.1 sec.sup.1 is in a range from 10000 to 50000 mPa.Math.s.

Provided is a coating composition containing: a hydroxyl group-containing resin (A), a curing agent (B), and cellulose nanocrystal particles (C), where a viscosity (V.sub.1) measured under conditions of a temperature of 25 C. and a shear rate of 1500 sec.sup.1 is in a range from 10 to 70 mPa.Math.s, and a viscosity (V.sub.2) measured under conditions of a temperature of 25 C. and a shear rate of 0.1 sec.sup.1 is in a range from 10000 to 50000 mPa.Math.s.

What is described are isocyanate compositions comprising -dicarbonyl compounds and a binder system, especially for use in a process from the group consisting of polyurethane cold-box process and polyurethane no-bake process, with this isocyanate composition as polyisocyanate component.

The present invention provides an adhesive film hardly suffering from fisheyes and having excellent mechanical strength and heat resistance as well as good adhesive properties with reduced transfer of an adhesive layer to an adherend, which can be suitably used as various surface protective films, etc. The present invention relates to an adhesive film comprising a polyester film and an adhesive layer formed on at least one surface of the polyester film, in which the adhesive layer comprises a resin having a glass transition point of not higher than 0 C., and a crosslinking agent, and an adhesion strength of the adhesive layer to a polymethyl methacrylate plate is in the range of 1 to 1000 mN/cm.

The objective of the present invention is to provide: an aqueous coating composition which has excellent adhesiveness to a plastic substrate and which is capable of forming a multilayer coating film, which has excellent finishing property and water resistance and in which mixing of the layers does not occur even when preheating is not conducted after coating and the next process of applying a finishing coat is performed thereafter; and a coating method using the composition. This aqueous coating composition is characterized by comprising an aqueous dispersion of a modified polyolefin (A), an aqueous acrylic resin (B) and a blocked polyisocyanate compound having a specific blocked isocyanate (C).

The objective of the present invention is to provide: an aqueous coating composition which has excellent adhesiveness to a plastic substrate and which is capable of forming a multilayer coating film, which has excellent finishing property and water resistance and in which mixing of the layers does not occur even when preheating is not conducted after coating and the next process of applying a finishing coat is performed thereafter; and a coating method using the composition. This aqueous coating composition is characterized by comprising an aqueous dispersion of a modified polyolefin (A), an aqueous acrylic resin (B) and a blocked polyisocyanate compound having a specific blocked isocyanate (C).