Provided is a surface-treated calcium carbonate that can make a vinyl chloride-based resin composition less colorable in a weathering test and excellent in impact strength. The surface-treated calcium carbonate is a calcium carbonate subjected to treatment with a surface treatment agent in which a proportion of saturated fatty acid contained in a fatty acid is 85% by mass or more, and has a content of elemental iron of 0.01% by mass or less, a content of elemental zinc of 0.1 to 2% by mass introduced by the treatment with the surface treatment agent, and a BET specific surface area of 5 to 30 m.sup.2/g.

A process for end capping and chain extending silanol terminated polydiorganosiloxanes with a mixture of one or more alkylacetoxydialkoxysilanes and one or more alkyldiacetoxyalkoxysilanes. The resulting capped polymeric material may be utilised as a polymer in e.g. a one-part alkoxy sealant composition such as, for example, an alkoxy low modulus clean (non-staining) or clear sealant composition.

A composite cooling film including a reflective nonporous inorganic-particle-filled organic polymeric layer, an ultra-violet-protective layer or layers, and an antisoiling layer.

A composition formed from a calcium or magnesium carbonate-including material and a surface-treatment composition including at least one cross-linkable compound, a dry process for the preparation of such a composition, a curable elastomer mixture comprising an elastomer resin and the composition, a cured elastomer product formed from the curable elastomer mixture, a process for preparing the cured elastomer product, the use of at least one cross-linkable compound including at least two functional groups, wherein at least one functional group is suitable for cross-linking an elastomer resin and wherein at least one functional group is suitable for reacting with the calcium or magnesium carbonate-including material in the compounding of an elastomer formed from an elastomer resin and at least one calcium or magnesium carbonate-comprising material as filler as well as an article formed from the cured elastomer product.

A curable fluoropolymer composition includes a crosslinkable fluorine-containing polymer, and a filler selected from surface-reacted calcium carbonate, ultrafine calcium carbonate, or a mixture thereof, wherein the surface-reacted calcium carbonate is a reaction product of natural ground calcium carbonate or precipitated calcium carbonate with carbon dioxide and one or more H.sub.3O.sup.+ ion donors, wherein the carbon dioxide is formed in situ by the H.sub.3O.sup.+ ion donors treatment and/or is supplied from an external source. Furthermore, the disclosure relates to a cured fluoropolymer product formed from said composition, an article including the cured fluoropolymer product, a method of producing a cured fluoropolymer product, and use of said filler for reinforcing a cured fluoropolymer product.

A urethane-based adhesive composition includes a urethane prepolymer, a carbon black A having a dibutyl phthalate oil absorption number of 30 to 40 ml/100 g, a carbon black B having a dibutyl phthalate oil absorption number of 98 to 108 ml/100 g, a calcium carbonate C, a plasticizer D, a modified product E of an aliphatic diisocyanate, and a catalyst, and the urethane-based adhesive composition is configured to satisfy all of the following (1) to (6): (1) 25≤a≤35, (2) 55≤b≤75, (3) 197≤a+3b≤251, (4) 30≤c≤35, (5) 35≤d≤45, and (6) 9≤e≤13.

A multi-layered thermoplastic roofing membrane comprising a planar body including at least three layers, said at least three layers including (i) a top layer that includes magnesium hydroxide dispersed within a thermoplastic resin, (ii) an upper middle layer disposed below said top layer and including magnesium hydroxide and calcium carbonate dispersed within a thermoplastic resin, and (iii) a lower layer disposed below said upper middle layer and including magnesium hydroxide and calcium carbonate dispersed within a thermoplastic resin.

An earth plant-based compostable biodegradable composition for the formation of a bioplastic and method of producing said resin, the composition comprising: about 17.5 to 45% ethanol-based green polyethylene by weight, about 20 to 25% calcium carbonate by weight, about 2 to 12% hemp hurd or soy protein by weight, about 32 to 45% starch by weight, and about 0.5 to 1% biodegradation additive by weight to enable biodegradation and composting of the bioplastic; wherein the composition is produced by first mill grinding the ethanol-based green polyethylene, calcium carbonate, hemp hurd or soy protein, starch and the biodegradation additive into fine powders, then mechanically mixing the fine powders one by one into a final mixture for about 5-25 minutes at a time, dry and without heat, and then heating the final mixture to about 220 to 430 degrees Fahrenheit.

A method for manufacturing a polyester film for embossing that is made from a recycled polyester material. A part of the recycled polyester material is physically reproduced to obtain physically regenerated polyester chips. The physically regenerated polyester chips include physically regenerated regular polyester chips. Another part of the recycled polyester material is chemically reproduced to obtain chemically regenerated polyester chips. The chemically regenerated polyester chips include chemically regenerated regular polyester chips and chemically regenerated electrostatic pinning polyester chips. The physically regenerated polyester chips and the chemically regenerated polyester chips are mixed to form a base material. The base material is used to form a base layer that having a main component of regenerated polyethylene terephthalate. A surface coating layer is formed onto the base layer. A material of the surface coating layer includes a main resin, fillers, and melamine.

The use of inhibitory calcium carbonate as additive for a composition containing at least one polymer different from cellulose, wherein the inhibitory calcium carbonate is obtainable by means of a method in which calcium carbonate particles are coated with a composition comprising, based on its total weight, at least 0.1% by weight of at least one weak acid. Further described is a composition containing at least one polymer different from cellulose and inhibitory calcium carbonate.