Cathode material from exhausted lithium ion batteries are dissolved in a solution for extracting the useful elements Co (cobalt), Ni (nickel), Al (Aluminum) and Mn (manganese) to produce active cathode materials for new batteries. The solution includes compounds of desirable materials such as cobalt, nickel, aluminum and manganese dissolved as compounds from the exhausted cathode material of spent cells. Depending on a desired proportion, or ratio, of the desired materials, raw materials are added to the solution to achieve the desired ratio of the commingled compounds for the recycled cathode material for new cells. The desired materials precipitate out of solution without extensive heating or separation of the desired materials into individual compounds or elements. The resulting active cathode material has the predetermined ratio for use in new cells, and avoids high heat typically required to separate the useful elements because the desired materials remain commingled in solution.

In a method for recovering an active metal of a lithium secondary battery, a sulfuric acid solution is added to a lithium metal composite oxide so as to prepare a sulfated active material solution. A transition metal is extracted from the sulfated active material solution. A lithium precursor is recovered by adding a lithium extracting agent to the solution remaining after the transition metal has been extracted from the sulfated active material solution. In the method, the amount of impurities is reduced, and sulfuric acid and the neutralizing agent can be recycled so that a high-yield lithium precursor recovery is enabled.

The present invention relates to a method for recycling iron and aluminum in a nickel-cobalt-manganese solution. The method comprises the following steps: leaching a battery powder and removing copper therefrom to obtain a copper-removed solution, and adjusting the pH value in stages to remove iron and aluminum, so as to obtain a goethite slag and an iron-aluminum slag separately; mixing the iron-aluminum slag with an alkali liquor, and heating and stirring same to obtain an aluminum-containing solution and alkaline slag; and heating and stirring the aluminum-containing solution, introducing carbon dioxide thereto and controlling the pH value to obtain aluminum hydroxide and an aluminum-removed solution.

A method for the recovery of metals from a feed stream containing one or more value metals and lithium, the method comprising: subjecting the feed stream to a sulphuric acid leach to form a slurry comprising a pregnant leach solution of soluble metal salts and a solid residue; separating the pregnant leach solution and the solid residue; subjecting the pregnant leach solution to one or more separate solvent extraction steps, wherein each solvent extraction step recovers one or more value metals from the pregnant leach solution, the remaining pregnant leach solution comprising lithium; and recovery of lithium from the pregnant leach solution.

The present disclosure relates to a process for the recovery of transition metals from batteries comprising treating a transition metal material with a leaching agent to yield a leach which contains dissolved copper impurities, and depositing the dissolved copper impurities as elemental copper on a particulate deposition cathode by electrolysis of an electrolyte containing the leach.

A process for recovering a nickel cobalt manganese hydroxide from recycled lithium-ion battery (LIB) material such as black mass, black powder, filter cake, or the like. The recycled LIB material is mixed with water and either sulfuric acid or hydrochloric acid at a pH less than 2. Cobalt, nickel, and manganese oxides from the recycled lithium-ion battery material dissolve into the acidic water with the reductive assistance of gaseous sulfur dioxide. Anode carbon is filtered from the acidic water, leaving the dissolved cobalt, nickel, and manganese oxides in a filtrate. The filtrate is mixed with aqueous sodium hydroxide at a pH greater than 8. Nickel cobalt manganese hydroxide precipitates from the filtrate. The nickel cobalt manganese hydroxide is filtered from the filtrate and dried. The filtrate may be treated ammonium fluoride or ammonium bifluoride to precipitate lithium fluoride from the filtrate. The composition ratio of nickel to cobalt to manganese in the acid filtrate may be adjusted to a desired ratio. The anode carbon is recovered and purified for reuse.

The present disclosure discloses a wet process for recovering valuable metals from a lithium battery. In the method, a waste lithium battery powder is subjected to selective leaching under the condition that a hydrogen sulfide gas is introduced through pressurization, such that Mn.sup.2+, Li.sup.+, and Al.sup.3+ metal ions enter a first-stage leaching liquor and nickel, cobalt, copper, and iron exist in a first-stage leaching residue in the form of a sulfide; then a pH of the first-stage leaching liquor is adjusted to remove aluminum and manganese, which achieves extremely thorough metal separation and leads to relatively pure products; a first-stage leaching residue is subjected to leaching in an acid liquor under a negative pressure, such that the sulfides of nickel, cobalt, iron, and copper are dissolved in a second-stage leaching liquor, and a hydrogen sulfide gas produced can be recycled in the first-stage leaching procedure through pressurization.

The present disclosure belongs to the technical field of lithium battery recycling, and discloses a method for separating and recovering valuable metals from waste ternary lithium batteries. The method includes the following steps: adding a persulfate to a waste ternary lithium battery powder, and conducting oxidative acid leaching to obtain a leaching liquor and a leaching residue; adding an alkali to the leaching liquor to allow a precipitation reaction; adding a sulfide salt to allow a reaction; adjusting a pH to allow a precipitation reaction to obtain a nickel hydroxide precipitate and a liquid phase A; adding a carbonate to the liquid phase A to allow a reaction, and conducting solid-liquid separation (SLS) to obtain lithium carbonate; and subjecting the leaching residue to calcination, adding a chlorate, heating a resulting mixture, and conducting SLS to obtain manganese dioxide.

Battery grade metal sulfate solutions can be prepared directly from electrolytically produced metal objects, such as cathode plates, when these are subjected to an aqueous leaching solution comprising at least one acid leaching agent and a liquid oxidizing agent in a continuous process at elevated temperature and with vigorous mixing. A leaching arrangement comprising a leaching column or reaction vessel is also disclosed.

A method for producing mixed metal salts containing manganese ions and at least one of cobalt ions and nickel ions, the method including: an Al removal step of subjecting an acidic solution containing at least manganese ions and aluminum ions, and at least one of cobalt ions and nickel ions, to removal of the aluminum ions by extracting the aluminum ions into a solvent, the acidic solution being obtained by subjecting battery powder of lithium ion batteries to a leaching step; and a precipitation step of neutralizing an extracted residual liquid obtained in the Al removal step under conditions where a pH is less than 10.0, to precipitate mixed metal salts comprising a metal salt of manganese and a metal salt of at least one of cobalt and nickel.