The present invention provides A magnesium oxide whisker in-situ formed MA spinel-reinforced magnesium oxide-based ceramic foam filter and a method for preparing the same. The method comprising: 1) preparing a ceramic slurry having a solid content of 60%-70% by dosing 15%-25% by mass of a nanometer alumina sol, 0.8%-1.5% by mass of a rheological agent, and the balance magnesium oxide ceramic powder comprising magnesium oxide whiskers, and then adding deionized water and ball milling to mix until uniform, and then vacuum degassing the mixture; 2) soaking a polyurethane foam template into the ceramic slurry, squeezing by a roller press the polyurethane foam template to remove redundant slurry therein to make a biscuit, and drying the biscuit by heating it to 80° C.-1200° C.; 3) putting the dried biscuit into a sintering furnace, elevating the temperature to 1400° C.-1600° C. and performing a high temperature sintering, cooling to the room temperature with the furnace to obtain the magnesium oxide-based ceramic foam filter.

A particulate filter and method of manufacture. The particulate filter comprises a ceramic honeycomb body comprising a plurality of intersecting walls that define a plurality of channels extending longitudinally though the ceramic honeycomb body. The intersecting walls comprise a porous ceramic material having a microstructure that comprises an interconnected network of porous spheroidal ceramic beads. The microstructure has a total porosity defined as the sum of an open intrabead porosity of the beads and an interbead porosity defined by interstices between the beads in the interconnected network. The microstructure has a bimodal pore size distribution in which an intrabead median pore size of the intrabead porosity is from 1.5 μm to 4 μm and an interbead median pore size of the interbead porosity is from 6 μm to 20 μm.

A particulate filter and method of manufacture. The particulate filter comprises a ceramic honeycomb body comprising a plurality of intersecting walls that define a plurality of channels extending longitudinally though the ceramic honeycomb body. The intersecting walls comprise a porous ceramic material having a microstructure that comprises an interconnected network of porous spheroidal ceramic beads. The microstructure has a total porosity defined as the sum of an open intrabead porosity of the beads and an interbead porosity defined by interstices between the beads in the interconnected network. The microstructure has a bimodal pore size distribution in which an intrabead median pore size of the intrabead porosity is from 1.5 μm to 4 μm and an interbead median pore size of the interbead porosity is from 6 μm to 20 μm.

A paste for ceramic 3D shaping according to the present invention is a paste for ceramic 3D shaping containing a curable resin and inorganic particles, in which the inorganic particles contain ceramic particles and glass particles.

Object

To provide a liquid contact member having high hydrophilicity and exhibiting high dirt removal efficiency by cleaning.

Solution

A liquid contact member includes a ceramic including a plurality of crystal grains and a grain boundary phase, and the concentration of silicon on a liquid contact surface of the ceramic is higher than that of silicon on a virtual internal surface parallel to the liquid contact surface.

Object

To provide a liquid contact member having high hydrophilicity and exhibiting high dirt removal efficiency by cleaning.

Solution

A liquid contact member includes a ceramic including a plurality of crystal grains and a grain boundary phase, and the concentration of silicon on a liquid contact surface of the ceramic is higher than that of silicon on a virtual internal surface parallel to the liquid contact surface.

A refractory filter suitable for filtering molten metal, such as steel, and a method and powdered composition for producing said filter. The filter comprises refractory material, said refractory material comprising: 60-90 wt % alumina; 8-30 wt % zirconia; and 3-20 wt % magnesia. The powdered composition comprises: 60-90 wt % alumina; 8-30 wt % zirconia; and 3-20 wt % magnesia, wherein the powdered composition comprises less than 12.5 wt % reactive alumina, calcined alumina or a mixture thereof, and wherein the remainder of the alumina is tabular alumina. The method comprises: providing a powdered composition in accordance with the invention; forming a filter precursor from the powdered composition and a liquid component; and firing the filter precursor to form a refractory filter.

A refractory filter suitable for filtering molten metal, such as steel, and a method and powdered composition for producing said filter. The filter comprises refractory material, said refractory material comprising: 60-90 wt % alumina; 8-30 wt % zirconia; and 3-20 wt % magnesia. The powdered composition comprises: 60-90 wt % alumina; 8-30 wt % zirconia; and 3-20 wt % magnesia, wherein the powdered composition comprises less than 12.5 wt % reactive alumina, calcined alumina or a mixture thereof, and wherein the remainder of the alumina is tabular alumina. The method comprises: providing a powdered composition in accordance with the invention; forming a filter precursor from the powdered composition and a liquid component; and firing the filter precursor to form a refractory filter.

The present invention provides a method of producing a honeycomb structured body having excellent mechanical strength. The present invention relates to a method of producing a honeycomb structured body including a honeycomb fired body in which multiple through-holes are arranged longitudinally in parallel with one another with a partition wall therebetween, the method including: a raw material mixing step of preparing a raw material paste containing ceria-zirconia composite oxide particles, alumina particles, an inorganic binder, and inorganic fibers; a molding step of molding the raw material paste into a honeycomb molded body in which multiple through-holes are arranged longitudinally in parallel with one another with a partition wall therebetween; a drying step of drying the honeycomb molded body obtained in the molding step; and a firing step of firing the honeycomb molded body dried in the drying step into a honeycomb fired body, wherein the raw material mixing step includes pre-mixing of the inorganic binder and the inorganic fibers.

The present invention provides a method of producing a honeycomb structured body having excellent mechanical strength. The present invention relates to a method of producing a honeycomb structured body including a honeycomb fired body in which multiple through-holes are arranged longitudinally in parallel with one another with a partition wall therebetween, the method including: a raw material mixing step of preparing a raw material paste containing ceria-zirconia composite oxide particles, alumina particles, an inorganic binder, and inorganic fibers; a molding step of molding the raw material paste into a honeycomb molded body in which multiple through-holes are arranged longitudinally in parallel with one another with a partition wall therebetween; a drying step of drying the honeycomb molded body obtained in the molding step; and a firing step of firing the honeycomb molded body dried in the drying step into a honeycomb fired body, wherein the raw material mixing step includes pre-mixing of the inorganic binder and the inorganic fibers.