Provided is a MnZnO sputtering target which can be used in DC sputtering, and a production method for the target. The MnZnO sputtering target comprises a chemical composition containing Mn, Zn, O, and at least one element X, the element X being a single one or two elements selected from the group consisting of W and Mo. The target has a relative density of 90% or more and a specific resistance of 110.sup.3 .Math.cm or less.

A positive electrode active material for a non-aqueous electrolyte secondary battery includes secondary particles of a lithium transition metal complex oxide as a main component. The main component is represented by a formula: Li.sub.t(Ni.sub.1-xCo.sub.x).sub.1-yMn.sub.yB.sub.P.sub.S.sub.O.sub.2, where t, x, y, , , and satisfy inequalities of 0x1, 0.00y0.50, (1x).Math.(1y)y, 0.0000.020, 0.0000.030, 0.0000.030, and 1+3+3+2t1.30, and satisfy at least one of inequalities of 0.002, 0.006, and 0.004. The secondary particles exhibit a pore distribution, where a pore volume Vp(1) having a pore diameter of not less than 0.01 m and not more than 0.15 m satisfies an inequality of 0.035 cm.sup.3/gVp(1) and where a pore volume Vp(2) having a pore diameter of not less than 0.01 m and not more than 10 m satisfies an inequality of Vp(2)0.450 cm.sup.3/g.

A piezoelectric material including a perovskite-type metal oxide represented by the following general formula (1); Bi; and Mn, wherein the content of Bi is 0.1-0.5 mol % with respect to 1 mol of the metal oxide, the content of Mn is 0.3-1.5 mol % with respect to 1 mol of the metal oxide, and the piezoelectric material satisfies (L.sub.4L.sub.5)/L.sub.50.05 and (L.sub.8L.sub.9)/L.sub.90.05 when the lengths of twelve BiO bonds with Bi that is located at a 12-fold site with respect to O in a perovskite-type unit cell as a starting point are taken to be L.sub.1 to L.sub.12 in length order:
(Ba.sub.1-xM1.sub.x)(Ti.sub.1-yM2.sub.y)O.sub.3(1)
wherein 0x0.2, 0y0.1, and M1 and M2 are mutually different metal elements which have a total valence of +6 and are selected from other elements than Ba, Ti, Bi and Mn.

The present disclosure relates to piezoelectric compositions of Formula I comprising Lead ZirconateLead Titanate solid solution. The disclosure further relates to a method of obtaining said composition, method of preparing/fabricating piezoelectric component(s) and piezoelectric component(s)/article(s) obtained thereof. The piezoelectric composition and articles of the present disclosure show excellent electromechanical characteristics along with very large insulation resistance (IR).

A positive electrode composition for a rechargeable battery, the composition comprising a first and a second powderous lithium metal oxide, the first lithium metal oxide comprising either one or more of Ni, Mn and Co, the second lithium metal oxide powder having either: the formula Li.sub.xWM.sub.yO.sub.z, M being a metal having a valence state of +2 or +3, with 0<y1, 3x4, 5z6, whereby x=(2*z)[y*(valence state of M)](valence state of W).

A metal oxide macroscopic fiber and a preparation method thereof, the method including: adding, as a spinning dope, an anionic metal oxide aqueous colloidal solution into wet spinning equipment, extruding the spinning dope from the spinning equipment into a thread, injecting the extruded thread into a coagulating bath containing a flocculating agent to obtain as-spun fiber, and repeatedly washing the resulted as-spun fiber with deionized water and drying same, thereby obtaining a metal oxide fiber. Said method makes the process simple and controllable, being adaptable to production on a large scale. The prepared metal oxide fiber having special physical and chemical properties is widely applicable in terms of intelligent spinning, biomedicine, energy recycling and conversion, and the field of microelectronic devices and the like.

A method for manufacturing a sintered body, the method including heating a mixture that contains a plurality of particles of a metal oxide having a spinel-type structure, and a metal acetylacetonate under pressure at a temperature of from a melting point or higher of the metal acetylacetonate to 600 C. or lower, to form a sintered body that contains the metal oxide having the spinel-type structure.

A method for manufacturing a sintered body, the method including heating a mixture that contains a plurality of particles of a metal oxide having a spinel-type structure, and a metal acetylacetonate under pressure at a temperature of from a melting point or higher of the metal acetylacetonate to 600 C. or lower, to form a sintered body that contains the metal oxide having the spinel-type structure.

The invention relates to the field of environmental protection, more specifically to the field of processing radioactive waste, and can he used for the safe and effective handling of a large quantity of liquid radioactive waste of various activity levels that has been formed as the result of decontaminating protective equipment of boxes and chambers, and makes it possible to decrease the volume of stored waste by solidifying same and incorporating same into a ceramic matrix. For this purpose, radioactive solutions after decontamination of surfaces of protective equipment are evaporated as alkaline and acidic solutions containing sodium hydroxide, potassium permanganate, oxalic acid, and nitric acid until a solid residue forms, and are calcined, and the calcinate is mixed with components of a fusion mixture containing oxides of titanium, calcium, iron (III), zirconium, and manganese (IV) and aluminum in a specified ratio, and fused.

The invention provides a dual component lithium-rich layered oxide positive electrode material for a secondary battery, the material consisting of a single-phase lithium metal oxide with space group R-3m and having the general formula Li.sub.1+.sub.bN.sub.1bO.sub.2, wherein 0.155b0.25 and N=Ni.sub.xMn.sub.yCO.sub.zZr.sub.cA.sub.d, with 0.10x0.40, 0.30y0.80, 0<z0.20, 0.005c0.03, and 0d0.10, and wherein x+y+z+c+d=1, with A being a dopant comprising at least one element, and the material further consisting of a Li.sub.2ZrO.sub.3 component.