A porous formed body (Y) including a porous formed body (X) that satisfies the following (x-1) to (x-3), and an alkali metal carbonate or an alkali metal bicarbonate, in which a content of the alkali metal carbonate or the alkali metal bicarbonate is in a range of from 1 part by mass to 230 parts by mass, with respect to 100 parts by mass of the porous formed body (X), and a production method thereof, an α-olefin dimerization catalyst and a production method thereof, and a method of producing an α-olefin dimer: requirement (x-1): a volume of pores with a pore diameter in a range of from 0.01 μm to 100 μm is from 0.10 mL/g to 1.00 mL/g; requirement (x-2): a median pore diameter of pores with a pore diameter in a range of from 0.01 μm to 100 μm is from more than 0.01 μm to 10.0 μm; and requirement (x-3): a crushing strength is from 0.7 kgf to 15.0 kgf.

An oligomerization catalyst, oligomer products, methods for making and using same. The catalyst can include a supported nickel phosphate compound. The catalyst is stable at oligomerization temperatures of 500° C. or higher and particularly useful for making oligomer products containing C4 to C26 olefins having a boiling point in the range of 170° C. to 360° C.

An oligomerization catalyst, oligomer products, methods for making and using same. The catalyst can include a supported nickel phosphate compound. The catalyst is stable at oligomerization temperatures of 500° C. or higher and particularly useful for making oligomer products containing C4 to C26 olefins having a boiling point in the range of 170° C. to 360° C.

An oligomerization catalyst, oligomer products, methods for making and using same. The catalyst can include a supported nickel phosphate compound. The catalyst is stable at oligomerization temperatures of 500° C. or higher and particularly useful for making oligomer products containing C4 to C26 olefins having a boiling point in the range of 170° C. to 360° C.

Disclosed herein are compositions containing branched C.sub.20 2-substituted alpha olefins and processes for making the compositions by dimerization reaction of a C.sub.10 olefin composition.

Disclosed herein are compositions containing branched C.sub.20 2-substituted alpha olefins and processes for making the compositions by dimerization reaction of a C.sub.10 olefin composition.

The present disclosure relates to a catalyst for direct nonoxidative conversion of methane and a method of preparing the same, and more particularly to a method of preparing a catalyst for direct nonoxidative conversion of methane, in which a catalyst optimized for the direct conversion reaction of methane can be easily prepared without precise control of the reaction conditions for direct conversion of methane, thereby simultaneously maximizing the catalytic reaction rate and minimizing coke formation, and exhibiting stable catalytic performance even after long-term operation, and to a catalyst for direct nonoxidative conversion of methane prepared using the above method.

The present disclosure relates to a catalyst for direct nonoxidative conversion of methane and a method of preparing the same, and more particularly to a method of preparing a catalyst for direct nonoxidative conversion of methane, in which a catalyst optimized for the direct conversion reaction of methane can be easily prepared without precise control of the reaction conditions for direct conversion of methane, thereby simultaneously maximizing the catalytic reaction rate and minimizing coke formation, and exhibiting stable catalytic performance even after long-term operation, and to a catalyst for direct nonoxidative conversion of methane prepared using the above method.

Provided is a method of producing a porous molded body, the method including: the step of obtaining a molded body by molding a raw material that contains from 1 part by mass to 100 parts by mass of a bicarbonate compound (A) represented by AHCO.sub.3 (wherein, A represents Na or K) and from 0 parts by mass to 99 parts by mass of a compound (B) represented by B.sub.nX (wherein, B represents Na or K; X represents CO.sub.3, SO.sub.4, SiO.sub.3, F, Cl, or Br; and n represents an integer of 1 or 2 as determined by the valence of X) (provided that a total amount of (A) and (B) is 100 parts by mass); and the step of obtaining a porous molded body by performing a heat treatment of the molded body in a temperature range of from 100° C. to 500° C. and an atmosphere that contains water vapor in an amount of from 1.0 g/m.sup.3 to 750,000 g/m.sup.3 and thereby thermally decomposing not less than 90% by mass of the bicarbonate compound (A).

Provided is a method of producing a porous molded body, the method including: the step of obtaining a molded body by molding a raw material that contains from 1 part by mass to 100 parts by mass of a bicarbonate compound (A) represented by AHCO.sub.3 (wherein, A represents Na or K) and from 0 parts by mass to 99 parts by mass of a compound (B) represented by B.sub.nX (wherein, B represents Na or K; X represents CO.sub.3, SO.sub.4, SiO.sub.3, F, Cl, or Br; and n represents an integer of 1 or 2 as determined by the valence of X) (provided that a total amount of (A) and (B) is 100 parts by mass); and the step of obtaining a porous molded body by performing a heat treatment of the molded body in a temperature range of from 100° C. to 500° C. and an atmosphere that contains water vapor in an amount of from 1.0 g/m.sup.3 to 750,000 g/m.sup.3 and thereby thermally decomposing not less than 90% by mass of the bicarbonate compound (A).