A precursor mixture for producing a porous body, wherein the precursor mixture comprises: (i) at least one milled alpha alumina powder having a particle size of 0.1 to 6 microns, (ii) non-silicate powder that functions as a binder of the alpha alumina powders, and (iii) at least one burnout material having a particle size of 1-10 microns and a decomposition temperature of less than 550° C., with the proviso that a burnout material having a decomposition temperature of 550° C. or greater is excluded from the precursor mixture.

A shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, having a BET surface area in the range of 2 to 20 m2/g and comprising silver and a rhenium promotor deposited on a porous alpha-alumina catalyst support, characterized in that the support has a calcination history of at least 1460° C. The catalyst support has a high surface area and little ethylene oxide isomerization and/or decomposition activity. The invention further relates to a porous alpha-alumina catalyst support having a BET surface area of 1.7 to 10 m2/g, the porous alpha-alumina catalyst support being obtainable by a) preparing a precursor material comprising a transition alumina and/or an alumina hydrate; b) forming the precursor material into shaped bodies; and c) calcining the shaped bodies at a temperature of 1460° C. to 1700° C. to obtain the porous alpha-alumina support. The invention also relates to a process for producing ethylene oxide by gas-phase oxidation of ethylene, comprising reacting ethylene and oxygen in the presence of a shaped catalyst body as described above.

A porous alpha-alumina catalyst support is prepared by (i) preparing a precursor material comprising a boehmitic-derived alumina having a pore volume of at least 0.6 mL/g, wherein the boehmitic-derived alumina is obtained by thermal decomposition of a boehmitic starting material and the boehmitic starting material consists predominantly of block-shaped crystals, and optionally an inorganic bond material; (ii) forming the precursor material into shaped bodies; (iii) calcining the shaped bodies to obtain the porous alpha-alumina catalyst support. The support structure has a high overall pore volume, while keeping its surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The support is useful for a catalyst for producing ethylene oxide by gas-phase oxidation of ethylene.

A porous alpha-alumina catalyst support is prepared by (i) preparing a precursor material comprising a boehmitic-derived alumina having a pore volume of at least 0.6 mL/g, wherein the boehmitic-derived alumina is obtained by thermal decomposition of a boehmitic starting material and the boehmitic starting material consists predominantly of block-shaped crystals, and optionally an inorganic bond material; (ii) forming the precursor material into shaped bodies; (iii) calcining the shaped bodies to obtain the porous alpha-alumina catalyst support. The support structure has a high overall pore volume, while keeping its surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The support is useful for a catalyst for producing ethylene oxide by gas-phase oxidation of ethylene.

A process for producing a porous alpha-alumina catalyst support, comprising i) preparing a precursor material comprising, based on inorganic solids content, at least 50 wt.-% of a transition alumina having a loose bulk density of at most 600 g/L, a pore volume of at least 0.6 mL/g and a median pore diameter of at least 15 nm; and at most 30 wt.-% of an alumina hydrate; ii) forming the precursor material into shaped bodies; and iii) calcining the shaped bodies to obtain the porous alpha-alumina catalyst support. The catalyst support has a high overall pore volume, thus allowing for impregnation with a high amount of silver, while keeping its surface area sufficiently large so as to provide optimal dispersion of catalytically active species, in particular metal species. The invention further relates to a shaped catalyst body for producing ethylene oxide by gas-phase oxidation of ethylene, comprising at least 15 wt.-% of silver, relative to the total weight of the catalyst, deposited on a porous alpha-alumina catalyst support obtained in the process described above. The invention also relates to a process for preparing a shaped catalyst body as described above comprising impregnating a porous alpha-alumina catalyst support obtained in the process described above with a silver impregnation solution, preferably under reduced pressure; and optionally subjecting the impregnated porous alumina support to drying; and b) subjecting the impregnated porous alpha-alumina support to a heat treatment; wherein steps a) and b) are optionally repeated. The invention further relates to a process for producing ethylene oxide by gas-phase oxidation of ethylene, comprising reacting ethylene and oxygen in the presence of a shaped catalyst body as described above.

A porous shaped catalyst support body comprising at least 85% by weight of alpha-alumina, wherein the support has a total pore volume in the range from 0.5 to 2.0 mL/g as determined by mercury porosimetry, and a pore structure characterized by a geometric tortuosity τ in the range from 1.0 to 2.0; and an effective diffusion parameter η in the range from 0.060 to 1.0; wherein geometric tortuosity τ and effective diffusion parameter η are determined by image analysis algorithms from computer-assisted 3D reconstructions of focused ion beam scanning electron microscope analyses. The structure of the support has a high total pore volume, such that impregnation with a large amount of silver is possible, while the surface area is kept sufficiently high in order to assure optimal dispersion of the catalytically active species, especially metal species. The support has a pore structure that leads to a maximum rate of mass transfer within the support. The invention also relates to a shaped catalyst body for preparation of ethylene oxide by gas phase oxidation of ethylene, comprising at least 15% by weight of silver, based on the total weight of the catalyst, deposited on a porous shaped catalyst support body as described above. The invention further relates to a process for producing the shaped catalyst body, in which a) a porous shaped catalyst support body as described above is impregnated with a silver impregnation solution, preferably under reduced pressure; and the impregnated porous shaped catalyst support body is optionally subjected to drying; and b) the impregnated porous shaped catalyst support body is subjected to a heat treatment; wherein steps a) and b) are optionally repeated. The invention also relates to a process for preparing ethylene oxide by gas phase oxidation of ethylene, comprising the reaction of ethylene and oxygen in the presence of a shaped catalyst body according to claim 11.

A porous shaped catalyst support body comprising at least 85% by weight of alpha-alumina, wherein the support has a total pore volume in the range from 0.5 to 2.0 mL/g as determined by mercury porosimetry, and a pore structure characterized by a geometric tortuosity τ in the range from 1.0 to 2.0; and an effective diffusion parameter η in the range from 0.060 to 1.0; wherein geometric tortuosity τ and effective diffusion parameter η are determined by image analysis algorithms from computer-assisted 3D reconstructions of focused ion beam scanning electron microscope analyses. The structure of the support has a high total pore volume, such that impregnation with a large amount of silver is possible, while the surface area is kept sufficiently high in order to assure optimal dispersion of the catalytically active species, especially metal species. The support has a pore structure that leads to a maximum rate of mass transfer within the support. The invention also relates to a shaped catalyst body for preparation of ethylene oxide by gas phase oxidation of ethylene, comprising at least 15% by weight of silver, based on the total weight of the catalyst, deposited on a porous shaped catalyst support body as described above. The invention further relates to a process for producing the shaped catalyst body, in which a) a porous shaped catalyst support body as described above is impregnated with a silver impregnation solution, preferably under reduced pressure; and the impregnated porous shaped catalyst support body is optionally subjected to drying; and b) the impregnated porous shaped catalyst support body is subjected to a heat treatment; wherein steps a) and b) are optionally repeated. The invention also relates to a process for preparing ethylene oxide by gas phase oxidation of ethylene, comprising the reaction of ethylene and oxygen in the presence of a shaped catalyst body according to claim 11.

A precursor mixture for producing a porous body, wherein the precursor mixture comprises: (i) milled alpha alumina powder having a particle size of 0.1 to 6 microns, (ii) boehmite powder that functions as a binder of the alpha alumina powders, and (iii) burnout materials having a particle sizes of 1-10 microns. In some embodiments, an unmilled alpha alumina powder having a particle size of 10 to 100 microns is also included in said precursor mixture. Also described herein is a method for producing a porous body in which the above-described precursor mixture is formed to a given shape, and subjected to a heat treatment step in which the formed shape is sintered to produce the porous body.

A precursor mixture for producing a porous body, wherein the precursor mixture comprises: (i) milled alpha alumina powder having a particle size of 0.1 to 6 microns, (ii) boehmite powder that functions as a binder of the alpha alumina powders, and (iii) burnout materials having a particle sizes of 1-10 microns. In some embodiments, an unmilled alpha alumina powder having a particle size of 10 to 100 microns is also included in said precursor mixture. Also described herein is a method for producing a porous body in which the above-described precursor mixture is formed to a given shape, and subjected to a heat treatment step in which the formed shape is sintered to produce the porous body.

Methods for conditioning an ethylene epoxidation catalyst are provided. The conditioning methods comprise contacting an ethylene epoxidation catalyst comprising a carrier, having silver and a rhenium promoter deposited thereon, with a conditioning feed gas comprising oxygen for a period of time of at least 2 hours at a temperature that is above 180° C. and at most 250° C., wherein the contacting of the ethylene epoxidation catalyst with the conditioning feed gas occurs in an epoxidation reactor and in the absence of ethylene. Associated methods for the epoxidation of ethylene are also provided.