A polymer composition that includes a polymer produced from ethylene, one or more branched vinyl ester monomers, and optionally, vinyl acetate; optionally a secondary foamable polymer; a foaming agent, and a peroxide is provided. Methods for making such a polymer composition include blending a polymer composition from a mixture of a polymer produced from ethylene, one or more branched vinyl ester monomers, and optionally, vinyl acetate, optionally a secondary foamable polymer; a foaming agent, and a peroxide are provided.

A thermally expandable composition includes at least one polymer P cross-linkable by peroxide, and at least one acrylate, and at least one peroxide, azodicarbonamide and a zinc compound. The thermally expandable composition leads to low odor formation and low ammonia emission during and after the foaming process. The thermally expandable composition further shows excellent properties in terms of expansion stability.

A pipe joint (1) comprising: a tubular main body (10) having a flow path inside, which is formed of a resin comprising a copolymer having one or more selected from a vinyl cyanide monomer unit and an acrylic monomer unit, a rubber component, and an aromatic vinyl monomer unit; and a socket section (20a) integrally formed with the main body (10), wherein: the main body (10) has a foamed resin layer (30) and a non-foamed resin layer (50) covering the foamed resin layer (30); the amount of the rubber component in the foamed resin layer (30) as determined by pyrolysis-gas chromatography/mass spectrometry is within a specific range; the amount of the rubber component in the non-foamed resin layer (50) is within a specific range; and a ratio (L.sub.a/L.sub.a) of length (L.sub.a) from a base end (21a) to an opening end (22a) of the socket section (20a) to a thickness (d.sub.a) of the socket section (20a) at the opening end is 2.0 or more and 10.0 or less.

To provide perfluoroelastomer molded product and a protective member, excellent in plasma resistance and fitting property.

A perfluoroelastomer molded product containing no carbon black, and having a shore A hardness of 25 or more and 60 or less, and a protective member comprising the perfluoroelastomer molded product.

A copolymer may include ethylene and vinyl acetate, in which the ethylene is at least partially obtained from a renewable source of carbon. Embodiments may also be directed to curable polymer compositions, expandable polymer compositions, articles, cured articles, and expanded articles formed from or including such copolymers of ethylene and vinyl acetate, in which the ethylene is at least partially obtained from a renewable source of carbon. A process for producing an ethylene vinyl acetate copolymer may include fermenting a renewable source of carbon to produce ethanol; dehydrating the ethanol, wherein the ethanol is dehydrated to produce ethylene; and polymerizing ethylene and vinyl acetate to produce the ethylene vinyl acetate copolymer.

Compositions are provided including an uncrosslinked thermoplastic nitrogen-containing matrix material and composite particles distributed in the matrix material. The composite particles each include a chemical blowing agent particle encapsulated within a shell including an uncrosslinked thermoplastic material. The uncrosslinked thermoplastic material exhibits at least a certain minimum complex viscosity at a decomposition temperature of the chemical blowing agent particle. Also described are foam compositions and particles including the foam compositions, such as a sheet or multilayer construction. Composite particles are further provided. Methods of making the foam compositions are additionally described herein. Also, polishing pads, polishing systems, and methods of polishing a substrate are provided.

A polyolefin-based resin foamed sheet includes a polyolefin-based resin, wherein a thickness of the foamed sheet is 0.05-0.5 mm, a 25% compression hardness defined in JIS K6767(1999) is 20-100 kPa, a ratio of cell sizes in longitudinal and thickness directions is 9-30, a ratio of cell sizes in width and thickness directions is 9-30, and an average cell film thickness in the thickness direction of the foamed sheet is 2-7 μm.

The polyolefin resin foam sheet is a polyolefin resin foam sheet having a plurality of cells in an inside thereof, wherein the 50% compressive strength is 120 kPa or less; the MD elongation percentage is 400% or less; and the TD elongation percentage is 200% or less.

A polymer composition including a crosslinkable thermoplastic matrix, a crosslinking agent, a blowing agent, and at least one cell opener is provided. A method of producing an open cell polymer foam from the polymer composition is also provided. The method includes heating a foamable precursor under positive pressure to a temperature greater than a decomposition temperature of the crosslinking agent and below a decomposition temperature of the chemical blowing agent to produce a primary foam. Then, the method includes heating the primary foam to a temperature greater than the decomposition temperature of the chemical blowing agent and then allowing the primary foam to cool to a temperature below a softening temperature of the crosslinkable thermoplastic polymer to form the open cell polymer foam. The produced open cell polymer foam has an open cell content of at least 80% immediately following the step of allowing the primary foam to cool.

A method of manufacturing a polyolefin foam sheet composition includes extruding a polyolefin sheet, irradiating the extruded sheet to obtain a physically crosslinked sheet, foaming the physically crosslinked sheet with heat to obtain a foamed layer, and skiving the foamed layer to obtain a foam sheet with at least one skived surface. The surface roughness of the skived surface of the foam sheet is different from the surface roughness of an unskived surface.