The invention relates to a process for production of expanded thermoplastic elastomer, said process comprising the steps of: (e) adding monomers and/or oligomers used for producing the thermoplastic elastomer with or without further starting materials into a first stage of a polymer-processing machine, (f) mixing the monomers and/or oligomers and also the optionally added further starting materials and reacting the monomers and/or oligomers to give a polymer melt in the first stage of the polymer-processing machine, (g) passing the polymer melt into a second stage of a polymer-processing machine and adding a physical blowing agent with or without further starting materials to obtain a polymer melt comprising a blowing agent, (h) molding the polymer melt comprising a blowing agent into an expanded thermoplastic elastomer.

Disclosed are compositions comprising HCFC-243db, HCFO-1233xf, HCFC-244db and/or HFO-1234yf and at least one to additional compound. For the composition comprising 1234yf, the additional compound is selected from the group consisting of HFO-1234ze, HFO-1243zf, HCFC-243db, HCFC-244db, HFC-245cb, HFC-245fa, HCFO-1233xf, HCFO-1233zd, HCFC-253fb, HCFC-234ab, HCFC-243fa, ethylene, HFC-23, CFC-13, HFC-143a, HFC-152a, HFC-236fa, HCO-1130, HCO-1130a, HFO-1336, HCFC-133a, HCFC-254fb, CHF═CHCl, HFO-1141, HCFO-1242zf, HCFO-1223xd, HCFC-233ab, HCFC-226ba, and HFC-227ca. Compositions comprising HCFC-243db, HCFO-1233xf, and/or HCFC-244db are useful in processes to make HFO-1234yf. Compositions comprising HFO-1234yf are useful, among other uses, as heat transfer compositions for use in refrigeration, air-conditioning and heat pump systems.

The invention relates to a process for manufacturing a copolymer foam containing polyamide blocks and polyether blocks, comprising the following steps: mixing the copolymer melt with a blowing agent, said copolymer having a coefficient of thermal diffusivity a and a crystallization temperature T.sub.c; providing a mold of thickness h at a temperature T.sub.m; injecting the mixture of the copolymer and of the blowing agent at a temperature T.sub.p, into the closed mold; foaming the mixture by opening the mold;
in which the maintenance time between the injection of the mixture of the copolymer and of the blowing agent into the closed mold and the opening of the mold is within the range extending from (t.sub.opt−25%) to (t.sub.opt+25%),
t.sub.opt being expressed in seconds and obtained by equation (I):

[00001]$\begin{array}{cc}{t}_{\mathrm{opt}}=-\frac{1}{{\pi }^2}\frac{h^2}{a}\ln \left(\frac{\pi }{4}\frac{T_m-T_c}{T_m-T_p}\right),& \left(I\right)\end{array}$

in which a is expressed in m.sup.2/s, h is expressed in m and T.sub.m, T.sub.c and T.sub.p are expressed in ° C.

Polyisocyanurate (PIR) and/or polyurethane (PUR) comprising insulation foams having significantly improved long term insulation values are disclosed as well as a processing method to fabricate said improved insulation foams and use of the improved insulation foams for thermal insulation.

A thermal insulating phenolic foam and method of manufacture thereof is provided. A phenolic foam is formed by foaming and curing a phenolic resin composition that comprises a phenolic resin, an acid catalyst, a blowing agent comprising a hydrocarbon having 6 carbon atoms or less, and an alkoxy alcohol. The resulting foam has low thermal conductivity and has excellent long term thermal stability.

The present application provides foams having improved insulation and thermal performance and processes of forming said foams. Exemplary foams described herein are prepared according to a process comprising reacting or extruding a foamable composition comprising (i) a compound selected from E-CHCl═CHCF.sub.3, Z—CF.sub.3CH═CHCF.sub.3, and E-CF.sub.3CH═CHCF.sub.3, or any mixture thereof, and (2) a C.sub.5 hydrocarbon (e.g. cyclopentane), under conditions effective to form the foam.

The present invention relates to blowing agent compositions of carbon dioxide and at least one hydrochlorofluoroolefin (HCFO). The HCFOs can include, but are not limited to, 1-chloro-3,3,3-trifluoropropene (HCFO-1233zd), 2-chloro-3,3,3-trifluoropropene (HCFO-1233xf) and mixtures thereof. The blowing agent compositions are useful in the production of low density insulating foams with improved k-factor made from thermoplastic resins. The blowing agent compositions may also optionally include one or more hydrofluoroolefins (HFOs).

A phenolic resin foam has a density of 30 kg/m.sup.3 to 80 kg/m.sup.3, a closed cell ratio of 85% or more, and reaches a total amount of heat release of 8 MJ/m.sup.2 in a time of 20 minutes or more in a heat release test performed using a cone calorimeter.

The present disclosure relates to an expanded foam solution for forming a thermosetting expanded foam having excellent flame retardancy produced using the same. According to the present disclosure, nanoclay is mixed with a polyol-based compound using ultrasonic waves, an isocyanate-based compound is added, and a trimerization catalyst or an isocyanurate compound is mixed with the polyol-based compound so that an isocyanurate structure is formed.

A thermoset foam comprises from 0.2 to 4.0 wt. % of at least one aliphatic brominated polyether polyol, from 2.0 to 7.0 wt. % of at least one aromatic brominated polyester polyol, and from 2.0 to 7.5 wt. % of at least one flame retardant comprising organo-phosphate, organo-phosphonate, or organo-phosphite, wherein the ratio of the amount of aliphatic bromine expressed as a percentage of total bromine to the amount of aromatic bromine expressed as a percentage of total bromine is from 10:90 to 50:50.